Method for producing metal-plated stainless material

Patent metadata

Field	Value
Publication number	US-2017327953-A1
Application number	US-201515533287-A
Country	US
Kind code	A1
Filing date	Dec 3, 2015
Priority date	Dec 12, 2014
Publication date	Nov 16, 2017
Grant date	—

Abstract

There is provided a method for producing a metal-plated stainless material, the method including performing an acid treatment of treating a stainless steel material with an acidic solution; performing an etching of treating the stainless steel material after the acid treatment with an etching treatment agent; and a modifying the surface of the stainless steel material after the etching into a state suitable for a metal plating process.

First claim

1 . A method for producing a metal-plated stainless material, the method comprising:
performing an acid treatment of treating a stainless steel material with an acidic solution; performing an etching of treating the stainless steel material after the acid treatment with an etching treatment agent; and modifying a surface of the stainless steel material into a state suitable for a metal plating process.

2 . The method for producing a metal-plated stainless material according to claim 1 , wherein the acid treatment includes treating the stainless steel material with the acidic solution thereby to form an oxide film, wherein the oxide film has a lower density than that of a passivation film existing on the surface of the stainless steel material before the treatment with the acidic solution.

3 . The method for producing a metal-plated stainless material according to claim 2 , wherein the acid treatment includes treating the stainless steel material with the acidic solution thereby to grow an oxide film than that before the acid treatment, wherein the oxide film includes the passivation film on the surface of the stainless steel material.

4 . The method for producing a metal-plated stainless material according to claim 1 , wherein the acidic solution comprises a solution that contains any one of hydrochloric acid, ammonium hydrogen fluoride, sulfuric acid, and nitric acid or a mixture thereof.

5 . The method for producing a metal-plated stainless material according to claim 1 , wherein the etching treatment agent comprises any one of nitric acid and sulfuric acid or a mixture thereof.

6 . A method for producing a metal-plated stainless material, the method comprising:
performing a film thickness reduction of reducing a thickness of an oxide film generated on a surface of a stainless steel material using an etching agent; performing a film growth of growing the thickness-reduced oxide film using an oxidation treatment agent; and modifying the surface of the stainless steel material into a state suitable for a metal plating process.

7 . The method for producing a metal-plated stainless material according to claim 6 , wherein the etching agent comprises any one of ammonium hydrogen fluoride, sulfuric acid, nitric acid, and hydrochloric acid or a mixture thereof.

8 . The method for producing a metal-plated stainless material according to claim 6 , wherein the oxidation treatment agent comprises any one of nitric acid and sulfuric acid or a mixture thereof.

9 . The method for producing a metal-plated stainless material according to claim 1 , wherein the modifying includes performing a process of immersing the stainless steel material in a sulfuric acid aqueous solution at a temperature of 50° C. to 70° C. for 5 to 600 seconds, wherein the sulfuric acid aqueous solution has a sulfuric acid concentration of 20 to 25 vol %.

10 . The method for producing a metal-plated stainless material according to claim 1 , further comprising
performing a metal plating for the stainless steel material after the modifying.

11 . The method for producing a metal-plated stainless material according to claim 6 , wherein the modifying includes performing a process of immersing the stainless steel material in a sulfuric acid aqueous solution at a temperature of 50° C. to 70° C. for 5 to 600 seconds, wherein the sulfuric acid aqueous solution has a sulfuric acid concentration of 20 to 25 vol %.

12 . The method for producing a metal-plated stainless material according to claim 6 , further comprising
performing a metal plating for the stainless steel material after the modifying.

Assignees

• Toyo Kohan Co Ltd

Inventors

• Yoshida Takahiro
• Tsuruda Tomoyuki

Classifications

• H01R13/03

  characterised by the material, e.g. plating, or coating materials · CPC title

• C23F1/30

  for etching other metallic material · CPC title

• C23C18/1637

  metallic substrate · CPC title

• C23C18/48

  Coating with alloys · CPC title

• H01M8/021

  Alloys based on iron · CPC title