Production method for metal oxide particles, metal oxide powder, and magnetic recording medium

Patent metadata

Field	Value
Publication number	US-2017287603-A1
Application number	US-201715627636-A
Country	US
Kind code	A1
Filing date	Jun 20, 2017
Priority date	Sep 30, 2013
Publication date	Oct 5, 2017
Grant date	—

Abstract

A production method for metal oxide particles includes: obtaining precursor particles of a metal oxide by performing a synthesis reaction of the precursor particles in the presence of an organic compound; and converting the obtained precursor particles into metal oxide particles by heating an aqueous solution containing the precursor particles to 300° C. or higher and pressurizing the aqueous solution at a pressure of 20 MPa or higher.

First claim

What is claimed is:

1 . A production method for metal oxide particles comprising:
obtaining precursor particles of a metal oxide by performing a synthesis reaction of the precursor particles in the presence of an organic compound; and converting the obtained precursor particles into metal oxide particles by heating an aqueous solution containing the precursor particles to 300° C. or higher and pressurizing the aqueous solution at a pressure of 20 MPa or higher.

2 . The production method for metal oxide particles according to claim 1 ,
wherein the heating and pressurization is performed while continuously feeding the aqueous solution.

3 . The production method for metal oxide particles according to claim 1 ,
wherein the synthesis reaction is performed in an aqueous reaction solution in a pH range of 5 to 14.

4 . The production method for metal oxide particles according to claim 1 ,
wherein an average particle size of the precursor particles is 25 nm or less.

5 . The production method for metal oxide particles according to claim 2 ,
wherein an average particle size of the precursor particles is 25 nm or less.

6 . The production method for metal oxide particles according to claim 3 ,
wherein an average particle size of the precursor particles is 25 nm or less.

7 . The production method for metal oxide particles according to claim 1 ,
wherein a coefficient of variation in the particle size of the precursor particles is 5% to 40%.

8 . The production method for metal oxide particles according to claim 1 ,
wherein, in the synthesis reaction, an iron salt, an alkali earth metal salt, and the organic compound are mixed with each other in an aqueous solution so as to cause precursor particles of hexagonal ferrite to precipitate.

9 . The production method for metal oxide particles according to claim 1 ,
wherein the conversion of the precursor particles into metal oxide particles is performed through the following steps including: adding a precursor particle solution containing the precursor particles, which are obtained in the synthesis reaction, to a liquid feeding path to which water, which is heated to 300° C. or higher and is pressurized at a pressure of 20 MPa or higher, is continuously fed; and converting the precursor particles into metal oxide particles by continuously feeding a mixed solution containing water and the precursor particle solution to the liquid feeding path while heating the mixed solution to 300° C. or higher and pressurizing the mixed solution at a pressure of 20 MPa or higher.

10 . The production method for metal oxide particles according to claim 1 ,
wherein the metal oxide particles are hexagonal ferrite particles selected from the group consisting of barium ferrite, strontium ferrite, and a mixed crystal of barium ferrite and strontium ferrite.

11 . The production method for metal oxide particles according to claim 1 ,
wherein the organic compound is selected from the group consisting of a carboxylic acid, a carboxylate, an anionic surfactant, and a water-soluble polymer.

12 . The production method for metal oxide particles according to claim 1 ,
wherein the precursor particles of a metal oxide are obtained by performing a reaction of two or more kinds of starting material compounds in the presence of an organic compound, the reaction being one in which the organic compound is added to a reaction solvent to allow the organic compound to be dissolved or suspended therein, and then the two or more kinds of starting material compounds are added to the reaction solvent, to perform the reaction.

Assignees

• Fujifilm Corp

Inventors

• Shirata Masashi
• Hosoya Yoichi

Classifications

• C01P2004/54

  Particles characterised by their aspect ratio, i.e. the ratio of sizes in the longest to the shortest dimension · CPC title

• G11B5/70678 Primary

  Ferrites · CPC title

• C01P2004/64

  Nanometer sized, i.e. from 1-100 nanometer · CPC title

• H01F1/11 Primary

  in the form of particles {(for magnetic record carriers G11B5/70626)} · CPC title

• G11B5/714

  characterised by the dimension of the magnetic particles · CPC title