Abstract

There is provided a method for producing a metal-plated stainless material, the method including performing an acid treatment of treating a stainless steel material with an acidic solution; performing an etching of treating the stainless steel material after the acid treatment with an etching treatment agent; and a modifying the surface of the stainless steel material after the etching into a state suitable for a metal plating process.

First claim

The invention claimed is:

1. A method for producing a metal-plated stainless material, the method comprising:
performing an acid treatment of treating a stainless steel material with an acidic solution;
performing an etching of treating the stainless steel material after the acid treatment with an etching treatment agent; and
modifying a surface of the stainless steel material into a state suitable for a metal plating process, wherein
the modifying includes immersing the stainless steel material in a sulfuric acid aqueous solution, and
the acid treatment comprises treating the stainless steel material with the acidic solution thereby to form an oxide film, wherein the oxide film has a lower density than that of a passivation film existing on the surface of the stainless steel material before the acid treatment.

2. The method for producing a metal-plated stainless material according to claim 1 , wherein the acid treatment includes treating the stainless steel material with the acidic solution thereby to grow an oxide film thicker than that before the acid treatment, wherein the oxide film includes the passivation film on the surface of the stainless steel material.

3. The method for producing a metal-plated stainless material according to claim 1 , wherein the acidic solution comprises a solution that contains any one of hydrochloric acid, ammonium hydrogen fluoride, sulfuric acid, and nitric acid or a mixture thereof.

4. The method for producing a metal-plated stainless material according to claim 1 , wherein the etching treatment agent comprises any one of nitric acid and sulfuric acid or a mixture thereof.

5. The method for producing a metal-plated stainless material according to claim 1 , wherein the modifying includes immersing the stainless steel material in a sulfuric acid aqueous solution at a temperature of 50° C. to 70° C. for 5 to 600 seconds, wherein the sulfuric acid aqueous solution has a sulfuric acid concentration of 20 to 25 vol %.

6. The method for producing a metal-plated stainless material according to claim 1 , further comprising
performing a metal plating for the stainless steel material after the modifying.

7. A method for producing a metal-plated stainless material, the method comprising:
performing a film thickness reduction of reducing a thickness of an oxide film generated on a surface of a stainless steel material using an etching agent;
performing a film growth of growing the thickness-reduced oxide film using an oxidation treatment agent; and
modifying the surface of the stainless steel material of which the oxide film grows in the film growth step into a state suitable for a metal plating process, wherein
the modifying includes immersing the stainless steel material in a sulfuric acid aqueous solution.

8. The method for producing a metal-plated stainless material according to claim 7 , wherein the etching agent comprises any one of ammonium hydrogen fluoride, sulfuric acid, nitric acid, and hydrochloric acid or a mixture thereof.

9. The method for producing a metal-plated stainless material according to claim 7 , wherein the oxidation treatment agent comprises any one of nitric acid and sulfuric acid or a mixture thereof.

10. The method for producing a metal-plated stainless material according to claim 7 , wherein the modifying includes immersing the stainless steel material in a sulfuric acid aqueous solution at a temperature of 50° C. to 70° C. for 5 to 600 seconds, wherein the sulfuric acid aqueous solution has a sulfuric acid concentration of 20 to 25 vol %.

11. The method for producing a metal-plated stainless material according to claim 7 , further comprising
performing a metal plating for the stainless steel material after the modifying.

12. The method for producing a metal-plated stainless material according to claim 7 , wherein the etching agent comprises ammonium hydrogen fluoride.

Assignees

• Toyo Kohan Co Ltd

Inventors

• Yoshida Takahiro
• Tsuruda Tomoyuki

Classifications

• C23C18/1837 Primary

  Multistep pretreatment · CPC title

• C23C18/1844 Primary

  with use of organic or inorganic compounds other than metals, first · CPC title

• H01R13/03

  characterised by the material, e.g. plating, or coating materials · CPC title

• C23C22/50

  Treatment of iron or alloys based thereon · CPC title

• H01M8/021

  Alloys based on iron · CPC title