Polymer modified asphalt roofing material

Patent metadata

Field	Value
Publication number	US-11851889-B2
Application number	US-202117530576-A
Country	US
Kind code	B2
Filing date	Nov 19, 2021
Priority date	Dec 15, 2017
Publication date	Dec 26, 2023
Grant date	Dec 26, 2023

Abstract

A shingle coating asphalt composition is provided that is produced from a paving grade asphalt. The asphalt composition comprises a paving-grade asphalt that has been modified with one or more polymer additives; and a secondary additive comprising one or more of a viscosity reducing agent, a wax, a salt of a fatty acid ester, and an amide of a fatty acid. The shingle coating asphalt coating composition is used to make a shingle. The shingle includes a substrate, the asphalt, and roofing granules.

First claim

The invention claimed is:

1. A roofing shingle comprising:
a substrate having a first surface and an opposing second surface;
a polymer-modified asphalt coating on the first surface of the substrate, wherein the polymer-modified asphalt comprises:
from 40 wt. % to 80 wt. % of a filler, based on the total weight of the polymer-modified asphalt coating,
from 1 wt. % to 13 wt. % of a polymer additive, based on the total weight of a non-filler portion of the polymer-modified asphalt coating; and
asphalt; and

a strip of nail zone reinforcement material adhered to the polymer-modified asphalt coating, the strip of nail zone reinforcement material having a width of 0.5 inches to 2.0 inches and a length that is greater than the width and runs in a machine direction of the shingle,
wherein the roofing shingle meets or surpasses the UL2218 Class 3 impact resistance standard, wherein the roofing shingle is free from an integrated polymeric backing that imparts impact resistance to the roofing shingle, and
wherein a cutting force required to cut the shingle through the nail zone reinforcement material is less than a cutting force required to cut through a nail zone reinforcement material area of an otherwise identical shingle having the same nail zone reinforcement material and an oxidized asphalt excluding the polymer additive.

2. The roofing shingle of claim 1 , wherein the strip of nail zone reinforcement material is a woven or nonwoven fabric.

3. The roofing shingle of claim 1 , wherein the polymer-modified asphalt includes the polymer additive in an amount from 2 wt. % to 7 wt. % based on the total weight of the non-filler portion of the polymer-modified asphalt coating.

4. The roofing shingle of claim 1 , wherein the polymer additive is selected from the group consisting of atactic polypropylene, isotactic polypropylene, styrene-butadiene block copolymer, chloroprene rubber, amorphous polyolefin, styrene butadiene latex, natural and reclaimed rubbers, butadiene rubber, acrylonitrile-butadiene rubber, isoprene rubber, styrene-polyisoprene, butyl rubber, ethylene propylene rubber, ethylene propylene diene monomer rubber, polyisobutylene, chlorinated polyethylene (CPE), styrene ethylene-butylene-styrene, hydrogenated styrene butadiene block copolymer, vinylacetate/polyethylene, and mixtures thereof.

5. The roofing shingle of claim 4 , wherein the polymer additive is selected from the group consisting of styrene-butadiene rubber, styrene ethylene-butylene-styrene, reclaimed rubber, and mixtures thereof.

6. The roofing shingle of claim 1 , wherein the polymer modified asphalt further includes a viscosity reducing agent selected from the group consisting of a wax, a salt of a fatty acid ester, an amide of a fatty acid, and mixtures thereof.

7. The roofing shingle of claim 1 , wherein a longitudinal adhesion of the strip of nail zone reinforcement material to the polymer-modified asphalt coating is greater than a longitudinal adhesion of an otherwise identical shingle having the same strip of nail zone reinforcement material and an oxidized asphalt without the polymer additive.

8. The roofing shingle of claim 1 , wherein a longitudinal adhesion of the strip of nail zone reinforcement material to the polymer-modified asphalt coating is greater than 1.25 lbf.

9. The roofing shingle of claim 1 , wherein a traverse adhesion of the strip of nail zone reinforcement material to the polymer-modified asphalt coating is greater than a traverse adhesion of an otherwise identical shingle having the same strip of nail zone reinforcement material and an oxidized asphalt without the polymer additive.

10. The roofing shingle of claim 1 , wherein a transverse adhesion of the strip of nail zone reinforcing material to the polymer-modified asphalt coating is greater than 5 lbf.

11. The roofing shingle of claim 1 , wherein the roofing shingle meets or surpasses the UL2218 Class 4 impact resistance standard.

12. The roofing shingle of claim 1 , wherein the substrate includes a headlap portion, a tab portion, and a boundary where the headlap portion meets the tab portion, and the strip of nail zone reinforcement is located on the headlap portion a distance of 0.125 inches to 0.375 inches from the boundary where the headlap portion meets the tab portion.

13. A roofing shingle comprising:
an asphalt coated overlay sheet comprising a headlap portion and a tab portion;
an asphalt coated underlay sheet secured to the overlay sheet such that a region of the underlay sheet overlaps a region of the headlap portion of the overlay sheet;
a strip of nail zone reinforcement material adhered to the headlap portion of the overlay sheet; and
a plurality of granules adhered to the asphalt coated overlay sheet and to the asphalt coated underlay sheet,
wherein at least one of the asphalt coated overlay sheet and the asphalt coated underlay sheet include an asphalt coating that is a polymer-modified asphalt comprising:
from 40 wt. % to 80 wt. % of a filler, based on the total weight of the polymer-modified asphalt coating, and
from 1 wt. % to 13 wt. % of a polymer additive based on the total weight of the non-filler portion of the polymer-modified asphalt coating,

wherein the strip of nail zone reinforcement material is adhered to the overlay sheet through the adhesive nature of the asphalt coating,
wherein the strip of nail zone reinforcement material has a width and a length, and wherein the width is from 0.5 inches to 2.0 inches and the length is greater than the width and runs in a machine direction of the shingle,
wherein a longitudinal adhesion of the strip of nail zone reinforcement material to the polymer-modified asphalt coating is greater than a longitudinal adhesion of an otherwise identical shingle having the same strip of nail zone reinforcement material and an oxidized asphalt without the polymer additive;
wherein the roofing shingle meets or surpasses the UL2218 Class 3 impact resistance standard, and wherein the roofing shingle is free from an integrated polymeric backing that imparts impact resistance to the roofing shingle.

14. The roofing shingle of claim 13 , wherein strip of nail zone reinforcement material is positioned on the headlap portion of the overlay sheet such that the nail zone reinforcement material is not over the region of the underlay sheet that overlaps a region of the headlap portion of the overlay sheet.

15. The roofing shingle of claim 13 , wherein strip of nail zone reinforcement material is positioned on the headlap portion of the overlay sheet such that the nail zone reinforcement material is over the region of the underlay sheet that overlaps a region of the headlap portion of the overlay sheet.

16. The roofing shingle of claim 13 , wherein the strip of nail zone reinforcement material is a woven or nonwoven fabric.

17. The roofing shingle of claim 13 , wherein the polymer-modified asphalt includes the polymer additive in an amount from 2 wt. % to 7 wt. % based on the total weight of the non-filler portion of the polymer-modified asphalt coating.

18. The roofing shingle of claim 13 , wherein the polymer additive is selected from the group consisting of atactic polypropylene, isotactic polypropylene, styrene-butadiene block copolymer, chloroprene rubber, amorphous polyolefin, styrene butadiene latex, natural and reclaimed rubbers, butadiene rubber, acrylonitrile-butadiene rubber, isoprene rubber, styrene-polyisoprene, butyl rubber, ethylene propylene rubber, ethylene propylene diene monomer rubber, polyisobutylene, chlorinated polyethylene (CPE), styrene e

Assignees

• Owens Corning Intellectual Capital Llc

Inventors

• Latorre Carmen Anthony
• Honsvick Jacob Paul
• Kasprzak Christopher Patrick
• Buckwalter Daniel James
• Harrington Edward R
• Davis Jonathan Ross
• Lewandowski Laurand Henry
• Ploense David Michael
• Smith William Edwin
• Schweiger Scott W

Classifications

• E04D7/005 Primary

  characterised by loose or embedded gravel or granules as an outer protection of the roof covering · CPC title

• C08K3/013

  Fillers, pigments or reinforcing additives · CPC title

• C08K5/01

  Hydrocarbons {(C08K5/0091 takes precedence)} · CPC title

• C08L95/00

  Compositions of bituminous materials, e.g. asphalt, tar, pitch · CPC title

• C09D195/00

  Coating compositions based on bituminous materials, e.g. asphalt, tar, pitch · CPC title