Process for producing polymerizable composition for optical material and polymerizable composition for optical material

Patent metadata

Field	Value
Publication number	US-10519060-B2
Application number	US-201615743383-A
Country	US
Kind code	B2
Filing date	Aug 5, 2016
Priority date	Aug 6, 2015
Publication date	Dec 31, 2019
Grant date	Dec 31, 2019

Abstract

A process for producing a polymerizable composition for an optical material of the present invention includes a step of mixing (A) at least one kind of thiol compound having at least two mercapto groups, (B) a tin compound represented by general formula (1), and (C) at least one kind of isocyanate compound having at least two isocyanato groups, in which the polymerizable composition for an optical material obtained in the above step has a haze value of 0.05 or less.

(R 4 ) c —Sn—X 4-c   (1)

First claim

The invention claimed is:

1. A process for producing a polymerizable composition for an optical material, comprising:
a step of mixing (A) at least one kind of thiol compound having at least two mercapto groups, (B) a tin compound represented by general formula (1), and (C) at least one kind of isocyanate compound having at least two isocyanato groups, to obtain a polymerizable composition for an optical material having a haze value of 0.05 or less,
(R 4 ) c —Sn—X 4-c   (1)

wherein, in general formula (1), R 4 represents an alkyl group having 1 to 8 carbon atoms, X represents a fluorine atom, a chlorine atom, a bromine atom, or —O—C(═O)—R 5 , R 5 represents an alkyl group having 1 to 11 carbon atoms, and c represents an integer of 1 to 3, and
wherein the isocyanate compound (C) is at least one kind of alicyclic isocyanate, aliphatic isocyanate and heterocyclic isocyanate.

2. A process for producing a polymerizable composition for an optical material, the method comprising:
a step of mixing (A) at least one kind of thiol compound having at least two mercapto groups and (B) a tin compound represented by general formula (1); and
a step of mixing (C) at least one kind of isocyanate compound having at least two isocyanato groups and the mixed solution obtained in the above step to obtain a polymerizable composition for an optical material,
wherein a haze value of the mixed solution including the component (A) and the component (B) is 0.05 or less,
(R 4 ) c —Sn—X 4-c   (1)

wherein, in general formula (1), R 4 represents an alkyl group having 1 to 8 carbon atoms, X represents a fluorine atom, a chlorine atom, a bromine atom, or —O—C(═O)—R 5 , R 5 represents an alkyl group having 1 to 11 carbon atoms, and c represents an integer of 1 to 3, and
wherein the isocyanate compound (C) is at least one kind of alicyclic isocyanate, aliphatic isocyanate and heterocyclic isocyanate.

3. A process for producing a polymerizable composition for an optical material, the method comprising:
a step of mixing (B) a tin compound represented by general formula (1) and (C) at least one kind of isocyanate compound having at least two isocyanato groups; and
a step of mixing the mixed solution obtained in the above step and (A) at least one kind of thiol compound having at least two mercapto groups to obtain a polymerizable composition for an optical material,
wherein a haze value of the mixed solution including the component (B) and the component (C) is 0.05 or less,
(R 4 ) c —Sn—X 4-c   (1)

wherein, in general formula (1), R 4 represents an alkyl group having 1 to 8 carbon atoms, X represents a fluorine atom, a chlorine atom, a bromine atom, or —O—C(═O)—R 5 , R 5 represents an alkyl group having 1 to 11 carbon atoms, and c represents an integer of 1 to 3, and
wherein the isocyanate compound (C) is at least one kind of alicyclic isocyanate, aliphatic isocyanate and heterocyclic isocyanate.

4. The process for producing a polymerizable composition for an optical material according to claim 1 ,
wherein the isocyanate compound (C) includes at least one kind of compound selected from 1,6-hexamethylene diisocyanate, 1,5-pentamethylene diisocyanate, m-xylylene diisocyanate, isophorone diisocyanate, 1,3-bis(isocyanatomethyl)cyclohexane, 1,4-bis(isocyanatomethyl)cyclohexane, dicyclohexyl methane diisocyanate, 2,5-bis(isocyanatomethyl)bicyclo-[2.2.1]-heptane, and 2,6-bis(isocyanatomethyl)bicyclo-[2.2.1]-heptane.

5. The process for producing a polymerizable composition for an optical material according to claim 1 ,
wherein the thiol compound (A) includes at least one kind of compound selected from 4,6-bis(mercaptomethylthio)-1,3-dithiane, 2-(2,2-bis(mercaptomethylthio)ethyl)-1,3-dithietane, pentaerythritol tetrakis (3-mercaptopropionate), pentaerythritol tetrakis (2-mercaptoacetate), trimethylolpropane tris(3-mercaptopropionate), trimethylolpropane tris(2-mercaptoacetate), 4-mercaptomethyl-1,8-dimercapto-3,6-dithiaoctane, 2,5-bismercaptomethyl-1,4-dithiane, 1,1,3,3-tetrakis (mercaptomethylthio)propane, 5,7-dimercaptomethyl-1,11-dimercapto-3,6,9-trithiaundecane, 4,7-dimercaptomethyl-1,11-dimercapto-3,6,9-trithiaundecane, 4,8-dimercaptomethyl-1,11-dimercapto-3,6,9-trithiaundecane, ethylene glycol bis(3-mercaptopropionate), diethylene glycol bis(3-mercaptopropionate), ethylene glycol bis(2-mercaptoacetate), and diethylene glycol bis(2-mercaptoacetate).

6. A polymerizable composition for an optical material produced by the process according to claim 1 ,
wherein the polymerizable composition for an optical material has a haze value of 0.05 or less.

7. A polymerizable composition for an optical material produced by the process according to claim 2 .

8. A polymerizable composition for an optical material produced by the process according to claim 3 .

9. The polymerizable composition for an optical material according to claim 6 ,
wherein the isocyanate compound (C) includes at least one kind of compound selected from 1,6-hexamethylene diisocyanate, 1,5-pentamethylene diisocyanate, m-xylylene diisocyanate, isophorone diisocyanate, 1,3-bis(isocyanatomethyl)cyclohexane, 1,4-bis(isocyanatomethyl)cyclohexane, dicyclohexyl methane diisocyanate, 2,5-bis(isocyanatomethyl)bicyclo-[2.2.1]-heptane, and 2,6-bis(isocyanatomethyl)bicyclo-[2.2.1]-heptane.

10. The polymerizable composition for an optical material according to claim 9 ,
wherein the isocyanate compound (C) includes at least one kind of compound selected from 1,6-hexamethylene diisocyanate, 2,5-bis(isocyanatomethyl)bicyclo-[2.2.1]-heptane, and 2,6-bis(isocyanatomethyl)bicyclo-[2.2.1]-heptane.

11. The polymerizable composition for an optical material according to claim 6 ,
wherein the thiol compound (A) includes at least one kind of compound selected from 4,6-bis(mercaptomethylthio)-1,3-dithiane, 2-(2,2-bis(mercaptomethylthio)ethyl)-1,3-dithietane, pentaerythritol tetrakis (3-mercaptopropionate), pentaerythritol tetrakis (2-mercaptoacetate), trimethylolpropane tris(3-mercaptopropionate), trimethylolpropane tris(2-mercaptoacetate), 4-mercaptomethyl-1,8-dimercapto-3,6-dithiaoctane, 2,5-bismercaptomethyl-1,4-dithiane, 1,1,3,3-tetrakis (mercaptomethylthio)propane, 5,7-dimercaptomethyl-1,11-dimercapto-3,6,9-trithiaundecane, 4,7-dimercaptomethyl-1,11-dimercapto-3,6,9-trithiaundecane, 4,8-dimercaptomethyl-1,11-dimercapto-3,6,9-trithiaundecane, ethylene glycol bis(3-mercaptopropionate), diethylene glycol bis(3-mercaptopropionate), ethylene glycol bis(2-mercaptoacetate), and diethylene glycol bis(2-mercaptoacetate).

12. The polymerizable composition for an optical material according to claim 11 ,
wherein the thiol compound (A) includes at least one kind of compound selected from 4-mercaptomethyl-1,8-dimercapto-3,6-dithiaoctane, and pentaerythritol tetrakis (3-mercaptopropionate).

13. A method for manufacturing a plastic lens comprising:
a step of injecting the polymerizable composition for an optical material according to claim 6 into a lens-casting mold;
a step of polymerizing the polymerizable composition for an optical material; and
a step of releasing the resin obtained in the above step from the lens-casting mold to obtain a molded product.

14. A molded product obtained by curing the polymerizable composition for an optical material according to claim 6 .

15. An optical material comprised of the molded product according to claim 14 .

16. A lens comprised of the optical material according to claim 15 .

17. A spectacle lens comprised of the lens according to claim 16 .

18. A spectacle lens comprising:
the lens acco

Assignees

• Mitsui Chemicals Inc

Inventors

• Suesugi Kouji
• Shinohara Naoki
• Okazaki Koju

Classifications

• C08G18/38

  having heteroatoms other than oxygen (C08G18/32 takes precedence) · CPC title

• G02B1/04

  made of organic materials, e.g. plastics (G02B1/08 takes precedence) · CPC title

• G02C7/02

  Lenses; Lens systems {; Methods of designing lenses} · CPC title

• G02B1/111

  using layers comprising organic materials · CPC title

• G02B1/14

  Protective coatings, e.g. hard coatings · CPC title