Multilayer coating, production and use thereof for the adhesion of glass panes

Patent metadata

Field	Value
Publication number	US-9752048-B2
Application number	US-201013265746-A
Country	US
Kind code	B2
Filing date	Apr 21, 2010
Priority date	Apr 21, 2009
Publication date	Sep 5, 2017
Grant date	Sep 5, 2017

Abstract

A multilayer coating comprising
(A) a multicoat paint system comprising
(A1) at least one basecoat of a basecoat material comprising at least one melamine resin, and (A2) at least one clearcoat as the topmost coat of the multicoat paint system, and
(B) an adhesive layer of a moisture-curing, isocyanate-based adhesive directly atop the topmost clearcoat layer of the multicoat paint system, wherein (i) all amino resins present in the basecoat material are fully methylolated, fully etherified melamine resins in which at least 90% of the etherified methylol groups are etherified with butanol, and (ii) the basecoat material contains at least 1.0% by weight, based on the total weight of the basecoat material, of at least one polyester binder having a hydroxyl number of at least 240 mg KOH/g and an acid number of not more than 10 mg KOH/g, and also a corresponding basecoat material and method of producing, and use of, the multilayer coating for adhesively bonding glass sheets.

First claim

What is claimed is:

1. A multilayer coating comprising:
(A) a multicoat paint system comprising:
(A1) at least one basecoat of a basecoat material that is water-free and comprises:
at least one amino resin that is a fully methylolated, fully etherified melamine resin in which at least 90% of the etherified methylol groups are etherified with butanol,
at least 1.0% by weight, based on the total weight of the basecoat material, of at least one polyester binder having a hydroxyl number of at least 240 mg KOH/g and an acid number of not more than 10 mg KOH/g,

(A2) at least one clearcoat as a topmost coat of the multicoat paint system; and

(B) an adhesive layer of a moisture-curing, isocyanate-based adhesive directly atop the clearcoat;
wherein the basecoat material comprises no further amino resins.

2. The multilayer coating of claim 1 , wherein the at least one amino resin present in the basecoat material (A1) comprises at least 95% of butanol-etherified methylol groups, based on all of the etherified methylol groups.

3. The multilayer coating of claim 1 , wherein the basecoat material (A1) comprises 8% to 15% by weight, based on the total weight of the basecoat material, of the melamine resin.

4. The multilayer coating of claim 1 , wherein the basecoat material (A1) comprises 1% to 6% by weight, based on the total weight of the basecoat material, of said at least one polyester binder.

5. The multilayer coating of claim 1 , wherein said at least one polyester binder has a hydroxyl number of 270 mg KOH/g to 300 mg KOH/g and an acid number of not more than 5 mg KOH/g.

6. The multilayer coating of claim 1 , wherein said at least one polyester binder comprises structural units which originate from aliphatic, cycloaliphatic and/or aromatic dicarboxylic and/or polycarboxylic acids and from diols and/or polyols.

7. The multilayer coating of claim 1 , wherein said at least one polyester binder has a weight-average molecular weight of 400 to 2500 g/mol.

8. The multilayer coating of claim 1 , which has precisely one basecoat having a dry film thickness of 10 to 25 μm and precisely one clearcoat having a dry film thickness of 25 to 70 μm.

9. The multilayer coating of claim 1 , wherein the at least one polyester has an acid number of from 2.2 mg KOH/g to not more than 5 mg KOH/g.

10. The multilayer coating of claim 1 , wherein the basecoat material (A1) comprises, by weight:
(i) 8% to 15% of the melamine resin;
(ii) 1% to 6% of the one polyester binder;
(iii) 10% to 30% of a further binder; and
(iv) 30% to 70% of an organic solvent.

11. The multilayer coating of claim 1 , wherein said at least one basecoat (A1) has a dry film thickness of 10 to 25 μm.

12. The multilayer coating of claim 11 , wherein said at least one basecoat (A1) has a dry film thickness of 15 to 25 μm.

13. The multilayer coating of claim 1 , wherein said at least one clearcoat has a dry film thickness of 25 to 50 μm.

14. The multilayer coating of claim 13 , wherein said at least one clearcoat has a dry film thickness of 25 to 45 μm.

15. A basecoat material for producing a multilayer coating, the basecoat material being water-free and comprising:
(i) at least one amino resin that is a fully methylolated, fully etherified melamine resin in which at least 90% of the etherified methylol groups are etherified with butanol, and
(ii) at least 1.0% by weight, based on the total weight of the basecoat material, of at least one polyester binder having a hydroxyl number of at least 240 mg KOH/g and an acid number of not more than 10 mg KOH/g,
wherein the basecoat material comprises no further amino resins.

16. The basecoat material of claim 15 comprising, by weight:
(i) 8% to 15% of the melamine resin;
(ii) 1% to 6% of the one polyester binder;
(iii) 10% to 30% of a further binder; and
(iv) 30% to 70% of an organic solvent.

Assignees

• Low Norbert
• Lavalaye Jorn
• Steffens Alexandra
• Basf Coatings Gmbh

Inventors

• Low Norbert
• Lavalaye Jorn
• Steffens Alexandra

Classifications

• Y10T156/10

  Methods of surface bonding and/or assembly therefor · CPC title

• Y10T428/264

  Up to 3 mils · CPC title

• Y10T428/265

  1 mil or less · CPC title

• Y10T428/2848

  Three or more layers · CPC title

• Y10T428/24975

  No layer or component greater than 5 mils thick · CPC title