Method for melt spinning, stretching, and winding a multifilament thread as well as a device for performing the method

Patent metadata

Field	Value
Publication number	US-9428848-B2
Application number	US-99317709-A
Country	US
Kind code	B2
Filing date	May 22, 2009
Priority date	May 23, 2008
Publication date	Aug 30, 2016
Grant date	Aug 30, 2016

Abstract

A method for melt spinning, stretching, and winding a multifilament thread to form an FDY-yarn as well as a device for performing the method are presented. Hereby, a plurality of filaments are first extruded from thermoplastic melt, cooled to a temperature below the glass transition temperature of the thermoplastic material, and gathered to form a filament bundle without adding a preparation fluid. The filament bundle is then drawn-off at a speed above 1,500 m/min., heated to have a temperature above the glass transition temperature of the thermoplastic material, and stretched at a drawing speed above 4,000 m/min. Preparation of the filament bundle with a preparation fluid and winding the thread to form a spool is then performed. The device has the preparation device arranged in a zone of the thread course between the drawing device and the winding device, in which the thread has a thread-running speed above 4,000 m/min.

First claim

The invention claimed is:

1. A method for melt spinning, drawing and winding a multifilament thread to form a Fully Drawn Yarn, the method performed in an apparatus having (i) a yarn guide, (ii) a drawing device, (iii) a preparation device, and (iv) a winding device, which are arranged in an order in which the drawing device is disposed after the yarn guide and before the preparation device from a process standpoint, and in which the preparation device is disposed after the drawing device and before the winding device from the process standpoint, the method comprising:
extruding a plurality of filaments from thermoplastic material;
cooling the filaments to a temperature below the glass transition temperature of said thermoplastic material;
in the yarn guide, after cooling the filaments, gathering the filaments to form a filament bundle without adding any fluid;
in the drawing device which is disposed after the yarn guide and before the preparation device, drawing-off the filament bundle at a draw-off speed in the range above 1,500 m/min;
in the drawing device which is disposed after the yarn guide and before the preparation device, heating the filament bundle to have a temperature above the glass transition temperature of the thermoplastic material and drawing the filament bundle at a drawing speed in the range above 3,500 m/min;
in the preparation device which is disposed after the drawing device and before the winding device, preparing the filament bundle with a preparation fluid; and
in the winding device, winding said thread to form a spool.

2. Method according to claim 1 , wherein the filament bundle is prepared in a piece of yarn tensioned between two driven godets.

3. Method according to claim 2 , wherein the filament bundle is guided at a curved contact surface of a perforated plate having fine pores, at the bottom side of which the preparation fluid is being continuously supplied.

4. Method according to claim 1 , wherein for drawing-off and drawing, the filament bundle is guided having single wraparounds at the circumference of driven godets, the filament bundle being guided in a circumferential guiding groove at least one draw-off godet.

5. Method according to claim 1 , wherein the filament bundle is heated by contacting a heated surface and without contact by radiant heat or by convection.

6. Method according to claim 1 , wherein the thread is mingled in a piece of yarn tensioned between two driven godets prior to winding, and in that the mingling creates an amount of at least 10 interweaving knots for every meter thread length.

7. Method according to claim 6 , wherein a thread tension for mingling is created in the piece of yarn of the thread by adjusting a differential speed at both godets.

8. Method according to claim 1 , wherein a twist is created at the filament bundle after gathering and prior to drawing-off the filament bundle.

9. Method according to claim 1 , wherein the filament bundle is heated by contacting a heated surface.

10. Method according to claim 1 , wherein drawing the filament bundle at a drawing speed in the range above 3,500 m/min includes drawing the filament bundle at a drawing speed in the range above 4,000 m/min.

11. Method according to claim 1 wherein the yarn guide is constructed and arranged to output the filament bundle in a freshly extruded dry state; and wherein drawing-off the filament bundle at the draw-off speed includes:
in the drawing device, drawing the filament bundle in the freshly extruded dry state prior to delivering the filament bundle to the preparation device.

12. Method according to claim 11 wherein drawing the filament bundle in the freshly extruded dry state prior to delivering the filament bundle to the preparation device includes:
performing a warm stretching operation which heats the filament bundle in the freshly extruded dry state above the glass transition temperature of the thermoplastic material.

13. Method according to claim 12 wherein preparing the filament bundle with the preparation fluid includes:
in the preparation device, humidifying the filament bundle in the freshly extruded dry state.

14. Method according to claim 1 wherein the acts of drawing-off the filament bundle at the draw-off speed in the range above 1,500 m/min and drawing the filament bundle at the drawing speed in the range above 3,500 m/min are performed after performing the acts of extruding the filaments, cooling the filaments, and gathering the filaments, and
wherein the act of preparing the filament bundle with the preparation fluid is performed after performing the acts of drawing-off the filament bundle at the draw-off speed in the range above 1,500 m/min and drawing the filament bundle at the drawing speed in the range above 3,500 m/min.

15. Method as in claim 14 wherein no fluid is added to the filaments or the filament bundle until after performing the acts of drawing-off the filament bundle at the draw-off speed in the range above 1,500 m/min and drawing the filament bundle at the drawing speed in the range above 3,500 m/min.

16. Method for melt spinning, drawing and winding a multifilament thread to form a Fully Drawn Yarn, the method comprising:
(A) extruding a plurality of filaments from thermoplastic material;
(B) subsequently to extruding said plurality of filaments, cooling the filaments to a temperature below the glass transition temperature of said thermoplastic material;
(C) subsequently to cooling said filaments, gathering the filaments to form a filament bundle without adding any fluid;
(D) subsequently to gathering said filaments to form said filament bundle, drawing-off the filament bundle;
(E) subsequently to drawing-off said filament bundle, heating the filament bundle to have a temperature above the glass transition temperature of the thermoplastic material and drawing the filament bundle;
(F) subsequently to heating and drawing said filament bundle, preparing the filament bundle with a preparation fluid; and
(G) subsequently to preparing said filament bundle, winding said thread to form a spool,
wherein no fluid is added to the filaments or the filament bundle until after performing the act of drawing the filament bundle in step (E).

17. Method as in claim 16 ,
wherein said drawing-off the filament bundle in step (D) occurs at a draw-off speed in the range above 1,500 m/min; and
wherein said drawing of the filament bundle in step (E) occurs at a drawing speed in the range above 3,500 m/min.

Assignees

• Weigend Helmut
• Meise Hansjörg
• Schulz Detlev
• Oerlikon Textile Gmbh & Co Kg

Inventors

• Weigend Helmut
• Meise Hansjörg
• Schulz Detlev

Classifications

• D01D11/06 Primary

  Coating with spinning solutions or melts · CPC title

• D01D5/16

  using rollers, or like mechanical devices, e.g. snubbing pins · CPC title

• D01D13/02

  Elements of machines in combination · CPC title

• D01D10/02

  Heat treatment (heating for finishing D02J13/00) · CPC title

• D01D10/0436

  while in continuous movement (forwarding filamentary material B65H51/00) · CPC title