Temporarily repositionable pressure sensitive adhesive blends

Patent metadata

Field	Value
Publication number	US-9359531-B2
Application number	US-86783309-A
Country	US
Kind code	B2
Filing date	Jan 19, 2009
Priority date	Feb 21, 2008
Publication date	Jun 7, 2016
Grant date	Jun 7, 2016

Abstract

Temporarily repositionable pressure sensitive adhesive compositions which are blends of a silicone-modified pressure sensitive adhesive component, a high Tg polymer component and a crosslinker are presented. The silicone-modified pressure sensitive adhesive includes a copolymer that is the reaction product of an acidic or basic monomer, a (meth)acrylic or vinyl monomer, and a silicone macromer. The high Tg polymer component contains acid or base functionality such that when mixed, the silicone-modified pressure sensitive adhesive component and the high Tg polymer component form an acid-base interaction.

First claim

What is claimed is:

1. An adhesive composition comprising a blend of:
a majority of a silicone-modified pressure sensitive adhesive component comprising:
an acidic or basic functional copolymer comprising the reaction product of an acidic or basic monomer, a (meth)acrylic or vinyl monomer, and a silicone macromer;
a high Tg polymer comprising an acid or base functionality;
and a crosslinker;
wherein the functionality of the silicone-modified pressure sensitive adhesive component and the functionality of the high Tg polymer form an acid-base interaction when mixed and the composition is a pressure sensitive adhesive.

2. The adhesive composition of claim 1 wherein the composition is optically clear on visual observation.

3. The adhesive composition of claim 1 wherein the high Tg polymer has a glass transition temperature greater than 20° C.

4. The adhesive composition of claim 1 wherein the high Tg polymer comprises a monomer selected from the group consisting of vinyl esters, (meth)acrylamide, styrenes, (meth)acrylontriles, substituted styrenes, vinyl halides, vinyl propionate, (meth)acrylates, and mixtures thereof.

5. The adhesive composition of claim 1 wherein the high Tg polymer is a basic copolymer.

6. The adhesive composition of claim 1 wherein the silicone-modified pressure sensitive adhesive is a (meth)acrylate copolymer formed from free-radically polymerizable monomers selected from the group of (meth)acrylates, vinyl monomers, and macromers.

7. The adhesive composition of claim 1 wherein the crosslinker is selected from the group consisting of multifunctional aziridine, peroxides, benzophenones, triazines, monoethylenically unsaturated mono-, di-, and trialkoxy silane compounds, diacrylates, triacrylates, tetraacrylates, isocyanates, epoxies, and mixtures thereof.

8. The adhesive composition of claim 1 wherein the silicone-modified pressure sensitive adhesive component comprises from 70 to 95 percent based on the weight of the total composition.

9. An article comprising:
a substrate, and
a pressure sensitive adhesive composition coated on at least one surface of the substrate, the pressure sensitive adhesive composition comprising a blend of:
a majority of a silicone-modified pressure sensitive adhesive component comprising:
an acidic or basic functional copolymer comprising the reaction product of an acidic or basic monomer, a (meth)acrylic or vinyl monomer, and a silicone macromer;
a high Tg polymer comprising an acid or base functionality;
and a crosslinker; wherein the functionality of the silicone-modified pressure sensitive adhesive component and the functionality of the high Tg polymer form an acid-base interaction when mixed.

10. The article of claim 9 wherein the substrate is selected from the group consisting of a release liner, a film, a sheet, a tape backing, and a rigid material.

11. A multi-layer assembly coated with an adhesive composition comprising a mixture of: a majority of a silicone-modified pressure sensitive adhesive component comprising at least one polymer with an acid or base functionality; a high Tg polymer comprising an acid or base functionality; and a crosslinker, wherein the functionality of the silicone-modified pressure sensitive adhesive component and the functionality of the high Tg polymer form an acid-base interaction when mixed, and wherein the adhesive composition is an optically clear pressure sensitive adhesive that bonds at least two layers together.

12. The multilayer assembly of claim 11 wherein the layers are selected from the group consisting of a release liner, a film, a sheet, a tape backing, and a rigid material.

13. The multilayer assembly of claim 11 wherein one of the layers is an outgassing layer.

14. A method of preparing a multi-layer article, the method comprising:
coating onto a substrate an adhesive composition comprising:
a mixture of: a majority of a silicone-modified pressure sensitive adhesive component comprising at least one polymer comprising an acid or base functionality; a high Tg polymer comprising an acid or base functionality; and a crosslinker, wherein the functionality of the silicone-modified pressure sensitive adhesive component and the functionality of the high Tg polymer form an acid-base interaction when mixed, and the composition is a pressure sensitive adhesive.

15. The method of claim 14 further comprising the step of laminating the adhesive coated substrate on a second substrate.

16. The method of claim 15 , further comprising the step of repositioning the adhesive coated substrate on the second substrate.

17. The method of claim 14 , wherein the adhesive composition is crosslinked after coating the adhesive composition on the substrate.

18. The method of claim 15 wherein the initial 180° Peel Adhesion upon lamination to the second substrate is in the range of 0.1-5 N/dm and 180° Peel Adhesion after 24 hour dwell is in the range of 50-100 N/dm.

19. A blend comprising:
a silicone-modified pressure sensitive adhesive component comprising an acidic or basic functional copolymer comprising the reaction product of an acidic or basic monomer, a (meth)acrylic or vinyl monomer, and a silicone macromer; and
a high Tg polymer additive comprising an acid or base functionality, wherein the functionality of the silicone-modified pressure sensitive adhesive component and the functionality of the high Tg polymer form an acid-base interaction when mixed.

20. The blend of claim 19 , further comprising a solvent.

Assignees

• Sherman Audrey A
• Winkler Wendi J
• 3M Innovative Properties Co

Inventors

• Sherman Audrey A
• Winkler Wendi J

Classifications

• C09J133/14

  of esters containing halogen, nitrogen, sulfur or oxygen atoms in addition to the carboxy oxygen · CPC title

• C09J2205/114

  Chemistry & Metallurgy · mapped topic

• C09J2433/00

  Presence of (meth)acrylic polymer · CPC title

• C09J133/10

  Homopolymers or copolymers of methacrylic acid esters · CPC title

• Y10T428/2891

  including addition polymer from alpha-beta unsaturated carboxylic acid [e.g., acrylic acid, methacrylic acid, etc.] Or derivative thereof · CPC title