Metal pretreatment composition containing zirconium, copper, and metal chelating agents and related coatings on metal substrates

Patent metadata

Field	Value
Publication number	US-9284460-B2
Application number	US-201313796585-A
Country	US
Kind code	B2
Filing date	Mar 12, 2013
Priority date	Dec 7, 2010
Publication date	Mar 15, 2016
Grant date	Mar 15, 2016

Abstract

Disclosed is a zirconium-based metal pretreatment coating composition that includes a metal chelator that chelates copper in the metal pretreatment coating composition and thereby improves adhesion of paints to a metal substrate coated with the pretreatment coating composition. The pretreatment coating composition has a longer pot life than one without the metal chelator and therefore can accommodate a wide latitude of application times. The chelating agent is present in a sufficient amount to ensure that in the deposited pretreatment coating on the metal substrate the average total atomic % of copper to atomic % of zirconium is equal to or less than 1.1. The pretreatment coating composition is useful for treating a variety of metal substrates.

First claim

We claim:

1. A zirconium-based metal pretreatment coating composition comprising water and dissolved Zr, a source of fluoride, a copper chelating agent, optionally materials comprising one or more of silicon, boron and yttrium and optional added dissolved Cu, wherein the composition has a pH in the range of 6.0 to 9.0.

2. The zirconium-based metal pretreatment coating composition of claim 1 wherein the copper chelating agent is capable of reducing amounts of copper deposited in a zirconium based coating on a metal substrate by contact with the zirconium based metal pretreatment coating composition, the copper chelating agent present in an amount sufficient to thereby produce an average total ratio of atomic % of Cu to atomic % of Zr in the coating deposited on the metal substrate that is in the range of 0.0001 and 1.1.

3. The zirconium-based metal pretreatment coating composition according to claim 1 , comprising:
A.) 50 to 300 ppm of said dissolved Zr,
B.) 0 to 50 ppm of said added dissolved Cu,
C.) 0 to 100 ppm of SiO 2 ,
D.) 150 to 2000 ppm of total Fluoride,
E.) 10 to 100 ppm of free Fluoride and
F.) at least 10 ppm of said copper chelating agent.

4. The zirconium-based metal pretreatment coating composition according to claim 3 , wherein the added dissolved Cu is present in the coating composition and the copper chelating agent is present in an amount of 25 to 1500 ppm.

5. The zirconium-based metal pretreatment coating composition according to claim 3 , wherein said copper chelating agent is selected from molecules having multiple carboxylic and/or phosphonic functional groups.

6. The zirconium-based metal pretreatment coating composition according to claim 3 , wherein said copper chelating agent is selected from the group consisting of aminosalicylic acid, ascorbic acid, aspartic acid, benzoic acid, citric acid, cyanuric acid, diethylenetriamine-pentamethylene phosphonic acid, dihydroxybenzoic acid, dimethylenetriaminepentaacetic acid, ethylenediaminetetraacetic acid, gluconic acid, glutamic acid, hydroxyacetic acid, hydroxyethylidene diphosphonic acid, hydroxyglutamic acid, iminodisuccinic acid, kojic acid, lactic acid, malonic acid, nitrilotriacetic acid, nitrobenzenesulfonic acid, nitrosalicylic acid, oxalic acid, polyacrylic acid, polyaspartic acid, salicylic acid, tartaric acid, and salts of said acids.

7. The zirconium-based metal pretreatment coating composition according to claim 3 , wherein the copper chelating agent comprises tartaric acid and/or salts thereof.

8. A method for improving paint adhesion to a metal substrate comprising the steps of:
a) optionally cleaning a metal substrate;
b) applying to the metal substrate a zirconium-based metal pretreatment coating composition according to any one of the preceding claims,
thereby forming a pretreatment coating on the metal substrate;
wherein the copper chelating agent is present in said zirconium-based metal pretreatment coating composition in an amount sufficient to result in an average total ratio of atomic % of Cu to atomic % of Zr in the pretreatment coating deposited on the metal substrate is equal to or less than 1.1; and
c) applying a paint to the metal pretreatment coated metal substrate.

9. A method for improving paint adhesion to a metal substrate that is subjected to a pretreatment with a zirconium-based pretreatment coating composition comprising the steps of:
a) contacting a metal substrate with a pre-rinse comprising a copper chelating agent, and optionally copper, prior to application of a zirconium-based pretreatment coating composition to the metal substrate;
b) applying to the metal substrate a zirconium-based metal pretreatment coating composition comprising dissolved Zr, a source of fluoride, optionally materials comprising one or more of silicon, boron and yttrium and optional added dissolved Cu, wherein the composition has a pH in the range of 6.0 to 9.0, thereby forming a pretreatment coating on the metal substrate;
wherein the copper chelating agent is present in the pre-rinse in an amount sufficient to control the amount of copper deposited onto the metal substrate by the zirconium-based pretreatment coating composition such that the average total ratio of atomic % of Cu to atomic % of Zr in the pretreatment coating deposited on the metal substrate is equal to or less than 1.1.

10. The method for improving paint adhesion to a metal substrate according to claim 8 wherein the copper chelating agent is present in an amount of at least 10 ppm and at most 2000 ppm.

11. The method for improving paint adhesion to a metal substrate according to claim 9 wherein the copper chelating agent is present in an amount of at least 10 ppm and at most 2000 ppm.

12. The zirconium-based metal pretreatment coating composition according to claim 2 , comprising:
A.) 50 to 300 ppm of said dissolved Zr,
B.) 0 to 50 ppm of said added dissolved Cu,
C.) 0 to 100 ppm of SiO 2 ,
D.) 150 to 2000 ppm of total Fluoride,
E.) 10 to 100 ppm of free Fluoride and
F.) at least 10 ppm of said copper chelating agent.

13. The zirconium-based metal pretreatment coating composition according to claim 1 or 2 wherein silicon; the added dissolved Cu; and one of boron or yttrium are present in the coating composition.

14. The zirconium-based metal pretreatment coating composition according to claim 13 wherein the copper chelating agent is present in an amount of at least 10 ppm and at most 2000 ppm.

15. The zirconium-based metal pretreatment coating composition of claim 1 , wherein the composition is free of added dissolved Cu.

16. A zirconium-based metal pretreatment coating composition comprising water and dissolved Zr, a source of fluoride, a copper chelating agent, silicon, added dissolved Cu, and one of boron or yttrium.

17. The zirconium-based metal pretreatment coating composition of claim 16 , wherein the copper chelating agent is capable of reducing amounts of copper deposited in a zirconium based coating on a metal substrate by contact with the zirconium based metal pretreatment coating composition, the copper chelating agent present in an amount sufficient to thereby produce an average total ratio of atomic % of Cu to atomic % of Zr in the coating deposited on the metal substrate that is in the range of 0.0001 and 1.1.

18. The zirconium-based metal pretreatment coating composition according to claim 16 , comprising:
A.) 50 to 300 ppm of the dissolved Zr,
B.) 1 to 50 ppm of the added dissolved Cu,
C.) 1 to 100 ppm of SiO 2 ,
D.) 150 to 2000 ppm of total fluoride,
E.) 10 to 100 ppm of free fluoride and
F.) at least 10 ppm of the copper chelating agent.

19. The zirconium-based metal pretreatment coating composition according to claim 18 , wherein the added dissolved Cu is present in the coating composition and the copper chelating agent is present in an amount of 25 to 1500 ppm.

20. The zirconium-based metal pretreatment coating composition according to claim 18 , wherein the copper chelating agent is selected from molecules having multiple carboxylic and/or phosphonic functional groups.

21. The zirconium-based metal pretreatment coating composition according to claim 18 , wherein the copper chelating agent is selected from the group consisting of aminosalicylic acid, ascorbic acid, aspartic acid, benzoic acid, citric acid, cyanuric acid, diethylenetriamine-pentamethylene phosphonic acid, dihydroxybenzoic acid, dimethylenetriaminepentaacetic acid, ethylenediaminetetraacetic acid, gluconic acid, glutamic acid, h

Assignees

• Henkel Ag & Co Kgaa

Inventors

• Vonk Donald R
• Kapic Edis
• Sienkowski Michael L

Classifications

• C23C22/34

  containing fluorides or complex fluorides · CPC title

• C09D7/1208 Primary

  Chemistry & Metallurgy · mapped topic

• C23C22/83

  Chemical after-treatment · CPC title

• B05D1/36

  Successively applying liquids or other fluent materials, e.g. without intermediate treatment · CPC title

• Y10T428/12778

  Alternative base metals from diverse categories · CPC title