Composition based on cerium, zirconium and tungsten, preparation process and use in catalysis

Patent metadata

Field	Value
Publication number	US-9169129-B2
Application number	US-201113698659-A
Country	US
Kind code	B2
Filing date	May 17, 2011
Priority date	May 19, 2010
Publication date	Oct 27, 2015
Grant date	Oct 27, 2015

Abstract

A composition based on cerium, zirconium and tungsten is described. The composition has a content expressed as an oxide, of which cerium is from 5% to 30% of the composition, tungsten is from 2% to 17% of the composition, and the remainder of the composition is zirconium. After aging at 750° C. under an air atmosphere including 10% water, it has a two-phase crystallographic structure having a tetragonal zirconia phase and a monoclinic zirconia phase, with no presence of a crystalline phase including tungsten. The composition can be used as a catalyst, especially in an SCR process.

First claim

The invention claimed is:

1. A composition comprising cerium, zirconium and tungsten, wherein the composition has the following mass contents, expressed as oxide:
cerium oxide: from 5% to 30%;
tungsten oxide: from 2% to 17%;
the remainder as zirconium oxide;

and in that after aging at 750° C. in an air atmosphere comprising 10% water, it has a two-phase crystallographic structure comprising a tetragonal zirconia phase and a monoclinic zirconia phase, with no presence of a crystalline phase comprising tungsten.

2. The composition as defined in claim 1 , wherein after aging, the composition has a specific surface area of at least 30 m 2 /g.

3. The composition as defined in claim 1 , wherein after aging, the composition has a specific surface area of at least 40 m 2 /g.

4. The composition as defined in claim 1 , wherein the composition has a two-phase crystallographic structure in which the tetragonal zirconia phase and the monoclinic zirconia phase are in a ratio of at least 5.

5. A process for preparing a composition as defined in claim 1 , wherein the process is comprised of the following steps:
(a) preparing an aqueous solution comprising sulfate anions and a zirconium salt, which can optionally be zirconium oxychloride, in proportions such that the ratio ZrO 2 /SO 3 is from 1/0.40 to 1/0.52,
(b) cooling the solution to a temperature below 25° C.,
(c) adding an alkaline compound to precipitate an amorphous zirconium hydroxide,
(d) filtering off the zirconium hydroxide and washing with water or an alkaline compound to remove the residual amounts of sulfate,
(e) mixing the zirconium hydroxide obtained from step (d) with a solution or a suspension of a tungsten salt or compound,
(f) subjecting the mixture obtained in step (e) to a hydrothermal treatment at a pressure of not more than 6 bar, via which a compound comprising tungsten and zirconium hydroxide is obtained, which can be either dried to be obtained in solid form or maintained in the form of a suspension,
(g) impregnating either the solid compound comprising tungsten and zirconium hydroxide with a solution or a suspension of cerium salts or mixing compounds, or the compound comprising tungsten and zirconium hydroxide in the form of a suspension with a solution or a suspension of cerium salts or compounds, and
(h) calcining the compound comprising tungsten and zirconium hydroxide after impregnation, or drying and calcining the suspension obtained from mixing the compound comprising tungsten and zirconium hydroxide with the solution or suspension of cerium salts or compounds obtained in step (g).

6. The process as defined in claim 5 , wherein after step (e), the pH of the mixture obtained is adjusted to a value of 6 to 8 by adding an acid.

7. The process as defined in claim 5 , wherein step (h), drying of the suspension is performed by atomization.

8. A catalytic system comprising the composition as defined in claim 1 .

9. The catalytic system as defined in claim 8 , wherein the catalytic system also comprises a zeolite.

10. A process for treating a gas for the conversion of the nitrogen oxides into nitrogen, the process comprising placing the gas in contact with a nitrogenous reducing agent, wherein a catalytic system or composition according to claim 1 is used.

11. The process as defined in claim 10 , wherein ammonia or urea is used as the nitrogenous reducing agent.

12. A process for treating a gas for the catalytic oxidation of carbon monoxide and hydrocarbons therein, the process comprising using a catalytic system according to claim 1 .

13. The process as defined in claim 10 , wherein an exhaust gas of a motor vehicle engine is treated.

14. A process for treating a gas for conversion of nitrogen oxides into nitrogen, the process comprising placing the gas in contact with a nitrogenous reducing agent, wherein the conversion uses a composition as defined in claim 1 .

15. A process for treating a gas for catalytic oxidation of carbon monoxide and hydrocarbons therein, the process comprising using a composition as defined in claim 1 .

Assignees

• Hernandez Julien
• Rohart Emmanuel
• Jorge Coelho Marques Rui
• Harris Deborah Jane
• Jones Clare
• Rhodia Operations
• Magnesium Elektron Ltd

Inventors

• Hernandez Julien
• Rohart Emmanuel
• Jorge Coelho Marques Rui
• Harris Deborah Jane
• Jones Clare

Classifications

• B01J2523/3712

  Cerium · CPC title

• B01D2255/2065

  Cerium · CPC title

• C01P2002/74

  by peak-intensities or a ratio thereof only · CPC title

• C01P2006/12

  Surface area · CPC title

• B01D2251/2062

  Ammonia · CPC title