Method for manufacturing a composite component of a timepiece or of a jewelry part, and composite component obtainable by such method

Patent metadata

Field	Value
Publication number	US-12161202-B2
Application number	US-202217575758-A
Country	US
Kind code	B2
Filing date	Jan 14, 2022
Priority date	May 13, 2015
Publication date	Dec 10, 2024
Grant date	Dec 10, 2024

Abstract

The invention relates to a method for manufacturing a composite component of a timepiece or of a jewelry part, the composite component comprising a porous ceramic part and a metallic material filling the pores of said ceramic part, said method comprising the steps of:
providing a porous ceramic preform of the component, providing a metallic material, heating the metallic material to a temperature higher than the melting point of the metallic material, filling the pores of the ceramic preform with the molten metallic material, cooling the metallic material and the ceramic preform to obtain a solidified metallic material in the pores of the ceramic preform, and applying finishing treatments to obtain the composite component,

wherein said porous ceramic preform consists essentially of a material selected from the group consisting of Si 3 N 4 , SiO 2 and mixtures thereof, and said metallic material is selected from the group consisting of gold, platinum, palladium metals and alloys of these metals.
The invention relates also to a composite component of a timepiece or of a jewelry part comprising a porous ceramic part and a metallic material filling the pores of said ceramic part, wherein said porous ceramic part consists essentially of a material selected from the group consisting of Si 3 N 4 , SO 2 and mixtures thereof, and said metallic material which is selected from the group consisting of gold, platinum, palladium metals and alloys of these metals.

First claim

What is claimed is:

1. A method for manufacturing a composite component of a timepiece or of a jewelry part, the composite component is 3 mm or less in thickness and comprises a porous ceramic part and a metallic material filling the pores of said ceramic part, said method comprising:
providing a porous ceramic preform of the component,
providing a metallic material,
heating the metallic material to a temperature higher than the melting point of the metallic material,
filling the pores of the ceramic preform with the molten metallic material without application of additional pressure,
cooling the metallic material and the ceramic preform to obtain a solidified metallic material in the pores of the ceramic preform, and
applying finishing treatments to obtain the composite component, wherein said porous ceramic preform consists essentially of a material selected from the group consisting of Si 3 N 4 , SiO 2 and mixtures thereof, and said metallic material is selected from the group consisting of gold, platinum, palladium metals and alloys of these metals.

2. The method according to claim 1 , wherein the metallic material is pure metal.

3. The method according to claim 1 , wherein the metallic material is an alloy of said metal and silicon.

4. The method according to claim 1 , wherein the ceramic preform of the composite component is a net-shape preform.

5. The method according to claim 1 , wherein a porosity level of the porous ceramic preform is calculated according to a desired carat level to be achieved by the composite component.

6. The method according to claim 1 , wherein the filling of the pores of the ceramic preform with the molten metallic material is an infiltration step by an infiltration process.

7. The method according to claim 1 , further comprising coating the internal walls of the pores of the ceramic preform with a wetting agent before the step of filling the pores of the ceramic preform with the molten metallic material.

8. The method according to claim 7 , wherein the wetting agent is pure gold or a gold alloy.

Assignees

• Swatch Group Res & Dev Ltd

Inventors

• Dubach Alban
• Rodriguez Pablo
• Pompe Robert

Classifications

• C22C1/1036

  starting from a melt · CPC title

• C22C32/0068

  only nitrides · CPC title

• C04B41/5111

  Ag, Au, Pd, Pt or Cu · CPC title

• C04B41/5105

  with a composition mainly composed of one or more of the noble metals or copper · CPC title

• C04B41/4531

  by C.V.D. · CPC title