Positive electrode active material for lithium secondary battery, method of preparing the same, and positive electrode for lithium secondary battery and lithium secondary battery which include the positive electrode active material

Patent metadata

Field	Value
Publication number	US-11799071-B2
Application number	US-201917050553-A
Country	US
Kind code	B2
Filing date	May 10, 2019
Priority date	May 11, 2018
Publication date	Oct 24, 2023
Grant date	Oct 24, 2023

Abstract

A positive electrode active material includes a lithium transition metal oxide, in which a cobalt content in the lithium transition metal oxide is less than a manganese content, wherein at least one of nickel, cobalt, and manganese in the lithium transition metal oxide has a concentration gradient that gradually changes from a center of a particle to a surface thereof, the positive electrode active material is in the form of a secondary particle formed by agglomeration of primary particles, and a ratio in which angles between c-axis directions, which are measured at at least 8 points on a surface of the positive electrode active material by TEM analysis, and a growth direction of the particle at the measuring point satisfy 85° to 95° is 60% or more.

First claim

The invention claimed is:

1. A positive electrode active material comprising:
a lithium transition metal oxide having an average composition represented by Formula 1 in which a cobalt content in the lithium transition metal oxide is less than a manganese content,
wherein at least one of nickel, cobalt, or manganese in the lithium transition metal oxide has a concentration gradient that gradually changes from a center of a particle to a surface thereof,
the positive electrode active material is in a form of a secondary particle formed by agglomeration of primary particles, and
a ratio in which angles between c-axis directions, which are measured at at least 8 points on a surface of the positive electrode active material by transmission electron microscope (TEM) analysis, and a growth direction of the particle at the measuring point satisfy 85° to 95° is 60% or more:
Li 1+a Ni x Co y Mn z M 1 w O 2   [Formula 1]

wherein, in Formula 1,
0≤a≤0.3, 0.65≤x<1, 0<y≤0.35, 0<z≤0.35, 0≤w≤0.02, and y<z, and
M 1 comprises at least one selected from the group consisting of aluminum (Al), zirconium (Zr), magnesium (Mg), zinc (Zn), yttrium (Y), iron (Fe), and titanium (Ti).

2. The positive electrode active material of claim 1 , wherein a molar ratio of cobalt:manganese in the lithium transition metal oxide is in a range of greater than 1:1 to 1:10 or less.

3. The positive electrode active material of claim 1 , wherein the positive electrode active material comprises columnar-structured primary particles, which are grown in a surface direction from a center of the positive electrode active material, in a surface portion.

4. The positive electrode active material of claim 1 , wherein the lithium transition metal oxide represented by Formula 1 comprises the cobalt in an amount of greater than 0 mol % to 15 mol % or less based on the total number of moles of transition metals excluding lithium.

5. The positive electrode active material of claim 1 , wherein the lithium transition metal oxide represented by Formula 1 comprises the manganese in an amount of 20 mol % or more to less than 35 mol % based on the total number of moles of transition metals excluding lithium.

6. A positive electrode for a lithium secondary battery, the positive electrode comprising the positive electrode active material of claim 1 .

7. A lithium secondary battery comprising the positive electrode of claim 6 .

8. The positive electrode active material of claim 3 , wherein the columnar-structure primary particles have a column-structure having an aspect ratio of 2 to 5.

Assignees

• Lg Chemical Ltd

Inventors

• Jeong Myung Gi
• Son Se Hwan
• Cho Seung Beom
• Choi Sang Soon

Classifications

• C01G53/82 Primary

  Compounds containing nickel, with or without oxygen or hydrogen, and containing two or more other elements · CPC title

• H01M4/364 Primary

  as mixtures · CPC title

• C01G53/006

  Chemistry & Metallurgy · mapped topic

• C01G53/50

  of the type (MnO2)n-, e.g. Li(NixMn1-x)O2 or Li(MyNixMn1-x-y)O2 · CPC title

• H01M4/131

  Electrodes based on mixed oxides or hydroxides, or on mixtures of oxides or hydroxides, e.g. LiCoOx · CPC title