Method of manufacturing catalyst ink free of eluted transition metal for fuel cell

Patent metadata

Field	Value
Publication number	US-11539054-B2
Application number	US-202017107272-A
Country	US
Kind code	B2
Filing date	Nov 30, 2020
Priority date	Mar 13, 2020
Publication date	Dec 27, 2022
Grant date	Dec 27, 2022

Abstract

Disclose is a method of manufacturing catalyst ink for a fuel cell, and particularly the method includes removing eluted transition metal from a noble-metal/transition-metal alloy catalyst.

First claim

What is claimed is:

1. A method of manufacturing catalyst ink for a fuel cell, comprising:
admixing 1) an alloy catalyst comprising a noble metal and a transition metal and 2) polymer particles, whereby an aggregate comprising i) the transition metal and ii) polymer particles forms,
wherein an admixture is provided comprising an alloy catalyst comprising a noble metal and a transition metal, an ionomer and a solvent; and
the admixture and the polymer particles to form the aggregate comprising 1) the transition metal eluted from the alloy catalyst and 2) the polymer particles,
wherein the aggregate is removed by filtration wherein the polymer particles comprise a chelating resin.

2. The method of claim 1 , wherein the noble metal comprises one or more selected from the group consisting of platinum (Pt), iridium (Ir), palladium (Pd), ruthenium (Ru), rhodium (Rd), gold (Au), ad silver (Ag).

3. The method of claim 1 , wherein the transition metal comprises one or more selected from the group consisting of cobalt (Co), nickel (Ni), yttrium (Y), chromium (Cr), manganese (Mn), copper (Cu), lanthanum (La), and scandium (Sc).

4. The method of claim 1 , wherein the alloy catalyst is supported on a support.

5. The method of claim 1 , wherein the polymer particles comprise, as a functional group, one or more chelating formation groups selected from the group consisting of glutamine, amidoxime, thiol, iminodiacetic acid, aminophosphonic acid, phosphonic acid, sulfonic acid, polyamine, thiourea, aminomethyl phosphonic acid, benzylamine, tertiary amine, and derivatives thereof.

6. The method of claim 1 , wherein the polymer particles comprise, as a main chain, one or more selected from the group consisting of polystyrene, polyacryl and divinylbenzene,
wherein the polymer particles comprises one or more selected from the group consisting of Structural Formula 1 and Structural Formula 2.

Here, * designates the connection point with the main chain.

Here, * designates the connection point with the main chain.

7. The method of claim 1 , wherein the polymer particles have an average diameter ranging from about 300 μm to about 800 μm.

8. The method of claim 1 , wherein the admixture is added with the polymer particles and allowed to react at a temperature of about 25° C. to about 60° C. for about 10 hr to 30 hr to afford an aggregate of the transition metal and the polymer particles.

9. The method of claim 1 , wherein the aggregate is removed by filtering the admixture using a filter of 32 mesh to 400 mesh.

10. A method of manufacturing an electrode for a fuel cell, comprising:
preparing catalyst ink manufactured by a method of claim 1 ; and
forming a catalyst layer by applying the catalyst ink on a substrate and performing drying.

Assignees

• Hyundai Motor Co Ltd
• Kia Motors Corp

Inventors

• Son Dae Yong
• Yoon Dong Hwan
• Cho Yoon Hwan

Classifications

• B01J23/40

  of the platinum group metals · CPC title

• H01M4/8828 Primary

  Coating with slurry or ink · CPC title

• H01M4/923 Primary

  Compounds thereof with non-metallic elements · CPC title

• H01M4/921 Primary

  Alloys or mixtures with metallic elements · CPC title

• H01M4/926

  on carbon or graphite · CPC title