Stripping of coatings Al-containing coatings

Patent metadata

Field	Value
Publication number	US-11377745-B2
Application number	US-201917270337-A
Country	US
Kind code	B2
Filing date	Aug 21, 2019
Priority date	Aug 21, 2018
Publication date	Jul 5, 2022
Grant date	Jul 5, 2022

Abstract

Method for stripping a coating from a coated surface of a substrate, wherein the coating is stripped in an aqueous alkaline solution, characterized in that the method comprises following steps:—preparing the coated substrate to be decoated by providing the substrate with a strippable coating by depositing a coating comprising one or more layers, wherein one layer comprising aluminum is deposited directly on the substrate surface to be decoated and—introducting the substrate to be decoated in the aqueous alkaline solution, thereby conducting a chemical stripping of the coating from the substrate, whereas the aqueous alkaline solution comprises NaOH in a concentration in weight percentage from 30 wt. % to 50 wt. %.

First claim

The invention claimed is:

1. A method for stripping a coating from a coated surface of a substrate, wherein the coating is stripped in an aqueous alkaline solution, the method comprising the following steps:
preparing the coated substrate to be decoated by providing the substrate with a strippable coating by depositing a coating comprising one or more layers, wherein one layer comprising aluminum is deposited directly on the substrate surface to be decoated; and
introducing the substrate to be decoated in the aqueous alkaline solution, thereby conducting a chemical stripping of the coating from the substrate, wherein the aqueous alkaline solution comprises NaOH in a concentration in weight percentage from 30 wt. % to 50 wt. %, and wherein the substrate is connected to a sacrificial anode for conducting the chemical stripping process, and the material of the sacrificial anode is selected having lower electrochemical potential than the material of the substrate to be decoated, or having lower electrochemical potential than material constituents contained in the substrate to be decoated that can be dissolved during chemical stripping.

2. The method according to claim 1 , wherein the layer deposited directly on the substrate surface to be decoated is selected from the group consisting of: a metallic interlayer layer, a wurtzite aluminum nitride layer, a layer comprising wurtzite aluminum nitride, and an aluminum oxide layer.

3. The method according to claim 1 , wherein the chemical stripping is conducted by maintaining the aqueous alkaline solution at a temperature corresponding to a value in a range from 80° C. to 160° C., the temperature range including border values 80° C. and 160° C., respectively.

4. The method according to claim 3 , wherein the temperature of the aqueous alkaline solution is a value in a range from 100° C. to 140° C., the range including border values 100° C. and 140° C., respectively.

5. The method according to claim 1 , wherein the concentration of NaOH in the aqueous alkaline solution is in a concentration range from 40 wt. % to 50 wt. %, the concentration range including border values 40 wt. % and 50 wt. %, respectively.

6. The method according to claim 1 , wherein the sacrificial anode is made of iron or is made of a material comprising iron.

7. The method according to claim 6 , wherein the substrate is made of cemented carbide having a cobalt binder phase or the substrate to be decoated is made of a material comprising cemented carbide having a cobalt binder phase.

8. The method according to claim 1 , wherein the substrate to be decoated is made of cemented carbide or the substrate is made of a material comprising cemented carbide.

9. A method for stripping a coating from a coated surface of a substrate, wherein the coating is stripped in an aqueous alkaline solution, the method comprising the following steps:
preparing the coated substrate to be decoated by providing the substrate with a strippable coating by depositing a coating comprising one or more layers, wherein one layer comprising aluminum is deposited directly on the substrate surface to be decoated using a physical vapor deposition process, and before conducting the deposition process a blasting media comprising alumina is used for blasting one or more cathodes that are used as a coating material source for depositing said layer directly on the substrate; and
introducing the substrate to be decoated in the aqueous alkaline solution, thereby conducting a chemical stripping of the coating from the substrate, wherein the aqueous alkaline solution comprises NaOH in a concentration in weight percentage from 30 wt. % to 50 wt. %.

Assignees

• Oerlikon Surface Solutions Ag Pfaeffikon

Inventors

• Eriksson Anders Olof
• Benedikt Sebastian
• Schott Vadim

Classifications

• C23C14/5873

  Removal of material · CPC title

• C23F1/36 Primary

  for etching aluminium or alloys thereof · CPC title

• C23G1/22

  Light metals · CPC title

• C23F1/44

  Compositions for etching metallic material from a metallic material substrate of different composition · CPC title