Steel alloy workpiece and a method for making a press-hardened steel alloy component

Patent metadata

Field	Value
Publication number	US-11255006-B2
Application number	US-201916509001-A
Country	US
Kind code	B2
Filing date	Jul 11, 2019
Priority date	Nov 16, 2018
Publication date	Feb 22, 2022
Grant date	Feb 22, 2022

Abstract

A steel alloy workpiece and a method for making a press-hardened steel (PHS) component using the steel alloy workpiece is provided. The steel alloy workpiece includes between about 1.0 and 5.0 weight percent chromium, between about 0.5 and 2.0 weight percent silicon, and a surface having a predetermined imprinted pattern. The imprinted pattern includes one of a plurality of overlapping nested sinusoidal waves and a honey-comb pattern, and ascribes a surface roughness of between about 1.0 microns and 2.5 microns. The method includes providing the steel alloy workpiece, heating the workpieces at a predetermined time and temperature, hot stamping the workpieces into the PHS component, quenching the PHS component at a predetermined quench rate, and e-coating the PHS component. The e-coating is applied directly onto the surface of the PHS component.

First claim

What is claimed is:

1. A steel alloy workpiece, comprising:
between about 1.0 and 5.0 weight percent chromium;
between about 0.5 and 2.0 weight percent silicon;
a surface having a predetermined imprinted pattern comprising a plurality of imprinted intersecting waves having an average intersection distance (d avg ) of more than 0 but less than about 150 micrometers; and
an electrophoretic coating applied directly onto the imprinted surface; and
wherein the steel alloy workpiece is press hardened.

2. The steel alloy workpiece of claim 1 , wherein the predetermined imprinted pattern ascribes a roughness of between about 1.0 micron and 2.5 micron onto the surface.

3. The steel alloy workpiece of claim 1 , wherein the plurality of intersecting waves comprises:
a first plurality of nested sinusoidal waves extending parallel to an A-axis; and
a second plurality of nested sinusoidal waves extending parallel to the A-axis;
wherein the second plurality of nested sinusoidal waves is out of phase with the first plurality of nested sinusoidal waves such that the second plurality of nested sinusoidal waves overlaps the first plurality of nested sinusoidal waves.

4. The steel alloy workpiece of claim 3 , wherein the first plurality of nested sinusoidal waves and the second plurality of nested sinusoidal waves includes at least one of a same amplitude and a same frequency.

5. The steel alloy workpiece of claim 3 , wherein the first plurality of nested sinusoidal waves is about 180 degrees out of phase with the second plurality of nested sinusoidal waves.

6. The steel alloy workpiece of claim 1 , wherein the plurality of intersecting waves ascribe a roughness of about 1.5 micron onto the surface of the steel alloy workpiece.

7. The steel alloy workpiece of claim 1 , further comprising:
from about 0.01 to about 0.35 weight percent Carbon (C); and
more than 0.0 to about 3.0 weight percent Manganese (Mn).

8. The steel alloy workpiece of claim 1 , wherein the predetermined imprinted pattern comprises a honey-comb pattern.

Assignees

• Gm Global Tech Operations Llc

Inventors

• Lu Qi
• Guo Yang

Classifications

• C22C38/34 Primary

  with more than 1.5% by weight of silicon · CPC title

• C25D13/20

  Pretreatment · CPC title

• C22C38/02

  containing silicon · CPC title

• B32B15/012

  one layer being formed of an iron alloy or steel, another layer being formed of aluminium or an aluminium alloy · CPC title

• C25D13/00

  Electrophoretic coating characterised by the process (C25D15/00 takes precedence; compositions for electrophoretic coating C09D5/44) · CPC title