Abstract

Implementations of the present disclosure generally relate to methods and apparatuses for epitaxial deposition on substrate surfaces. More particularly, implementations of the present disclosure generally relate to methods and apparatuses for surface preparation prior to epitaxial deposition. In one implementation, a method of processing a substrate is provided. The method comprises etching a surface of a silicon-containing substrate by use of a plasma etch process to form an etched surface of the silicon-containing substrate and forming an epitaxial layer on the etched surface of the silicon-containing substrate. The plasma etch process comprises flowing an etchant gas mixture comprising a fluorine-containing precursor and a hydrogen-containing precursor into a substrate-processing region of a first processing chamber and forming a plasma from the etchant gas mixture flowed into the substrate-processing region.

First claim

The invention claimed is:

1. A method of processing a substrate, comprising:
transferring a patterned substrate into a substrate processing region, wherein the patterned substrate has a silicon-containing surface having native oxides formed thereon and positioned at a bottom of a high aspect ratio feature having a depth more than ten times a width of the high aspect ratio feature;
removing the native oxides from the silicon-containing surface by a first plasma etch process, comprising:
flowing a fluorine-containing precursor and a heavy inert gas into the substrate processing region while applying a first plasma power to form a plasma containing fluorine ions and heavy inert gas ions, wherein the first plasma etch process uses the plasma formed by one or more process gases consisting of the fluorine-containing precursor and the heavy inert gas; and
etching the silicon-containing surface with the fluorine ions while applying a first bias to the substrate to remove the native oxides and form an etched silicon-containing surface;

etching the etched silicon-containing surface by a second plasma etch process, comprising:
flowing an etching gas mixture comprising a chlorine-containing precursor and a hydrogen-containing precursor into the substrate processing region while applying a second plasma power to form chlorine-containing ions and hydrogen-containing ions; and
etching the etched silicon-containing surface with the chlorine-containing ions and the hydrogen-containing ions while applying a second bias to the substrate; and

forming an epitaxial layer on the etched silicon-containing surface,
wherein the first plasma etch process, the second plasma etch process, and forming the epitaxial layer are performed without exposing the patterned substrate to atmosphere,
wherein the heavy inert gas is selected from the group consisting of: argon (Ar), krypton (Kr), xenon (Xe), and combinations thereof, and
wherein a flow rate of the fluorine-containing precursor and the heavy inert gas result in a heavy inert gas-to-fluorine flow ratio of between 80:1 and 150:1.

2. The method of claim 1 , wherein the fluorine-containing precursor is selected from the group consisting of: diatomic fluorine (F 2 ), monatomic fluorine (F), nitrogen trifluoride (NF 3 ), nitrogen pentafluoride (NF 5 ), sulfur hexafluoride (SF 6 ), xenon difluoride (XeF 2 ), carbon tetrafluoride (CF 4 ), octafluorocyclobutane (C 4 F 8 ), trifluoromethane (CHF 3 ), hydrogen fluoride (HF), and combinations thereof.

3. The method of claim 2 , wherein the first plasma etch process is an inductively coupled plasma etch process.

4. The method of claim 1 , wherein the patterned substrate is maintained at a temperature between about 20 degrees Celsius and about 50 degrees Celsius.

5. The method of claim 1 , wherein the first plasma etch process is performed at a pressure between about 5 mTorr and about 80 mTorr.

6. The method of claim 1 , further comprising:
removing etchant residue produced during the second plasma etch process from the silicon-containing surface of the patterned substrate by a third plasma etch process, comprising:
flowing the chlorine-containing precursor and the hydrogen-containing precursor into the substrate processing region while applying a third plasma power to form chlorine-containing ions and hydrogen-containing ions; and
etching the silicon-containing surface with the chlorine-containing ions and the hydrogen-containing ions, wherein the third plasma etch process is a bias-free process.

7. A method of processing a substrate, comprising:
transferring a patterned substrate into a substrate processing region, wherein the patterned substrate has a silicon-containing surface having native oxides formed thereon and positioned at a bottom of a high aspect ratio feature having a depth more than ten times a width of the high aspect ratio feature;
removing the native oxides from the silicon-containing surface by a first plasma etch process, comprising:
flowing nitrogen trifluoride (NF 3 ) and argon gas into the substrate processing region while applying a first plasma power to form a plasma containing fluorine ions and argon ions, wherein the first plasma etch process uses the plasma formed by one or more process gases consisting of the NF 3 and the argon gas and a flow rate of NF 3 and argon gas results in an argon gas-to-NF 3 flow ratio of between 80:1 and 150:1; and
etching the silicon-containing surface with the fluorine ions and the argon ions while applying a first bias to the substrate to remove the native oxides and form an etched silicon-containing surface;

etching the etched silicon-containing surface by a second plasma etch process, comprising:
flowing an etching gas mixture comprising a chlorine-containing precursor and a hydrogen-containing precursor into the substrate processing region while applying a second plasma power to form chlorine-containing ions and hydrogen-containing ions; and
etching the etched silicon-containing surface with the chlorine-containing ions and the hydrogen-containing ions while applying a second bias to the substrate; and

forming an epitaxial layer on the etched silicon-containing surface, wherein the first plasma etch process, the second plasma etch process, and forming the epitaxial layer on the etched silicon-containing surface of the patterned substrate are performed without exposing the patterned substrate to atmosphere.

8. The method of claim 7 , wherein the first bias has a power level within a range from about 200 W to 400 W.

9. The method of claim 8 , wherein the patterned substrate is maintained at a temperature between about 20 degrees Celsius and about 50 degrees Celsius.

10. The method of claim 9 , wherein the first plasma etch process is performed at a pressure between about 5 mTorr and about 80 mTorr.

11. The method of claim 7 , further comprising:
removing etchant residue produced during the second plasma etch process from the silicon-containing surface of the patterned substrate by a third plasma etch process, comprising:
flowing the chlorine-containing precursor and the hydrogen-containing precursor into the substrate processing region while applying a third plasma power to form chlorine-containing ions and hydrogen-containing ions; and
etching the silicon-containing surface with the chlorine-containing ions and the hydrogen-containing ions, wherein the third plasma etch process is a bias-free process.

12. A method of processing a substrate, comprising:
transferring a patterned substrate into a substrate processing region, wherein the patterned substrate has a silicon-containing surface having native oxides formed thereon and positioned at a bottom of a high aspect ratio feature having a depth more than ten times a width of the high aspect ratio feature;
removing the native oxides from the silicon-containing surface by a first plasma etch process, comprising:
flowing a fluorine-containing precursor and a heavy inert gas precursor into the substrate processing region while applying a first plasma power to bombard the silicon-containing surface with fluorine ions while applying a first bias to the substrate, wherein the first plasma etch process uses a plasma formed by one or more process gases consisting of the fluorine-containing precursor and the heavy inert gas precursor;

etching the silicon-containing surface by a second plasma etch process, comprising:
flowing an etching gas mixture comprising a chlorine-containing precursor and a hydrogen-containing precursor into the substrate processing region while applying a second plasma power to form chlorine-containing ions and hydrogen-containing ions; and
etching the sil

Assignees

• Applied Materials Inc

Inventors

• Stone Peter
• Olsen Christopher S
• Kuo Teng-Fang
• Hsieh Ping Han
• Ding Zhenwen

Classifications

• H10P70/12

  by dry cleaning only (H10P70/52 takes precedence) · CPC title

• H10P50/283

  by chemical means · CPC title

• H10P72/7612

  characterised by lifting arrangements, e.g. lift pins · CPC title

• H10P72/0462

  characterised by the construction of the processing chambers, e.g. modular processing chambers · CPC title

• H10P70/234

  the processing being the formation of vias or contact holes · CPC title