Composition and process for metallizing nonconductive plastic surfaces

Patent metadata

Field	Value
Publication number	US-10377947-B2
Application number	US-201916238596-A
Country	US
Kind code	B2
Filing date	Jan 3, 2019
Priority date	Apr 1, 2014
Publication date	Aug 13, 2019
Grant date	Aug 13, 2019

Abstract

The present invention relates to a process for metallizing electrically nonconductive plastic surfaces of articles using the etching solution. The etching solution is based on a stabilized acidic permanganate solution. After the treatment with the etching solution, the articles can be metallized.

First claim

The invention claimed is:

1. Process for etching electrically nonconductive plastic surfaces of articles, comprising the process step of:
A) treating the plastic surface with at least one etching solution for treating nonconductive plastic surfaces, the etching solution comprising
(i) at least one acid,
(ii) at least one permanganate salt selected from alkali metal permanganates and earth alkali metal permanganates, and
(iii) at least one source for a metal ion, wherein the metal of the metal ion is selected from titanium, zirconium, niobium, molybdenum, ruthenium, rhodium, nickel, copper, silver, zinc and cadmium,
characterized in that the molar ratio of permanganate ions according to (ii) to metal ions according to (iii) ranges from 8.75:1 to 40:1.

2. Process according to claim 1 , characterized in that the plastic surface has been manufactured from at least one electrically nonconductive plastic and the at least one electrically nonconductive plastic is selected from the group comprising an acrylonitrile-butadiene-styrene copolymer, a polyamide, a polycarbonate and a mixture of an acrylonitrile-butadiene-styrene copolymer with at least one further polymer.

3. Process according to claim 1 , characterized in that the following further process step is performed after process step A) and, if process step B) is performed, prior to process step B):
A i) treating the plastic surface with an alkaline etching solution.

4. Process according to claim 1 , characterized in that the following further process step is performed after process step A) and, if process step B) is performed, prior to process step B):
A ii) treating the plastic surface in a solution comprising a reducing agent for manganese dioxide.

5. Process for metallizing electrically nonconductive plastic surfaces of articles, comprising the process steps of:
A) treating the plastic surface with at least one etching solution for treating nonconductive plastic surfaces, the etching solution comprising
(i) at least one acid,
(ii) at least one permanganate salt selected from alkali metal permanganates and earth alkali metal permanganates, and
(iii) at least one source for a metal ion, wherein the metal of the metal ion is selected from titanium, zirconium, niobium, molybdenum, ruthenium, rhodium, nickel, copper, silver, zinc and cadmium, and

B) metallizing the plastic surface with a metallizing solution,
characterized in that the molar ratio of permanganate ions according to (ii) to metal ions according to (iii) ranges from 8.75:1 to 40:1.

6. The process according to claim 5 , characterized in that process step A) is preceded by performance of the following further process step:
pretreatment step: treating the plastic surface in an aqueous solution comprising at least one glycol compound.

7. Process according to claim 6 , characterized in that the at least one glycol compound is selected from compounds of the general formula (I)

wherein
n is an integer from 1 to 4; and
R1 and R2 are each independently —H, —CH3, —CH2-CH3, —CH2-CH2-CH3, —CH(CH3)-CH3, —CH2-CH2-CH2-CH3, —CH(CH3)-CH2-CH3, —CH2-CH(CH3)-CH3, —CH2-CH2-CH2-CH2-CH3, —CH(CH3)-CH2-CH2-CH3, —CH2-CH(CH3)-CH2-CH3, —CH2-CH2-CH(CH3)-CH3, —CH(CH2-CH3)-CH2-CH3, —CH2-CH(CH2-CH3)-CH3, —CO—CH3, —CO—CH2-CH3, —CO—CH2-CH2-CH3, —CO—CH(CH3)-CH3, —CO—CH(CH3)-CH2-CH3, —CO—CH2-CH(CH3)-CH3, —CO—CH2-CH2-CH2-CH3.

8. Process according to claim 5 , characterized in that the following further process step is performed between process steps A) and B):
A iii) treating the plastic surface with a solution of a metal colloid or of a compound of a metal, the metal being selected from the metals of transition group I of the Periodic Table of the Elements and transition group VIII of the Periodic Table of the Elements.

9. Process according to claim 5 , characterized in that the following further process step is performed between process steps A) and B):
A iv) treating the plastic surfaces in a conversion solution.

10. Process according to claim 5 , characterized in that the following alternative process step is performed between process steps A) and B):
A iv) treating the plastic surfaces in a sulfide containing solution.

11. Process according to claim 5 , characterized in that the following process step is performed prior to process step A):
Slipping stripes of a plastic material not being etched by the at least one etching solution over a plastic coat of a rack, the rack holding the articles having nonconductive plastic surfaces.

12. Process according to claim 5 , characterized in that the plastic surface has been manufactured from at least one electrically nonconductive plastic and the at least one electrically nonconductive plastic is selected from the group comprising an acrylonitrile-butadiene-styrene copolymer, a polyamide, a polycarbonate and a mixture of an acrylonitrile-butadiene-styrene copolymer with at least one further polymer.

13. Process according to claim 5 , characterized in that the following further process step is performed after process step A) and, if process step B) is performed, prior to process step B):
A i) treating the plastic surface with an alkaline etching solution.

14. Process according to claim 5 , characterized in that the following further process step is performed after process step A) and, if process step B) is performed, prior to process step B):
A ii) treating the plastic surface in a solution comprising a reducing agent for manganese dioxide.

Assignees

• Atotech Deutschland Gmbh

Inventors

• Middeke Hermann
• Schneider Steve
• Fels Carl Christian

Classifications

• C09K13/04

  containing an inorganic acid · CPC title

• C23C18/24 Primary

  using acid aqueous solutions · CPC title

• C23C18/30

  Activating {or accelerating or sensitising with palladium or other noble metal} · CPC title

• C09K13/02 Primary

  containing an alkali metal hydroxide · CPC title

• C23C18/1653

  Two or more layers with at least one layer obtained by electroless plating and one layer obtained by electroplating · CPC title