Composition for forming Mn and Nb co-doped PZT-based piezoelectric film

Patent metadata

Field	Value
Publication number	US-10112872-B2
Application number	US-201515127531-A
Country	US
Kind code	B2
Filing date	Mar 12, 2015
Priority date	Mar 28, 2014
Publication date	Oct 30, 2018
Grant date	Oct 30, 2018

Abstract

A composition used for forming a PZT-based piezoelectric film formed of Mn and Nb co-doped composite metal oxides is provided, in which the composition includes PZT-based precursors so that a metal atom ratio (Pb:Mn:Nb:Zr:Ti) in the composition satisfies (1.00 to 1.25):(0.002 to 0.056):(0.002 to 0.056):(0.40 to 0.60):(0.40 to 0.60), a rate of Mn is from 0.20 to 0.80 when the total of metal atom rates of Mn and Nb is 1, a rate of Zr is from 0.40 to 0.60 when the total of metal atom rates of Zr and Ti is 1, and the total rate of Zr and Ti is from 0.9300 to 0.9902 when the total of metal atom rates of Mn, Nb, Zr, and Ti is 1.

First claim

The invention claimed is:

1. A composition for forming a Mn and Nb co-doped PZT-based piezoelectric film used for forming a PZT-based piezoelectric film formed of Mn and Nb co-doped composite metal oxides, the composition comprising:
PZT-based precursors containing metal atoms configuring the composite metal oxides;
acetylacetone as a stabilizer; and
a diol as a solvent,
wherein the PZT-based precursors are contained in the composition so that a metal atom ratio (Pb:Mn:Nb:Zr:Ti) in the composition satisfies (1.00 to 1.25):(0.002 to 0.056):(0.002 to 0.056):(0.40 to 0.60):(0.40 to 0.60),
a rate of Mn is from 0.20 to 0.80 when the total of metal atom rates of Mn and Nb is 1,
a rate of Zr is from 0.40 to 0.60 when the total of metal atom rates of Zr and Ti is 1, and
the total rate of Zr and Ti is from 0.9300 to 0.9902 when the total of metal atom rates of Mn, Nb, Zr, and Ti is 1,
the diol is propylene glycol or ethylene glycol,
an amount of acetylacetone contained in the composition is from 0.5 moles to 4 moles when the total amount of Mn, Nb, Zr, and Ti contained in the composition is 1 mole, and
a rate of the diol in 100 mass % of the composition is from 16 mass % to 56 mass %.

2. The composition for forming a Mn and Nb co-doped PZT-based piezoelectric film according to claim 1 , further comprising:
polyvinylpyrrolidone at a rate so as to obtain 0.01 moles to 0.25 moles of polyvinylpyrrolidone with respect to 1 mole of the PZT-based precursor, in terms of monomers.

Assignees

• Mitsubishi Materials Corp

Inventors

• Doi Toshihiro
• Sakurai Hideaki
• Soyama Nobuyuki

Classifications

• C04B2235/3251

  Niobium oxides, niobates, tantalum oxides, tantalates, or oxide-forming salts thereof · CPC title

• C04B2235/96

  Properties of ceramic products, e.g. mechanical properties such as strength, toughness, wear resistance · CPC title

• C01P2006/40

  Electric properties · CPC title

• C04B2235/606

  Drying · CPC title

• C04B35/491 Primary

  based on lead zirconates and lead titanates {, e.g. PZT} · CPC title