Surface treatment composition for galvanized steel sheet, surface treatment method for galvanized steel sheet, and galvanised steel sheet

Patent metadata

Field	Value
Publication number	US-9856380-B2
Application number	US-201214758225-A
Country	US
Kind code	B2
Filing date	Dec 28, 2012
Priority date	Dec 26, 2012
Publication date	Jan 2, 2018
Grant date	Jan 2, 2018

Abstract

A surface treatment composition for a galvanized steel sheet containing, based on 100 parts by weight of the total solution, 3.0 to 25.0 parts by weight of a silane compound, 0.5 to 5.0 parts by weight of a molybdenum compound, 0.5 to 5.0 parts by weight of a vanadium compound, 0.1 to 3.0 parts by weight of a nickel compound, 0.05 to 1.0 parts by weight of a copper compound, and a remainder of solvent, a surface treatment method for a galvanized steel sheet using the surface treatment composition, and a surface-treated galvanized steel sheet, are provided. Corrosion resistance, blackening resistance, warm water resistance, and conductivity are secured free from concerns regarding the installation of additional equipment for treating chromium, increased manufacturing costs, and environmental pollution.

First claim

The invention claimed is:

1. A surface treatment composition for a galvanized steel sheet, comprising:
based on 100 parts by weight of the total solution, 3.0 to 25.0 parts by weight of a silane compound;
0.5 to 5.0 parts by weight of a molybdenum compound;
0.5 to 5.0 parts by weight of a vanadium compound;
0.1 to 3.0 parts by weight of a nickel compound;
0.05 to 1.0 parts by weight of a copper compound; and
a remainder of solvent.

2. The surface treatment composition for a galvanized steel sheet of claim 1 , further comprising based on 100 parts by weight of the total solution, one or more of:
1 to 20 parts by weight of one or more metal compound selected from the group consisting of a zirconium compound and a titanium compound capable of forming an oxygen acid salt on a metal surface;
0.5 to 10 parts by weight of a phosphoric acid compound;
1.0 to 10 parts by weight of a carboxylic acid;
0.1 to 3.0 parts by weight of a calcium compound; and
3 to 10 parts by weight of an organic acid.

3. The surface treatment composition for a galvanized steel sheet of claim 1 , wherein the solvent is a mixture of water and ethanol.

4. The surface treatment composition for a galvanized steel sheet of claim 1 , wherein the solution contains 0.05 to 0.5 wt % of copper (Cu) and 0.5 to 3.0 wt % of nickel (Ni), and the weight ratio of Cu and Ni is 0.1:1.0 to 0.1:3.0.

5. The surface treatment composition for a galvanized steel sheet of claim 2 , wherein the phosphoric acid compound is a mixture of one, two or more selected from a group consisting of orthophosphoric acid, pyrophosphate, polyphosphate, metaphosphate, biphosphate, triphosphate, quadriphosphate, metal salt of a phosphoric acid, and ammonium salt of a phosphoric acid.

6. The surface treatment composition for a galvanized steel sheet of claim 2 , wherein the carboxylic acid is a mixture of one or more selected from a group consisting of ascorbic acid, tartaric acid, citric acid, tannic acid, benzoic acid, glycol acid, and dihydro-acid.

7. The surface treatment composition for a galvanized steel sheet of claim 1 , wherein the silane compound includes a compound having an amino group and a compound having an epoxy group, and a mixing ratio of the compound having an amino group versus the compound having an epoxy group is 1:1.5 to 1:3.0.

8. The surface treatment composition for a galvanized steel sheet of claim 1 , wherein the molybdenum compound is one or more of ammonium molybdate, sodium molybdate, calcium molybdate, molybdenum selenide, lithium molybdate, molybdenum disulfide, molybdenum trioxide, and molybdic acid.

9. The surface treatment composition for a galvanized steel sheet of claim 1 , wherein the vanadium compound is one or more of vanadium pentoxide, vanadium trioxide, vanadium dioxide, vanadium oxy-acetylacetonate, vanadium acetylacetonate, vanadium trichloride, and ammonium metavanadate.

10. The surface treatment composition for a galvanized steel sheet of claim 1 , wherein the nickel compound is one or more of nickel acetate, nickel chloride, nickel fluoride, nickel nitrate, sulfamic acid nickel, nickel formate, nickel hydroxide, nickel ammonium sulfate, and nickel carbonate.

11. The surface treatment composition for a galvanized steel sheet of claim 2 , wherein the calcium compound is one or more of calcium hydroxy-stearate, calcium carbonate, calcium acetate, calcium chloride, calcium fluoride, calcium hypophosphite, calcium hydroxide, calcium gluconate, calcium nitrate, calcium permanganate, calcium phosphate, calcium silicate, calcium sulfate, calcium stearate, and formic acid.

12. The surface treatment composition for a galvanized steel sheet of claim 1 , wherein the copper compound is one or more of copper acetylacetonate, copper acetate, copper carbonate, copper chloride, cuprous oxide, copper pyrophosphate, copper nitrate, copper sulfate, copper iodide, cuprous oxide, tetraamine copper sulfate, and copper disodium ethylenediaminetetraacetic acid.

13. The surface treatment composition for a galvanized steel sheet of claim 2 , wherein the organic acid is one or more of polyvinyl acetate, vinyl acetate, and polyvinyl chloride.

14. The surface treatment composition for a galvanized steel sheet of claim 1 , further comprising one or more of wax, a leveling agent, an anti-foaming agent, a water-soluble resin, and an insoluble resin in a state of being mechanically dispersed in water.

15. A galvanized steel sheet comprising:
a base steel sheet;
a galvanized layer formed on the base steel sheet; and
a coated layer formed on the galvanized layer,
wherein the coated layer is formed of the surface treatment composition of claim 1 .

16. The galvanized steel sheet of claim 15 , wherein a dry film thickness of the coated layer is 0.1 to 1.2 g/m 2 .

17. The galvanized steel sheet of claim 15 , wherein the galvanized layer contains 0.1 wt % or more of magnesium (Mg), 0.1 wt % or more of aluminum (Al), and zinc (Zn) as a remainder.

18. The galvanized steel sheet of claim 17 , wherein the galvanized layer further comprises one or more selected from a group consisting of silicon (Si), beryllium (Be), nickel (Ni), and zirconium (Zr).

Assignees

• Posco

Inventors

• Kim Hyun-Tae
• Jin Young-Sool

Classifications

• C23C22/42

  containing also phosphates · CPC title

• C23C2/06

  Zinc or cadmium or alloys based thereon · CPC title

• C23C18/1216

  Metal oxides (C23C18/1212 takes precedence) · CPC title

• C25D7/0614

  Strips or foils · CPC title

• C23C22/40 Primary

  containing molybdates, tungstates or vanadates · CPC title