Chemical conversion-treated steel sheet and method for producing same, and chemical conversion treatment solution

Patent metadata

Field	Value
Publication number	US-10619069-B2
Application number	US-201515128273-A
Country	US
Kind code	B2
Filing date	Mar 27, 2015
Priority date	Mar 27, 2014
Publication date	Apr 14, 2020
Grant date	Apr 14, 2020

Abstract

This chemical conversion-treated steel sheet ( 10 ) has a chemical conversion treatment coating ( 12 ) upon a plating layer ( 17 ) of a steel sheet ( 11 ). The chemical conversion treatment coating ( 12 ) contains a fluororesin, a base resin which is a resin other than a fluororesin, metal flakes ( 13 ), and a chemical conversion treatment component. The content of the fluororesin in relation to the total quantity of resins is 3.0 mass % or more in terms of fluorine atoms, the content of the base resin in relation to 100 parts by mass of the fluororesin is 10 parts by mass or more, and the content of metal flakes ( 13 ) in the chemical conversion treatment coating ( 12 ) is more than 20 mass % but at most 60 mass %.

First claim

The invention claimed is:

1. A chemical conversion-treated steel sheet comprising: a plated steel sheet including a steel sheet and a plating layer disposed on a surface of the steel sheet; and a chemical conversion treatment coating film disposed on a surface of the plating layer, wherein:
the plating layer contains a zinc alloy containing 0.05 to 60 mass % of aluminum and 0.5 to 4.0 mass % of magnesium,
the chemical conversion treatment coating film contains a fluororesin, a base resin, a metal flake, and a chemical conversion treatment component,
a content of the base resin relative to 100 parts by mass of the fluororesin in the chemical conversion treatment coating film is 100 parts by mass or more,
the base resin is one or more selected from the group consisting of a polyurethane, a polyester, an acrylic resin, an epoxy resin, and a polyolefin,
a content of the fluororesin relative to a total amount of the fluororesin and the base resin is 3.0 mass % or more in terms of fluorine atoms,
a content of the metal flake in the chemical conversion treatment coating film is more than 20 mass % and 60 mass % or less,
a metal material for the metal flake is one or more metal materials selected from the group consisting of aluminum and alloys thereof, iron and alloys thereof, copper and alloys thereof, silver, nickel, and titanium,
the chemical conversion treatment component is one or more compounds selected from the group consisting of a 4A metal compound, a molybdate and a valve metal compound,
the 4A metal compound is a compound including one or more selected from the group consisting of Ti, Zr, and Hf, and
the valve metal compound is a compound including one or both of V and Nb.

2. The chemical conversion-treated steel sheet according to claim 1 , wherein the chemical conversion treatment coating film has a film thickness of 0.5 to 10 μm.

3. The chemical conversion-treated steel sheet according to claim 1 , wherein the content of the base resin relative to 100 parts by mass of the fluororesin in the chemical conversion treatment coating film is 100 parts by mass or more and 900 parts by mass or less.

4. The chemical conversion-treated steel sheet according to claim 1 , wherein
a content of the 4A metal compound in the chemical conversion treatment coating film based on the chemical conversion treatment coating film is 0.005 to 5.0 mass % in terms of 4A metal.

5. The chemical conversion-treated steel sheet according to claim 1 , wherein the chemical conversion treatment coating film further contains one or both of a silane coupling agent and a phosphate.

6. The chemical conversion-treated steel sheet according to claim 1 , wherein
the chemical conversion-treated steel sheet further includes a pretreatment coating film which contains a phosphate compound or a valve metal component, the pretreatment coating film being disposed between the plated steel sheet and the chemical conversion treatment coating film,
the phosphate compound is a metal phosphate or a composite phosphate, and
the valve metal component is an oxide, a hydroxide, or a fluoride containing one or more selected from the group consisting of Ti, Zr, Hf, V, Nb, Ta, Mo, and W.

7. The chemical conversion-treated steel sheet according to claim 1 , wherein the chemical conversion treatment coating film further contains a pigment.

8. The chemical conversion-treated steel sheet according to claim 1 , wherein the chemical conversion treatment coating film further contains a wax.

9. A method for producing a chemical conversion-treated steel sheet comprising: applying a chemical conversion treatment solution on a plating layer of a plated steel sheet; and drying the applied chemical conversion treatment solution to manufacture the chemical conversion-treated steel sheet, wherein:
the plating layer is composed of a zinc alloy containing 0.05 to 60 mass % of aluminum and 0.5 to 4.0 mass % of magnesium,
the chemical conversion treatment solution contains an emulsion of a fluororesin, an emulsion of a base resin, a metal flake, and a pre-chemical conversion treatment component,
a particle diameter of the emulsion of the fluororesin is 10 to 300 nm,
a particle diameter of the emulsion of the base resin is 10 to 100 nm,
the base resin is one or more selected from the group consisting of a polyurethane, a polyester, an acrylic resin, an epoxy resin, and a polyolefin,
a content of the fluororesin relative to a total amount of the fluororesin and the base resin in the chemical conversion treatment solution is 3.0 mass % or more in terms of fluorine atoms,
a content of the base resin relative to 100 parts by mass of the fluororesin in the chemical conversion treatment solution is 10 parts by mass or more, and
a content of the metal flake relative to a solid content in the chemical conversion treatment solution is more than 20 mass % and 60 mass % or less,
a metal material for the metal flake is one or more metal materials selected from the group consisting of aluminum and alloys thereof, iron and alloys thereof, copper and alloys thereof, silver, nickel, and titanium,
the pre-chemical conversion treatment component is one or both of a chemical conversion treatment component and a component which changes to the pre-chemical conversion treatment component in the chemical conversion treatment solution or through drying the chemical conversion treatment solution,
the chemical conversion treatment component is one or more compounds selected from the group consisting of a 4A metal compound, a molybdate and a valve metal compound,
the 4A metal compound is a compound including one or more selected from the group consisting of Ti, Zr, and Hf, and,
the valve metal compound is a compound including one or both of V and Nb.

10. The method for producing a chemical conversion-treated steel sheet according to claim 9 , further comprising pretreating the plated steel sheet with a phosphate compound or a valve metal component before applying the chemical conversion treatment solution, wherein the phosphate compound is a metal phosphate or a composite phosphate, and the valve metal component is an oxide, a hydroxide, or a fluoride containing one or more selected from the group consisting of Ti, Zr, Hf, V, Nb, Ta, Mo, and W.

11. A chemical conversion treatment solution comprising: an emulsion of a fluororesin, an emulsion of a base resin, a metal flake, and a pre-chemical conversion treatment component, wherein:
a particle diameter of the emulsion of the fluororesin is 10 to 300 nm,
a particle diameter of the emulsion of the base resin is 10 to 100 nm,
the base resin is one or more selected from the group consisting of a polyurethane, a polyester, an acrylic resin, an epoxy resin, and a polyolefin,
a content of the fluororesin relative to a total amount of the fluororesin and the base resin in the chemical conversion treatment solution is 3.0 mass % or more in terms of fluorine atoms,
a content of the base resin relative to 100 parts by mass of the fluororesin in the chemical conversion treatment solution is 10 parts by mass or more, and
a content of the metal flake relative to a solid content in the chemical conversion treatment solution is more than 20 mass % and 60 mass % or less,
a metal material for the metal flake is one or more metal materials selected from the group consisting of aluminum and alloys thereof, iron and alloys thereof, copper and alloys thereof, silver, nickel, and titanium,
the pre-chemical conversion treatment component is one or both of a chemical conversion treatment component and a component which changes to the chemical conversion treatment component in the chemical conversion treatment solution or through dryin

Assignees

• Nisshin Steel Co Ltd
• Nippon Steel Nisshin Co Ltd

Inventors

• Matsuno Masanori
• Yamamoto Masaya

Classifications

• C23C22/40

  containing molybdates, tungstates or vanadates · CPC title

• C23C18/48

  Coating with alloys · CPC title

• C23C22/361

  containing titanium, zirconium or hafnium compounds · CPC title

• C09D175/04

  Polyurethanes · CPC title

• B32B2307/102

  Insulating · CPC title