Multilayer heat-shrinkable styrene-based film and method for producing the same

Patent metadata

Field	Value
Publication number	US-9845386-B2
Application number	US-37518507-A
Country	US
Kind code	B2
Filing date	Jul 20, 2007
Priority date	Jul 26, 2006
Publication date	Dec 19, 2017
Grant date	Dec 19, 2017

Abstract

The present invention provides the following multilayer heat-shrinkable styrene-based film having an appropriate surface shape, together with excellent lubricity and blocking resistance, and resistance to ink skipping and like problems during the printing process:
a multilayer heat-shrinkable styrene-based film having: layers (A) each containing 0.8 to 2.5 parts by weight of high impact polystyrene resin and 0.02 to 0.15 parts by weight of organic fine particles having a mean particle diameter of 0.5 to 5 μm per 100 parts by weight of a block copolymer of 75 to 90 wt % vinyl aromatic hydrocarbon and 10 to 25 wt % conjugated diene hydrocarbon; and a layer (B1) containing a block copolymer of 70 to 85 wt % vinyl aromatic hydrocarbon and 15 to 30 wt % conjugated diene hydrocarbon; or a layer (B2) containing a resin composition containing a copolymer of 98 to 40 wt % vinyl aromatic hydrocarbon and 2 to 60 wt % aliphatic unsaturated carboxylic acid ester.

First claim

The invention claimed is:

1. A multilayer heat-shrinkable styrene-based film comprising a layer (B1) between two layers (A),
each of the layers (A) comprising 1 to 1.8 parts by weight of high impact polystyrene resin and 0.04 to 0.12 parts by weight of organic fine particles having a mean particle diameter of 0.5 to 5 μm per 100 parts by weight of a block copolymer of 80 to 90 wt % vinyl aromatic hydrocarbon and 10 to 20 wt % conjugated diene hydrocarbon,
the layer (B1) comprising 55 to 100 wt % of a block copolymer of 70 to 85 wt % vinyl aromatic hydrocarbon and 15 to 30 wt % conjugated diene hydrocarbon.

2. A multilayer heat-shrinkable styrene-based film according to claim 1 , wherein, in each of the layers (A), the block copolymer of a vinyl aromatic hydrocarbon and a conjugated diene hydrocarbon is a styrene-butadiene block copolymer (85 wt % styrene and 15 wt % butadiene); the high impact polystyrene is a styrene-butadiene graft polymer; and the organic fine particles are particles of cross-linked methyl methacrylate-styrene copolymer.

3. A multilayer heat-shrinkable styrene-based film according to claim 1 , wherein, in the layer (B1), the block copolymer of a vinyl aromatic hydrocarbon and a conjugated diene hydrocarbon is a block copolymer of styrene and 1,3-butadiene.

4. A multilayer heat-shrinkable styrene-based film according to claim 1 , wherein a rubber phase of the high impact polystyrene has a particle diameter of 1 to 3 μm.

5. A multilayer heat-shrinkable styrene-based film according to claim 1 , wherein the total thickness of the multilayer heat-shrinkable styrene-based film is 30 to 70 μm, the thickness of each of the layers (A) is 2.5 to 17.5 μm, and the thickness of the layer (B1) is 25 to 58.3 μm.

6. A multilayer heat-shrinkable styrene-based film according to claim 1 , having a three-layer structure of layer (A)/layer (B1)/layer (A).

7. A multilayer heat-shrinkable styrene-based film according to claim 6 , further comprising a layer (C) as an intermediate layer between the layer (B1) and one or each of the layers (A);
the layer (C) being at least one element selected from the group consisting of styrene homopolymers, styrene-conjugated diene block copolymer hydrogenation products, a mixture of resins that form the layers (A) and the layer (B1).

8. A multilayer heat-shrinkable styrene-based film according to claim 7 , having a five-layer structure of layer (A)/layer (C)/layer (B1)/layer (C)/layer (A).

9. A method for producing a multilayer heat-shrinkable styrene-based film, the method comprising the steps of extruding and stretching:
a resin composition (a) comprising 1 to 1.8 parts by weight of high impact polystyrene resin and 0.04 to 0.12 parts by weight of organic fine particles having a mean particle diameter of 0.5 to 5 μm per 100 parts by weight of a block copolymer of 80 to 90 wt % vinyl aromatic hydrocarbon and 10 to 20 wt % conjugated diene hydrocarbon; and
a resin composition (b1) comprising 55 to 100 wt % of a block copolymer of 70 to 85 wt % vinyl aromatic hydrocarbon and 15 to 30 wt % conjugated diene hydrocarbon, so that the resin composition (a) forms a front layer and a back layer, and the resin composition (b1) forms a core layer.

Assignees

• Maruo Masaharu
• Ohno Naoki
• Tanaka Tadayoshi
• Furukawa Hiroyuki
• Gunze Kk

Inventors

• Maruo Masaharu
• Ohno Naoki
• Tanaka Tadayoshi
• Furukawa Hiroyuki

Classifications

• B32B27/08

  of synthetic resin · CPC title

• B32B27/18

  characterised by the use of special additives · CPC title

• C08L51/04 Primary

  grafted on to rubbers · CPC title

• B32B2519/00

  Labels, badges · CPC title

• B32B25/14

  comprising {synthetic rubber copolymers (B32B25/18 and B32B25/20 take precedence)} · CPC title