Process for producing water-absorbing polymer particles with high free swell rate

Patent metadata

Field	Value
Publication number	US-9833769-B2
Application number	US-201213365807-A
Country	US
Kind code	B2
Filing date	Feb 3, 2012
Priority date	Feb 7, 2011
Publication date	Dec 5, 2017
Grant date	Dec 5, 2017

Abstract

The invention relates to a process for producing water-absorbing polymer particles with high free swell rate, comprising the steps of polymerization, drying, grinding, classification and thermal surface postcrosslinking, remoisturization and drying again.

First claim

The invention claimed is:

1. A process for producing water-absorbing polymer particles with high free swell rate by
(i) polymerizing a monomer solution or suspension comprising
a) at least one ethylenically unsaturated monomer which bears an acid group and may be at least partly neutralized,
b) at least one crosslinker,
c) at least one initiator,
d) optionally one or more ethylenically unsaturated monomer copolymerizable with the monomer mentioned under a), and
e) optionally one or more water-soluble polymer to form a polymer gel,

(ii) drying, grinding, and classifying the polymer gel of step (i), the polymer particles being classified to a particle size in a range from m to n pm, wherein m is in a range from 50 to 300 and n is in a range from 400 to 1200;
(iii) coating the classified polymer particles with
f) at least one surface postcrosslinker, and
g) optionally at least one polyvalent metal cation;

(iv) thermally surface postcrosslinking the coated classified particles of step (iii);
(v) cooling the surface postcrosslinked particles of step (iv);
(vi) adding sufficient gaseous water to the cooled postcrosslinked particles of step (v) to increase the moisture content of the postcrosslinked particles by 1 to 150% by weight;
(vii) then drying the cooled postcrosslinked particles of step (vi) by heating the postcrosslinked particles at a sufficient temperature of less than 150° C. to form visible cracks in the particle surface under 20,000-fold magnification.

2. The process according to claim 1 , wherein the moisture content of the water-absorbing polymer particles after the thermal postcrosslinking is increased by 10 to 25% by weight.

3. The process according to claim 1 , wherein the water-absorbing polymer particles after increasing the moisture content are dried at a temperature of less than 130° C.

4. The process according to claim 1 , wherein the water-absorbing polymer particles after increasing the moisture content are dried down to a moisture content of less than 10% by weight.

5. The process according to claim 1 , wherein the dried, ground, and classified polymer gel is coated with 0.05 to 0.2% by weight of the surface postcrosslinker f).

6. The process according to claim 1 , wherein the dried, ground, and classified polymer gel is coated with 0.02 to 0.8% by weight of the polyvalent metal cation g).

7. The process according to claim 1 , wherein the water-absorbing polymer particles before increasing the moisture content have a saline flow conductivity of at least 100×10 −7 cm 3 s/g and a vortex of at least 60 s.

8. The process according to claim 1 , wherein the water-absorbing polymer particles before increasing the moisture content have a centrifuge retention capacity of at least 15 g/g.

9. The process according to claim 1 , wherein the monomer a) is acrylic acid.

10. A hygiene article comprising water-absorbing polymer particles prepared according to claim 1 .

11. The process according to claim 1 , wherein the water-absorbing particles after increasing the moisture content in step (vii) are dried by heating at a temperature of 80° C. to less than 150° C.

12. Water-absorbing polymer particles obtainable by a process according to claim 1 .

13. Polymer particles according to claim 12 , wherein the polymerized monomer i) is polymerized acrylic acid.

14. A hygiene article comprising water-absorbing polymer particles according claim 12 .

Assignees

• Daniel Thomas
• Braig Volker
• Karim Asif
• Basf Se

Inventors

• Daniel Thomas
• Braig Volker
• Karim Asif

Classifications

• B01J20/264

  derived from different types of monomers, e.g. linear or branched copolymers, block copolymers, graft copolymers · CPC title

• B01J20/267

  Cross-linked polymers · CPC title

• B01J2220/68

  Superabsorbents · CPC title

• B01J20/28004

  Sorbent size or size distribution, e.g. particle size · CPC title

• B01J20/3021 Primary

  Milling, crushing or grinding · CPC title