Gypsum plaster-based material containing an EDTA metal complex

Patent metadata

Field	Value
Publication number	US-9764983-B2
Application number	US-201415109509-A
Country	US
Kind code	B2
Filing date	Dec 23, 2014
Priority date	Jan 3, 2014
Publication date	Sep 19, 2017
Grant date	Sep 19, 2017

Abstract

A plaster-based material, in particular a plasterboard intended for the interior fitting of dwellings, contains a metal complex of EDTA. The plaster-based material is used for reducing the amount of volatile organic compounds present in the atmosphere inside dwellings, offices or public buildings.

First claim

The invention claimed is:

1. A plaster-based building material, comprising a zinc complex of EDTA, wherein the zinc complex of EDTA is included in an amount selected to reduce an amount of ambient volatile organic compounds in an environment in which the building material is used.

2. The plaster-based building material according to claim 1 , wherein a total amount of the zinc complex of EDTA ranges from 0.0001 to 40 parts by weight per 100 parts by weight of plaster.

3. The plaster-based building material according to claim 1 , further comprising the following additives in the following weight proportions, expressed per 100 parts by weight of plaster:
0.1 to 15 parts of an adhesion agent,
0.001 to 10 parts of a setting accelerator,
0 to 10 parts of a biocide,
0.0001 to 1 part of a foaming agent,
0 to 10 parts of at least one water repellent,
0 to 20 parts of at least one fire retardant,
0 to 20 parts of at least one reinforcer,
0 to 20 parts of an agent adapted to trap formaldehyde,
0 to 20 parts of active charcoal or a zeolite.

4. The plaster-based building material according to claim 1 , wherein the plaster-based material is in the form of a powder, a paste or a plaster panel.

5. The plaster-based building material according to claim 4 , wherein the plaster-based material is a plasterboard.

6. The plaster-based building material according to claim 2 , wherein the total amount of the metal complex of EDTA ranges from 0.001 to 10 parts by weight per 100 parts by weight of plaster.

7. The plaster-based building material according to claim 6 , wherein the total amount of the metal complex of EDTA ranges from 0.05 to 5 parts by weight per 100 parts by weight of plaster.

8. The plaster-based building material according to claim 3 , wherein the adhesion agent is a starch, a dextrin or a vegetable flour.

9. The plaster-based building material according to claim 3 , wherein the setting accelerator is hydrated calcium sulfate or potassium sulfate.

10. The plaster-based building material according to claim 3 , wherein the biocide is sodium omadine.

11. The plaster-based building material according to claim 3 , wherein the foaming agent is sodium lauryl sulfate.

12. The plaster-based building material according to claim 3 , wherein the at least one water repellent is a siloxane or a polysiloxane.

13. The plaster-based building material according to claim 3 , wherein the at least one fire retardant is vermiculite, silica, a clay or metal fibres.

14. The plaster-based building material according to claim 3 , wherein the at least one reinforcer is polymer fibres, mineral fibres, animal or vegetable fibres.

15. The plaster-based building material according to claim 3 , wherein the agent adapted to trap formaldehyde is acetoacetamide, adipic acid dihydrazide or a protein.

Assignees

• Saint Gobain Placo

Inventors

• Chuda Katarzyna
• Demathieu-Roeltgen Caroline

Classifications

• C04B2111/00025

  Aspects relating to the protection of the health, e.g. materials containing special additives to afford skin protection · CPC title

• C04B28/14

  containing calcium sulfate cements {(gypsum-paper plates E04C)} · CPC title

• C04B28/145

  Calcium sulfate hemi-hydrate with a specific crystal form · CPC title

• C04B2111/00456

  Odorless cements · CPC title

• C04B24/383

  Cellulose or derivatives thereof · CPC title