Polymer substrate with hard coat layer and manufacturing method for such polymer substrate

Patent metadata

Field	Value
Publication number	US-9758630-B2
Application number	US-201515127035-A
Country	US
Kind code	B2
Filing date	Mar 27, 2015
Priority date	Mar 27, 2014
Publication date	Sep 12, 2017
Grant date	Sep 12, 2017

Abstract

The present invention realizes a polymer substrate with hard coating layer comprising a high level of environmental resistance and a high level of abrasion resistance.
A polymer substrate with hard coating layer is provided that comprises a polymer substrate ( 60 ) having a thickness of 1 mm to 20 mm and a hard coating layer ( 70,80 ) on the surface thereof. Here, in this polymer substrate with hard coating layer, the hard coating layer ( 70,80 ) is laminated on the surface of the polymer substrate, contains as a main component thereof a hydrolysis-condensation product of an organic silicon compound, has a thickness of 0.1 μm to 20 μm, makes direct contact with a cured underlayer on the opposite side of the polymer substrate, is formed from an organic silicon compound by PE-CVD, and satisfies all of the following requirements (a) to (c): (a) film thickness of the silicon oxide layer is within the range of 3.5 μm to 9.0 μm, (b) maximum indentation depth of the surface of the silicon oxide layer as determined by measuring nanoindentation under conditions of a maximum load of 1 mN is 150 nm or less, and (c) the value of critical compression ratio K of the silicon oxide layer, as defined by formula (1) in a 3-point bending test of the polymer substrate with hard coating layer that imparts indentation displacement in which the surface laminated with the silicon oxide layer becomes concave, is 0.975 or less.

First claim

What is claimed is:

1. A polymer substrate with hard coating layer, comprising a polymer substrate having a thickness of 1 mm to 20 mm and a hard coating layer on the surface thereof; wherein,
the hard coating layer comprises:
a cured underlayer laminated on the surface of the polymer substrate, containing as a main component thereof a hydrolysis-condensation product of an organic silicon compound, and having a thickness of 0.1 μm to 20 μm, and
a silicon oxide layer that makes direct contact with the cured underlayer on the opposite side from the polymer substrate, is formed by PE-CVD using an organic silicon compound as raw material, and satisfies all of the following requirements (a) to (c):
(a) film thickness of the silicon oxide layer is within the range of 3.5 μm to 9.0 μm,
(b) maximum indentation depth of the surface of the silicon oxide layer as determined by measuring nanoindentation under conditions of a maximum load of 1 mN is 150 nm or less, and
(c) the value of critical compression ratio K of the silicon oxide layer, as defined by formula (1) in a 3-point bending test of the polymer substrate with hard coating layer that imparts indentation displacement in which the surface laminated with the silicon oxide layer becomes concave, is 0.975 or less:
K =( R−D/ 2)/ R −(0.00215 ×d )

R =(( G/ 2) 2 +(δ L ) 2 )/(2 ×δL )   Formula (1)

(wherein,
D represents the total thickness (mm) of the polymer substrate with hard coating layer,
d represents the film thickness (μm) of the silicon oxide layer,
G represents the distance (mm) between two end fulcrum points in a 3-point bending tester,
δL, represents indentation displacement (mm), measured when the silicon oxide layer begins to separate from a cut line (separation starting line) drawn in advance at the location of the central fulcrum point where a weight is applied in a 3-point bending test, and
R represents the bend radius (mm) of the polymer substrate with hard coating layer, measured when the silicon oxide layer begins to separate from a cut line (separation starting line) drawn in advance at the location of the central fulcrum point where a weight is applied in a 3-point bending test).

2. The polymer substrate with hard coating layer according to claim 1 , wherein the ratio of infrared absorbance of the silicon oxide layer at a wave number of 930 cm −1 to that at a wave number of 1020 cm −1 (α 930 /α 1020 ) is 0.30 or less.

3. The polymer substrate with hard coating layer according to claim 2 , wherein the ratio of infrared absorbance of the silicon oxide layer at a wave number of 1280 cm −1 to that at a wave number of 1020 cm −1 (α 1280 /α 1020 ) is within the range of 0.002 to 0.020.

4. The polymer substrate with hard coating layer according to claim 2 , wherein indentation hardness of the surface of the silicon oxide layer as determined by measuring nanoindentation under conditions of a maximum load of 1 mN is 3 GPa or more.

5. The polymer substrate with hard coating layer according to claim 2 , wherein surface roughness (Ra) of the silicon oxide layer when measured using the dynamic force mode (DFM) of a scanning probe microscope under conditions of observing by 5.0 μm square is 5.0 nm or less.

6. The polymer substrate with hard coating layer according to claim 2 , wherein an adhesive layer containing an acrylic resin composition as a main component thereof and having a film thickness of 0.1 μm to 20 μm is interposed between the polymer substrate and the cured underlayer.

7. The polymer substrate with hard coating layer according to claim 1 , wherein the ratio of infrared absorbance of the silicon oxide layer at a wave number of 1280 cm −1 to that at a wave number of 1020 cm −1 (α 1280 /α 1020 ) is within the range of 0.002 to 0.020.

8. The polymer substrate with hard coating layer according to claim 7 , wherein indentation hardness of the surface of the silicon oxide layer as determined by measuring nanoindentation under conditions of a maximum load of 1 mN is 3 GPa or more.

9. The polymer substrate with hard coating layer according to claim 7 , wherein surface roughness (Ra) of the silicon oxide layer when measured using the dynamic force mode (DFM) of a scanning probe microscope under conditions of observing by 5.0 μm square is 5.0 nm or less.

10. The polymer substrate with hard coating layer according to claim 7 , wherein an adhesive layer containing an acrylic resin composition as a main component thereof and having a film thickness of 0.1 μm to 20 μm is interposed between the polymer substrate and the cured underlayer.

11. The polymer substrate with hard coating layer according to claim 1 , wherein indentation hardness of the surface of the silicon oxide layer as determined by measuring nanoindentation under conditions of a maximum load of 1 mN is 3 GPa or more.

12. The polymer substrate with hard coating layer according to claim 11 , wherein surface roughness (Ra) of the silicon oxide layer when measured using the dynamic force mode (DFM) of a scanning probe microscope under conditions of observing by 5.0 μm square is 5.0 μm or less.

13. The polymer substrate with hard coating layer according to claim 11 , wherein an adhesive layer containing an acrylic resin composition as a main component thereof and having a film thickness of 0.1 μm to 20 μm is interposed between the polymer substrate and the cured underlayer.

14. The polymer substrate with hard coating layer according to claim 1 , wherein surface roughness (Ra) of the silicon oxide layer when measured using the dynamic force mode (DFM) of a scanning probe microscope under conditions of observing by 5.0 μm square is 5.0 nm or less.

15. The polymer substrate with hard coating layer according to claim 1 , wherein an adhesive layer containing an acrylic resin composition as a main component thereof and having a film thickness of 0.1 μm to 20 μm is interposed between the polymer substrate and the cured underlayer.

16. A method for producing the polymer substrate with hard coating layer according to claim 1 , comprising: forming the cured underlayer by coating a precursor material composition, in which the degree of aging (Ag) as represented by the following formula has a value within the range of 0.80 to 0.85, on the polymer substrate followed by drying and heat curing:
Ag ={([ X ]+2×[ Y ]+3×[ Z ])/[ S ]}/3

(wherein,
with respect to the chemical shifts of silicon atoms of a hydrolysis-condensation product of the organic silicon compound, which is measured when a silicon atom of tetramethylsilane is assigned a value of 0 ppm after measuring the silicon nuclear magnetic resonance spectrum ( 29 Si-NMR) using heavy water(D 2 O) for the solvent under conditions consisting of an observation frequency of 79 MHz, observation pulse of 6.0 μs, repetition time of 30 seconds, and broadening factor of 5 Hz,
the integration value of all peaks within the range of −45.0 ppm to −70.0 ppm is defined as [S], and,
within that peak integration value,
the peak integration value within the range of −45.0 ppm to −52.5 ppm is defined as [X],
the peak integration value within the range of −52.5 ppm to −61.0 ppm is defined as [Y], and
the peak integration value within the range of −61.0 ppm to −70.0 ppm is defined as [Z].

17. A method for producing the polymer substrate with hard coating layer according to claim 1 , comprising: adjusting the surface of the cured underlayer so that surface roughness (Ra) in the case of having measured with the dynamic force mode (DFM) of a scanning probe microscope under conditions of observing by 5 μm sq

Assignees

• Teijin Ltd
• Tsukishima Kikai Co

Inventors

• Kon Tatsuichirou
• Ekinaka Tatsuya
• Kishimoto Hiroshi
• Morita Yume
• Suga Takehiro
• Ogata Satoshi
• Nakagomi Masato

Classifications

• C08J7/0427

  with only one layer of a composition containing a polymer binder (with more layers C08J7/042) · CPC title

• C23C16/402

  Silicon dioxide · CPC title

• C23C16/02

  Pretreatment of the material to be coated (C23C16/04 takes precedence) · CPC title

• C23C16/5096

  Flat-bed apparatus · CPC title

• C23C16/45572

  Cooled nozzles · CPC title