Method for preparing a hydrogel matrix by photopolymerization

Patent metadata

Field	Value
Publication number	US-9758598-B2
Application number	US-201214359425-A
Country	US
Kind code	B2
Filing date	Aug 29, 2012
Priority date	Nov 28, 2011
Publication date	Sep 12, 2017
Grant date	Sep 12, 2017

Abstract

The invention relates to a method for preparing a hydrogel type matrix comprising at least two contiguous zones with distinct stiffnesses, comprising a step to photopolymerize a solution comprising one or several polymerizable compounds and a photopolymerization initiator, by application of light onto the entire solution and at a different intensity in at least two zones of the solution, as a result of which a hydrogel matrix is obtained comprising at least two contiguous zones with distinct stiffnesses, characterized in that the photopolymerization step is done in the presence of a polymerization catalyst.

First claim

The invention claimed is:

1. A method for preparing a hydrogel type matrix comprising at least two contiguous zones with distinct stiffnesses comprising
photopolymerizing a solution in the presence of a polymerization catalyst, said solution comprising one or several polymerizable compounds and a photopolymerization initiator, by applying light onto the entire solution and at a different intensity in at least two zones of the solution, thereby obtaining a hydrogel matrix comprising at least two contiguous zones with distinct stiffnesses.

2. A method according to claim 1 , wherein the hydrogel type matrix is made from a material selected from the group consisting of:
polyacrylamides;
polyethyleneglycols containing repetitive patterns derived from polymerization of acrylate or methacrylate compounds;
polysaccharides, optionally modified;
(co)polymers derived from polymerization of diacrylate and/or (meth)acrylate compounds;
polyvinyl alcohols containing repetitive patterns derived from polymerization of acrylate or methacrylate compounds;
dextranes containing repetitive patterns derived from polymerization of (meth)acrylate compounds;
polypropylene fumarates and derivatives thereof; and
combinations thereof.

3. A method according to claim 1 , wherein the photopolymerization initiator is selected from the group consisting of aromatic ketones, acridine compounds and fluorone compounds.

4. A method according to claim 1 , wherein the polymerization catalyst is an amine compound.

5. A method according to claim 1 , wherein the solution further comprises one or several ingredients selected from the group consisting of stains, cross-linking agents, water and mixtures thereof.

6. A method according to claim 1 , wherein light is applied to the solution through a stencil, delimiting zones with distinct light intensity.

7. A method according to claim 1 , wherein light is applied according to a distribution with spatially modulated intensity.

8. A method according to claim 1 , wherein the hydrogel type matrix comprises at least two contiguous zones with distinct stiffnesses with a stiffness gradient of the order of 1 kPa/μm.

9. A method according to claim 1 , further comprising a matrix functionalization step after the photopolymerizing, using a protein inducing cell adhesion through integrins.

10. An in vitro cell adhesion method comprising:
a) preparing a hydrogel type matrix according to claim 1 ;
b) depositing cells of one or several types on the matrix obtained in step a), such that the cells of at least one of the types adhere entirely or partly to some zones of the matrix with higher stiffness than contiguous zones.

11. An in vitro cell shaping method comprising:
a) preparing a hydrogel type matrix according to claim 1 ;
b) depositing cells of one or several types on the matrix obtained in step a), such that the cells of at least one of the types are concentrated entirely or partly on some zones of the matrix with higher stiffness than contiguous zones and adopt the shape of said higher stiffness zones.

12. A method for preparing a hydrogel type matrix comprising at least two contiguous zones with distinct stiffnesses comprising photopolymerizing a solution in the presence of a polymerization catalyst, said solution comprising one or several polymerizable compounds and a photopolymerization initiator, by application of light onto the entire solution and at a different intensity in at least two zones of the solution, wherein a hydrogel matrix is obtained comprising at least two contiguous zones with distinct stiffnesses and, wherein the solution comprises acrylamide, a photopolymerization initiator with the following formula:

where Ph denotes a phenyl group,
n-propylamine as the polymerization catalyst, N,N′-methylenebisacrylamide as the cross-linking agent and water.

Assignees

• Gulino Danielle
• Nicolas Alice
• Commissariat Energie Atomique
• Centre Nat Rech Scient

Inventors

• Gulino Danielle
• Mgharbel Abbas
• Nicolas Alice

Classifications

• G03F7/20

  Exposure; Apparatus therefor (photographic printing apparatus for making copies G03B27/00) · CPC title

• C12N11/08

  the carrier being a synthetic polymer · CPC title

• C08F120/56

  Acrylamide; Methacrylamide · CPC title

• C08F220/56

  Acrylamide; Methacrylamide · CPC title

• C08F2/48 Primary

  by ultraviolet or visible light · CPC title