Sizing compositions and glass fiber reinforced thermoplastic composites

Patent metadata

Field	Value
Publication number	US-9758429-B2
Application number	US-232007-A
Country	US
Kind code	B2
Filing date	Dec 14, 2007
Priority date	Dec 15, 2006
Publication date	Sep 12, 2017
Grant date	Sep 12, 2017

Abstract

The present invention relates to sizing compositions, glass fibers at least partially coated with sizing compositions, and glass fiber reinforced composite materials. In one embodiment, a sizing composition comprises at least one maleic anhydride copolymer, at least one coupling agent, and a reaction product of an alkoxylated amine and a polycarboxylic acid, which is further reacted with an epoxy compound.

First claim

That which is claimed is:

1. A polyamide-compatible sizing composition comprising:
at least one maleic anhydride copolymer, which is present in an amount greater than 10% by weight on a total solids basis;
at least one coupling agent; and
a third component that is a reaction product of an alkoxylated amine and a polycarboxylic acid, which is further reacted with an epoxy compound;
wherein the third component is present in an amount greater than about 50 weight percent of the sizing composition on a total solids basis.

2. The sizing composition of claim 1 , wherein the third component is present in an amount greater than about 70 weight percent of the sizing composition on a total solids basis.

3. The sizing composition of claim 1 , wherein the at least one maleic anhydride copolymer comprises a maleic anhydride monomer and a monomer selected from the group consisting of ethylene, butadiene, isobutylene, and mixtures thereof.

4. The sizing composition of claim 3 , wherein the at least one maleic anhydride copolymer is present in an amount less than about 50 weight percent of the sizing composition on a total solids basis.

5. The sizing composition of claim 3 , wherein the at least one maleic anhydride copolymer is present in an amount up to about 40 weight percent of the sizing composition on a total solids basis.

6. The sizing composition of claim 1 , wherein the maleic anhydride copolymer comprises carboxylate moieties, carboxylate salt moieties, amide moieties, imide moieties, or combinations thereof.

7. The sizing composition of claim 1 , wherein the at least one coupling agent comprises a silane.

8. The sizing composition of claim 7 , wherein the silane comprises an aminosilane.

9. The sizing composition of claim 1 wherein the at least one coupling agent is present in an amount up to about 20 weight percent of the sizing composition on a total solids basis.

10. The sizing composition of claim 1 , further comprising at least one additional component, the at least one additional component comprising a polyester, polyvinyl alcohol, polyurethane, polyvinylpyrrolidone, fatty acid ester of a polyethylene glycol, acrylic, wax, chemically modified rosin, or epoxide.

11. The sizing composition of claim 1 , wherein the alkoxylated amine comprises an alkoxylated fatty amine.

12. The sizing composition of claim 11 , wherein the alkoxylated fatty amine comprises an alkoxylated dodecyl amine, alkoxylated tetradecyl amine, alkoxylated hexadecyl amine, alkoxylated stearyl amine, alkoxylated octadecyl amine, or mixtures thereof.

13. The sizing composition of claim 1 , wherein the alkoxylated amine comprises an ethoxylated amine, a propoxylated amine, a butoxylated amine, or mixtures thereof.

14. The sizing composition of claim 1 , wherein the polycarboxylic acid comprises an aromatic polycarboxylic acid.

15. The sizing composition of claim 14 , wherein the aromatic carboxylic acid comprises phthalic acid, terephthalic acid, isophthalic acid, or mixtures thereof.

16. The sizing composition of claim 1 , wherein the epoxy compound comprises a polyepoxy compound.

17. The sizing composition of claim 16 , wherein the polyepoxy compound comprises a diglycidyl ether, diglycidyl ester, or mixtures thereof.

18. The sizing composition of claim 17 , wherein the diglycidyl ether comprises an alkyl diglycidyl ether, aromatic diglycidyl ether, or mixtures thereof.

19. The sizing composition of claim 18 , wherein the aromatic diglycidyl ether comprises a bisphenol A diglycidyl ether.

20. A glass fiber at least partially coated with the sizing composition of claim 1 .

21. The glass fiber of claim 20 , wherein the glass fiber is a continuous glass fiber.

22. The glass fiber of claim 20 , wherein the glass fiber is a chopped glass fiber.

23. The glass fiber of claim 22 , wherein the chopped glass fiber has a length of at least about 3 mm.

24. The glass fiber of claim 22 , wherein the chopped glass fiber has a length up to about 50 mm.

25. The glass fiber of claim 22 , wherein the chopped glass fiber has a length greater than about 50 mm.

26. A composite composition comprising:
a polyamide resin; and
a plurality of glass fibers according to claim 20 .

27. The composite composition of claim 26 , wherein the plurality of glass fibers have an average aspect ratio of at least 50.

28. The composite composition of claim 26 , wherein the plurality of glass fibers have an average aspect ratio of at least 200.

29. The composite composition of claim 26 , wherein the plurality of glass fibers are present in an amount of at least about 10 weight percent of the composite.

30. The composite composition of claim 26 , wherein the plurality of glass fibers are present in an amount up to about 90 weight percent of the composite.

31. The sizing composition of claim 1 , wherein the at least one maleic anhydride copolymer is present in an amount less than about 40 weight percent of the sizing composition on a total solids basis and wherein the at least one coupling agent is present in an amount between about 2 and about 15 weight percent of the sizing composition on a total solids basis.

32. A method of making a glass fiber reinforced composite comprising:
providing a plurality of continuous glass fibers;
at least partially coating the plurality of continuous fibers with a sizing composition comprising: (a) at least one maleic anhydride copolymer, which is present in an amount greater than 10% by weight on a total solids basis, (b) at least one coupling agent, and (c) a third component that is a reaction product of an alkoxylated amine and a polycarboxylic acid, which is further reacted with an epoxy compound, which is present in an amount greater than about 50 weight percent on a total solids basis; and
disposing the plurality of coated continuous glass fibers in a polyimide resin.

33. The method of claim 32 , further comprising chopping the plurality of coated continuous glass fibers prior to disposing the glass fibers in the polyamide resin.

34. The method of claim 32 , wherein the at least one maleic anhydride copolymer is present in an amount less than about 40 weight percent of the sizing composition on a total solids basis and wherein the at least one coupling agent is present in an amount between about 2 and about 15 weight percent of the sizing composition on a total solids basis.

35. A polyamide-compatible sizing composition comprising:
at least one maleic anhydride copolymer, which is present in amount greater than 10% by weight on a total solids basis;
at least one coupling agent; and
a third component that is a reaction product of an alkoxylated amide and a polycarboxylic acid, which is further reacted with an epoxy compound;
wherein the third component is present in an amount greater than about 50 weight percent of the sizing composition on a total solids basis.

36. The sizing composition of claim 35 , wherein the at least one maleic anhydride copolymer is present in an amount less than about 40 weight percent of the sizing composition on a total solids basis and wherein the at least one coupling agent is present in an amount between about 2 and about 15 weight percent of the sizing composition on a total solids basis.

Assignees

• Dijt Jacob Cornelis
• Van Der Woude Jacob Hendricus
• Boelman Ronald
• Ppg Ind Ohio Inc

Inventors

• Dijt Jacob Cornelis
• Van Der Woude Jacob Hendricus
• Boelman Ronald

Classifications

• D06M15/592

  made from polymerised unsaturated fatty acids and polyamines · CPC title

• C03C25/26

  Macromolecular compounds or prepolymers · CPC title

• Y10T428/2964

  Artificial fiber or filament · CPC title

• C08J5/08

  glass fibres · CPC title

• D06M15/55

  Epoxy resins · CPC title