Cr-containing austenitic alloy and method for producing the same

Patent metadata

Field	Value
Publication number	US-9695486-B2
Application number	US-201314388283-A
Country	US
Kind code	B2
Filing date	Feb 27, 2013
Priority date	Mar 28, 2012
Publication date	Jul 4, 2017
Grant date	Jul 4, 2017

Abstract

There is provided a Cr-containing austenitic alloy having a chromium oxide film with a thickness of 5 nm or larger on the surface, wherein the content of Mn in a base metal is, by mass percent, less than 0.1%. The chemical composition of the base metal desirably consists of, by mass percent, C: 0.15% or less, Si: 1.00% or less, Mn: less than 0.1%, P: 0.030% or less, S: 0.030% or less, Cr: 10.0 to 40.0%, Ni: 8.0 to 80.0%, Ti: 0.5% or less, Cu: 0.6% or less, Al: 0.5% or less, and N: 0.20% or less, the balance being Fe and impurities.

First claim

What is claimed is:

1. A Cr-containing austenitic alloy having a base metal and a chromium oxide film consisting essentially of Cr 2 O 3 , MnCr 2 O 4 , TiO 2 , Al 2 O 3 and SiO 2 with a thickness of 5 nm or larger, wherein the chemical composition of the base metal consists of, by mass percent, C: 0.15% or less, Si: 1.00% or less, Mn: less than 0.1%, P: 0.030% or less, S: 0.030% or less, Cr: 10.0 to 40.0%, Ni: 55 to 80.0%, Ti: 0.5% or less, Cu: 0.6% or less, Al: 0.5% or less, and N: 0.20% or less, the balance being Fe and impurities, and wherein the chromium oxide film is formed directly on a surface of the base metal or directly on another oxide layer formed directly on a surface of the base metal.

2. The Cr-containing austenitic alloy according to claim 1 , wherein the thickness of the chromium oxide film is smaller than 180 nm.

3. The Cr-containing austenitic alloy according to claim 2 , wherein the Mn/Cr ratio in a surface layer of the chromium oxide film is, by atom ratio, 0.00001 or higher and lower than 0.05.

4. The Cr-containing austenitic alloy according to claim 3 , wherein the Cr-containing austenitic alloy is used as a member for a nuclear plant.

5. The Cr-containing austenitic alloy according to claim 2 , wherein the Cr-containing austenitic alloy is used as a member for a nuclear plant.

6. The Cr-containing austenitic alloy according to claim 1 , wherein the Mn/Cr ratio in a surface layer of the chromium oxide film is, by atom ratio, 0.00001 or higher and lower than 0.05.

7. The Cr-containing austenitic alloy according to claim 6 , wherein the Cr-containing austenitic alloy is used as a member for a nuclear plant.

8. The Cr-containing austenitic alloy according to claim 1 , wherein the Cr-containing austenitic alloy is used as a member for a nuclear plant.

9. A method for producing the Cr-containing austenitic alloy according to claim 1 , wherein the surface of the Cr-containing austenitic alloy, in which the content of Mn in the base metal is, by mass percent, less than 0.1%, is heated to the temperature range of 600 to 1200° C. in a gaseous mixture atmosphere in which water vapor is contained in a non-oxidizing gas, and thereby a chromium oxide film is formed on the surface of the Cr-containing austenitic alloy.

10. The method for producing a Cr-containing austenitic alloy according to claim 9 , wherein the water vapor concentration is 1000 ppm or less.

Assignees

• Nippon Steel & Sumitomo Metal Corp

Inventors

• Masaki Yasuhiro
• Kanzaki Manabu
• Hidaka Yasuyoshi
• Uehira Akihiro
• Miyahara Osamu

Classifications

• C22C19/058

  without Mo and W · CPC title

• C22C38/40

  with nickel · CPC title

• Y02P10/253

  Cross-Sectional Technologies · mapped topic

• C22C38/06

  containing aluminium · CPC title

• Y10T428/265

  1 mil or less · CPC title