Lithium silicate glass ceramic and lithium silicate glass comprising a tetravalent metal oxide

Patent metadata

Field	Value
Publication number	US-9695082-B2
Application number	US-201214001185-A
Country	US
Kind code	B2
Filing date	Oct 11, 2012
Priority date	Oct 14, 2011
Publication date	Jul 4, 2017
Grant date	Jul 4, 2017

Abstract

Lithium silicate glass ceramics and glasses containing specific oxides of tetravalent elements are described which crystallize at low temperatures and are suitable in particular as dental materials.

First claim

The invention claimed is:

1. Lithium silicate glass ceramic which comprises
a tetravalent metal oxide selected from ZrO 2 , TiO 2 , CeO 2 , GeO 2 , SnO 2 and mixtures thereof,
67.0 to 79.0 wt.-% SiO 2 ,
at least 12.1 wt.-% Li 2 O,
0 to 6.0 wt.-% Al 2 O 3 ,
less than 0.1 wt.-% La 2 O 3 ,
less than 1.0 wt.-% K 2 O and
less than 2.0 wt.-% Na 2 O,and
which has lithium metasilicate as a main crystal phase and has more than 5 vol.-%, lithium metasilicate crystals.

2. Glass ceramic according to claim 1 , wherein lithium silicate glass ceramic is excluded which comprises at least 6.1 wt.-% ZrO 2 .

3. Glass ceramic according to claim 1 , wherein glass ceramic is excluded which comprises at least 8.5 wt.-% transition metal oxide selected from the group consisting of oxides of yttrium, oxides of transition metals with an atomic number from 41 to 79 and mixtures of these oxides.

4. Glass ceramic according to claim 1 , which comprises less than 0.5 wt.-% K 2 O.

5. Glass ceramic according to claim 1 , which comprises less than 1.0 wt.-% Na 2 O.

6. Glass ceramic according to claim 1 , which is substantially free from La 2 O 3 .

7. Glass ceramic according to claim 1 , which comprises the tetravalent metal oxide or mixtures thereof in an amount of from 0.1 to 15 wt.-%.

8. Glass ceramic according to claim 1 , which comprises 12.5 to 20.0 wt.-% Li 2 O.

9. Glass ceramic according to claims 1 , which comprises 0 to 10.0 wt.-% P 2 O 5 .

10. Glass ceramic according to claims 1 , which comprises at least one of the following components:

Component
wt.-%

Li 2 O
12.5 to 20.0

tetravalent metal
 2.0 to 15.0

oxide or mixtures

P 2 O 5
  0 to 7.0

Al 2 O 3
  0 to 6.0.

11. Lithium silicate glass ceramic according to claims 1 , which comprises SiO 2 and Li 2 O in a molar ratio of from 1.7 to 3.1.

12. Glass ceramic according to claim 1 , wherein the glass ceramic is present in the form of a powder, a granular material, a blank or a dental restoration.

13. Process for the preparation of the glass ceramic according to claim 1 , wherein a starting glass with nuclei or a glass ceramic with lithium metasilicate as main crystal phase is subjected to at least one heat treatment in the range of from 450 to 950° C,.

14. Process of using a glass ceramic which comprises
tetravalent metal oxide selected from ZrO 2 , TiO 2 , CeO 2 , GeO 2 , SnO 2 and mixtures thereof,
67.0 to 79.0 wt.-% SiO 2 ,
at least 12.1 wt.-% Li 2 O,
less than 0.1 wt.-% La 2 O 3 ,
less than 1.0 wt.-% K 2 O and
less than 2.0 wt.-% Na 2 O, and
which has lithium metasilicate as a main crystal phase and has more than 5 vol.-% lithium metasilicate crystals,
as dental material for the preparation of dental restorations.

15. Process for the preparation of a lithium silicate glass ceramic which comprises
tetravalent metal oxide selected from ZrO 2 , TiO 2 , CeO 2 , GeO 2 , SnO 2 and mixtures thereof,
at least 12.1 wt. -% Li 2 ° ,
less than 0.1 wt.-% La 2 O 3 ,
less than 1.0 wt.-% K 2 O and
less than 2.0 wt.-% Na 2 O,
wherein
(a) a starting glass which comprises the components of the glass ceramic is subjected to a heat treatment at a temperature of from 480 to 520° C. for a period of from 10 min to 120 min in order to form a glass with nuclei which are suitable for forming lithium disilicate crystals, and
(b)the glass with nuclei is subjected to a heat treatment at a temperature of from 640 to 740° C. in order to form a glass ceramic with lithium disilicate as main crystal phase.

16. Process for the preparation of a lithium silicate glass ceramic according to claim 15 , which has lithium disilicate as a main crystal phase and a fracture toughness, measured as K IC value, of at least 1.9 MPa·m 0.5 .

17. Process of preparing dental restorations according to claim 14 , wherein the glass ceramic is shaped by pressing or machining to the desired dental restoration.

18. Process for the preparation of a lithium silicate glass ceramic according to claim 15 , which has lithium disilicate as a main crystal phase and has more than 10 vol.-% lithium disilicate crystals.

Assignees

• Ivoclar Vivadent Ag

Inventors

• Ritzberger Christian
• Apel Elke
• Höland Wolfram
• Rheinberger Volker

Classifications

• A61K6/802

  comprising ceramics · CPC title

• A61K6/818

  comprising zirconium oxide · CPC title

• A61K6/816

  comprising titanium oxide · CPC title

• A61C13/08

  Artificial teeth; Making same (kilns for artificial teeth F27B) · CPC title

• C03C10/0027

  containing SiO2, Al2O3, Li2O as main constituents · CPC title