Thermoplastic polymer composition and molded article

Patent metadata

Field	Value
Publication number	US-9670354-B2
Application number	US-201113818695-A
Country	US
Kind code	B2
Filing date	Aug 24, 2011
Priority date	Aug 27, 2010
Publication date	Jun 6, 2017
Grant date	Jun 6, 2017

Abstract

A thermoplastic polymer composition which is excellent in flexibility, mechanical properties, moldability, and particularly in heat resistance and is capable of adhering to ceramics, metals, and synthetic resins even at low temperature (for example, 190° C. or lower) without the treatment with a primer, and a molded product produced by using the thermoplastic polymer composition are described. The thermoplastic polymer composition includes 100 parts by mass of a thermoplastic elastomer (A), 1 to 100 parts by mass of a polyvinyl acetal resin (B), and 5 to 100 parts by mass of a polar group-containing polypropylene resin (C). The thermoplastic elastomer (A) is a block copolymer which is constituted by a polymer block including aromatic vinyl compound units and a polymer block including isoprene units, butadiene units, or isoprene/butadiene units wherein the total of a content of 1,2-bonding and a content of 3,4-bonding is 40 mol % or more, or the thermoplastic elastomer (A) is a hydrogenated product of the block copolymer.

First claim

What is claimed is:

1. A thermoplastic polymer composition, comprising:
100 parts by mass of a thermoplastic elastomer;
1 to 45 parts by mass of a polyvinyl acetal resin per 100 parts of the thermoplastic elastomer, wherein the polyvinyl acetal resin is obtained by acetalizing a polyvinyl alcohol having an average degree of polymerization of 100 to 4,000 to a degree of acetalization of 55 to 88% by mole; and
20 to 100 parts by mass of a polar group-comprising polypropylene resin per 100 parts of the thermoplastic elastomer,
wherein the thermoplastic elastomer is a block copolymer or a hydrogenated product of the block copolymer, the block copolymer comprises a polymer block comprising an aromatic vinyl compound unit and a polymer block comprising an isoprene unit, a butadiene unit, or an isoprene/butadiene unit, and a total of a content of 1,2-bonding and a content of 3,4-bonding is 40 mol % or more,
wherein the polar group-comprising polypropylene resin comprises, in polymerized form, from 0 to 45 mol % of α-olefin units other than propylene, based on a total of constitutional units in the polar group-containing polypropylene resin,
wherein a melt flow rate (MFR) of the polar-group comprising polypropylene resin is 0.1 to 100 g/10 min, when measured at 230° C. under a load of 2.16 kg (21.18 N),
wherein a hardness of the thermoplastic polymer composition is 93 or less, when measured according to JIS-A method of JIS K 6253, and
wherein the thermoplastic polymer composition has both an adhesion strength on a glass plate and an adhesion strength on an aluminum plate of 20 N/25mm or more respectively, wherein the adhesion strength is determined by:
washing both surfaces a glass plate with an aqueous solution of surfactant, methanol, acetone, and distilled water successively in this order, and washing both sides of an aluminum plate with an aqueous solution of surfactant and distilled water successively in this order;
drying the glass plate and the aluminum plate;
piling the glass plate thus treated, each of a sheet of the thermoplastic polymer composition and a polyethylene terephthalate (PET) sheet having a thickness of 50 μm at the center of a metal spacer in this order;
piling the aluminum plate thus treated, each of a sheet of the thermoplastic polymer composition and a polyethylene terephthalate (PET) sheet having a thickness of 50 μm at the center of a metal spacer in this order;
placing the piled sheets together with the metal spacer between two sheets of polytetrafluoroethylene, which is then put between two metal plates and compression-molded with a press molding machine at a temperature 180° C. under a load of 2 N/mm 2 for 3 min, thereby obtaining a laminate of PET/thermoplastic polymer composition/glass plate or a laminate of PET/thermoplastic polymer composition/aluminum plate;
measuring the peeling strength between the thermoplastic polymer composition layer and the glass plate and the peeling strength between the thermoplastic polymer composition layer and the aluminum plate at a peel angle of 180°, a tensile speed of 50 mm/min and a temperature of 60° C. according to JIS K 6854-2.

2. The thermoplastic polymer composition according to claim 1 , further comprising 0.1 to 300 parts by mass of a softener.

3. The thermoplastic polymer composition according to claim 1 , further comprising 1 to 100 parts by mass of a tackifier resin.

4. The thermoplastic polymer composition according to claim 1 , wherein the polyvinyl acetal resin is a polyvinyl butyral.

5. The thermoplastic polymer composition according to claim 1 , wherein the polypropylene resin is a carboxylic acid-modified polypropylene resin.

6. The thermoplastic polymer composition according to claim 1 , wherein the block copolymer comprises a polymer block comprising an aromatic vinyl compound unit and a polymer block comprising an isoprene unit.

7. The thermoplastic polymer composition according to claim 1 , wherein the block copolymer comprises a polymer block comprising an aromatic vinyl compound unit and a polymer block comprising a butadiene unit.

8. The thermoplastic polymer composition according to claim 1 , wherein the block copolymer comprises a polymer block comprising an aromatic vinyl compound unit and a polymer block comprising an isoprene/butadiene unit.

9. The thermoplastic polymer composition according to claim 1 , wherein a total of a content of 1,2-bonding and a content of 3,4-bonding is 40 to 95 mol %.

10. The thermoplastic polymer composition according to claim 1 , wherein a total of a content of 1,2-bonding and a content of 3,4-bonding is 50 to 85 mol %.

11. The thermoplastic polymer composition according to claim 1 , wherein the polyvinyl acetal resin is obtained by acetalizing a polyvinyl alcohol having an average degree of polymerization of 100 to 3,000 to a degree of acetalization of 60 to 88% by mole.

12. The thermoplastic polymer composition according to claim 1 , wherein the polyvinyl acetal resin is obtained by acetalizing a polyvinyl alcohol having an average degree of polymerization of 250 to 2,000 to a degree of acetalization of 75 to 85% by mole.

13. The thermoplastic polymer composition according to claim 1 , having both an adhesion strength on a glass plate and an adhesion strength on an aluminum plate of 20 N/25mm or more respectively, wherein the adhesion strength is determined by:
washing both surfaces a glass plate with an aqueous solution of surfactant, methanol, acetone, and distilled water successively in this order, and washing both sides of an aluminum plate with an aqueous solution of surfactant and distilled water successively in this order;
drying the glass plate and the aluminum plate;
piling the glass plate thus treated, each of a sheet of the thermoplastic polymer composition and a polyethylene terephthalate (PET) sheet having a thickness of 50 μm at the center of a metal spacer in this order;
piling the aluminum plate thus treated, each of a sheet of the thermoplastic polymer composition and a polyethylene terephthalate (PET) sheet having a thickness of 50 μm at the center of a metal spacer in this order;
placing the piled sheets together with the metal spacer between two sheets of polytetrafluoroethylene, which is then put between two metal plates and compression-molded with a press molding machine at a temperature 240° C. under a load of 2 N/mm 2 for 3 min, thereby obtaining a laminate of PET/thermoplastic polymer composition/glass plate or a laminate of PET/thermoplastic polymer composition/aluminum plate;
measuring the peeling strength between the thermoplastic polymer composition layer and the glass plate and the peeling strength between the thermoplastic polymer composition layer and the aluminum plate at a peel angle of 180°, a tensile speed of 50 min/min, and a temperature of 60° C. according to JIS K 6854-2.

14. The thermoplastic polymer composition according to claim 1 , comprising 100 parts by mass of the thermoplastic elastomer, 5 to 45 parts by mass of the polyvinyl acetal resin, and 20 to 70 parts by mass of the polypropylene resin.

15. The thermoplastic polymer composition according to claim 14 , comprising 100 parts by mass of the thermoplastic elastomer, 10 to 45 parts by mass of the polyvinyl acetal resin, and 20 to 60 parts by mass of the polypropylene resin.

16. The thermoplastic polymer composition according to claim 14 , comprising 100 parts by mass of the thermoplastic elastomer, 15 to 45 parts by mass of the polyvinyl acetal resin, and 20 to 30 parts by mass of the polypropylene resin.

17. A molded product comprising the thermo

Assignees

• Minamide Asako
• Masuda Mikio
• Kuraray Co

Inventors

• Minamide Asako
• Masuda Mikio

Classifications

• Y10T428/31667

  Next to addition polymer from unsaturated monomers, or aldehyde or ketone condensation product · CPC title

• C08L29/14

  Homopolymers or copolymers of acetals or ketals obtained by polymerisation of unsaturated acetals or ketals or by after-treatment of polymers of unsaturated alcohols · CPC title

• C09J153/025

  modified · CPC title

• Y10T428/31696

  Including polyene monomers [e.g., butadiene, etc.] · CPC title

• B32B15/08

  of synthetic resin · CPC title