Poly(phenylene ether) composition and article

Patent metadata

Field	Value
Publication number	US-9567461-B2
Application number	US-201415109739-A
Country	US
Kind code	B2
Filing date	Dec 16, 2014
Priority date	Jan 20, 2014
Publication date	Feb 14, 2017
Grant date	Feb 14, 2017

Abstract

A composition is prepared by melt blending specific amounts of components including a poly(phenylene ether), a first hydrogenated block copolymer (HBC1) that includes a polystyrene-poly(ethylene-butylene)-polystyrene triblock copolymer having a polystyrene content of 50 to 75 weight percent, and a second hydrogenated block copolymer. The second hydrogenated block copolymer can selected from five different hydrogenated block copolymer types and their combinations. The composition exhibits high light transmittance, low haze, and high impact strength at low temperature, which make it useful for molding objects such as containers for storage in refrigerators and freezers.

First claim

The invention claimed is:

1. A composition comprising the product of melt blending components comprising:
29 to 95.5 weight percent of a poly(phenylene ether);
4 to 50 weight percent of a first hydrogenated block copolymer (HBC1) comprising a polystyrene-poly(ethylene-butylene)-polystyrene triblock copolymer having a polystyrene content of 50 to 75 weight percent; and
a second hydrogenated block (HBC2) copolymer comprising
(HBC2a) 0.5 to 18 weight percent of a polystyrene-poly(ethylene-butylene-styrene)-polystyrene triblock copolymer having a polystyrene content of 50 to 65 weight percent and a weight average molecular weight of 200,000 to 400,000 atomic mass units, wherein the first hydrogenated block copolymer and the second hydrogenated block copolymer are present in a weight ratio of 1:1 to 15:1;
(HBC2b) 2 to 10 weight percent of a polystyrene-poly(ethylene-butylene-styrene)-polystyrene triblock copolymer having a polystyrene content of 55 to 65 weight percent and a weight average molecular weight of 100,000 to 190,000 atomic mass units, wherein the first hydrogenated block copolymer and the second hydrogenated block copolymer are present in a weight ratio of 2:1 to 4:1, and wherein the melt blended components further comprise 0.2 to 1.5 weight percent of a C 3 -C 24 alpha-hydroxyketone;
(HBC2c) 1 to 5 weight percent of a polystyrene-poly(ethylene-butylene-styrene)-polystyrene triblock copolymer having a polystyrene content of 33 to 47 weight percent, wherein the second hydrogenated block copolymer and the first hydrogenated block copolymer are present in a weight ratio of 2:1 to 15:1;
(HBC2d) 1 to 20 weight percent of a polystyrene-poly(ethylene-butylene)-polystyrene triblock copolymer having a polystyrene content of 20 to 37 weight percent and a weight average molecular weight of 50,000 to 200,000 atomic mass units, wherein the second hydrogenated block copolymer and the first hydrogenated block copolymer are present in a weight ratio of 2:1 to 7:1, provided that when the first hydrogenated block copolymer amount is greater than or equal to 10 weight percent, the weight ratio of the second hydrogenated block copolymer and the first hydrogenated block copolymer is less than 5:1; or
(HBC2e) 0.5 to 15 weight percent of a polystyrene-poly(ethylene-butylene)-polystyrene triblock copolymer having a polystyrene content of 38 to 48 weight percent, wherein the first hydrogenated block copolymer and the second hydrogenated block copolymer are present in a weight ratio of 1.25:1 to 25:1, wherein the melt blended components further comprise 0.2 to 0.7 weight percent of a C 3 -C 24 alpha-hydroxyketone, provided that when the amount of the polystyrene-poly(ethylene-butylene)-polystyrene triblock copolymer having a polystyrene content of 38 to 48 weight percent is 0.5 weight percent, the amount of the first hydrogenated block copolymer is greater than 5 weight percent, and provided that the sum of the first hydrogenated block copolymer and the polystyrene-poly(ethylene-butylene)-polystyrene triblock copolymer having a polystyrene content of 38 to 48 weight percent is less than 46 weight percent;

wherein the melt blended components comprise 0 to 0.5 weight percent polyolefins;
provided that when the melt blended components comprise (HBC2b), the maximum amount of the poly(phenylene ether) is 94 weight percent; and provided that when the melt blended components comprise (HBC2c) or (HBC2d), the maximum amount of the poly(phenylene ether) is 95 weight percent.

2. The composition of claim 1 , exhibiting a correlated haze value less than or equal to 20%, a transmittance value greater than or equal to 60%, and a −20° C. multiaxial impact energy to failure value greater than or equal to 20 joules, wherein correlated haze and transmittance are determined at a sample thickness of 3.175 millimeters.

3. The composition of claim 1 , wherein the melt blended components further comprise 0.2 to 1.5 weight percent of the C 3 -C 24 alpha-hydroxyketone when the second hydrogenated block copolymer comprises (HBC2a) the polystyrene-poly(ethylene-butylene-styrene)-polystyrene triblock copolymer having a polystyrene content of 50 to 65 weight percent and a weight average molecular weight of 200,000 to 400,000 atomic mass units, (HBC2c) the polystyrene-poly(ethylene-butylene-styrene)-polystyrene triblock copolymer having a polystyrene content of 33 to 47 weight percent, or (HBC2d) the polystyrene-poly(ethylene-butylene)-polystyrene triblock copolymer having a polystyrene content of 20 to 37 weight percent and a weight average molecular weight of 50,000 to 200,000 atomic mass units.

4. The composition of claim 1 , wherein the melt blended components comprise 75 to 93 weight percent of the poly(phenylene ether).

5. The composition of claim 1 , wherein the second hydrogenated block copolymer comprises (HBC2a) the polystyrene-poly(ethylene-butylene-styrene)-polystyrene triblock copolymer having a polystyrene content of 50 to 65 weight percent and a weight average molecular weight of 200,000 to 400,000 atomic mass units.

6. The composition of claim 1 , wherein the second hydrogenated block copolymer comprises (HBC2b) the polystyrene-poly(ethylene-butylene-styrene)-polystyrene triblock copolymer having a polystyrene content of 55 to 65 weight percent and a weight average molecular weight of 100,000 to 190,000 atomic mass units.

7. The composition of claim 1 , wherein the second hydrogenated block copolymer comprises (HBC2c) the polystyrene-poly(ethylene-butylene-styrene)-polystyrene triblock copolymer having a polystyrene content of 33 to 47 weight percent.

8. The composition of claim 1 , wherein the second hydrogenated block copolymer comprises (HBC2d) the polystyrene-poly(ethylene-butylene)-polystyrene triblock copolymer having a polystyrene content of 20 to 37 weight percent and the weight average molecular weight of 50,000 to 200,000 atomic mass units.

9. The composition of claim 1 , wherein the second hydrogenated block copolymer comprises (HBC2e) the polystyrene-poly(ethylene-butylene)-polystyrene triblock copolymer having a polystyrene content of 38 to 48 weight percent.

10. The composition of claim 1 , wherein the first hydrogenated block copolymer has a weight average molecular weight of 50,000 to 200,000 atomic mass units.

11. The composition of claim 1 , wherein the first hydrogenated block copolymer comprises 10 to 20 weight percent of the polystyrene-poly(ethylene-butylene)-polystyrene triblock copolymer having a polystyrene content of 50 to 75 weight percent, and has a weight average molecular weight of 50,000 to 100,000 atomic mass units.

12. The composition of claim 1 , wherein the melt-blended components comprise 0 to 1 weight percent of ethylenically unsaturated rubber.

13. The composition of claim 1 , wherein the melt-blended components comprise 0 to 2 weight percent of homopolystyrene.

14. The composition of claim 1 , wherein the melt-blended components comprise 0 to 1 weight percent of radial block copolymers of an alkenyl aromatic monomer and a conjugated diene.

15. The composition of claim 1 , wherein the melt-blended components comprise 0 to 1 weight percent of polystyrene-poly(ethylene-butylene)-polystyrene triblock copolymers having a weight average molecular weight greater than 200,000 atomic mass units.

16. The composition of claim 1 , wherein the melt-blended components comprise 0 to 1 weight percent of hydrocarbon resins comprising aliphatic hydrocarbon resins, hydrogenated aliphatic hydrocarbon resins, aliphatic/aromatic hydrocarbon resins, hydrogenated aliphatic/aromatic hydrocarbon resins, cycloaliphatic hyd

Assignees

• Sabic Global Technologies Bv

Inventors

• Ziegler Christopher
• Balfour Kim G
• Vendon Mark Victor

Classifications

• C08L2205/02

  containing two or more polymers of the same C08L -group · CPC title

• C08L2205/03

  containing three or more polymers in a blend · CPC title

• C08K5/132

  Phenols containing keto groups {, e.g. benzophenones} · CPC title

• C08K5/07

  Aldehydes; Ketones · CPC title

• C08L53/025

  modified · CPC title