Pigmented coating composition with a phosphorus acid functionalized binder

Patent metadata

Field	Value
Publication number	US-9346972-B2
Application number	US-201414565920-A
Country	US
Kind code	B2
Filing date	Dec 10, 2014
Priority date	Dec 20, 2013
Publication date	May 24, 2016
Grant date	May 24, 2016

Abstract

The present invention is a composition comprising a) a stable aqueous dispersion of polymer particles functionalized with structural units of a phosphorus acid monomer or a salt thereof and; b) a water-soluble polymer functionalized with structural units of a sulfonic acid monomer or a salt thereof as well as a method comprising mixing the stable aqueous dispersion of the phosphorus acid functionalized polymer particles with the sulfonic acid functionalized polymer, and TiO 2 . The composition of the present invention is useful as a coatings formulation that provides improved hiding over phosphorus acid functionalized binders that do not include the water-soluble polymer. Alternatively, the same hiding benefit is seen at lower phosphorus acid concentration when the sulfonic acid functionalized polymer is present.

First claim

The invention claimed is:

1. A process for preparing a coatings composition comprising the steps of contacting: a) an aqueous solution of a water-soluble polymer functionalized with structural units of a sulfonic acid monomer or a salt thereof; b) a stable aqueous dispersion of polymer particles functionalized with structural units of a phosphorus acid monomer or a salt thereof; and c) TiO 2 ;
wherein the weight percent of the sulfonic acid functionalized polymer is from 0.1 to 10 percent, based on the weights of the sulfonic acid functionalized and the phosphorus acid functionalized polymer particles;
wherein the weight percent of the phosphorus acid functionalized polymer particles is from 20 to 80%, based on the weight of the sulfonic acid functionalized and the phosphorus acid functionalized polymer particles, and the TiO 2 ;
wherein the weight percent of the TiO 2 is from 20 to 80% based on the weight of the sulfonic acid functionalized polymer, the phosphorus acid functionalized polymer particles, and the TiO 2 ; and
wherein the weight percent of structural units of the phosphorus acid monomer or a salt thereof is from 0.1 to 5 weight percent, based on the weight of the phosphorus acid functionalized polymer particles.

2. The process of claim 1 wherein the stable aqueous dispersion of the phosphorus acid functionalized polymer particles are acrylic, styrene-acrylic, or vinyl ester-acrylic latex binders;
wherein weight percent of the sulfonic acid functionalized polymer is from 0.4 to 8 weight percent, based on the weight of the sulfonic acid functionalized polymer and the phosphorus acid functionalized polymer particles; and
wherein the sulfonic acid functionalized polymer or salt thereof is functionalized with structural units of a sulfonic acid monomer selected from the group consisting of 2-acrylamido-2-methylpropane sulfonic acid, vinyl sulfonic acid, 2-sulfoethyl acrylate, 2-sulfoethyl methacrylate, 3-sulfopropyl acrylate, 3-sulfopropyl methacrylate, sodium styrene sulfonate, and 2-propene-1-sulfonic acid, and salts thereof.

3. The process of claim 2 wherein the sulfonic acid monomer or salt thereof is 2-acrylamido-2-methylpropane sulfonic acid or a salt thereof, wherein the phosphorus acid functionalized polymer particles further comprise structural units of one or more monomers selected from the group consisting of methyl methacrylate, butyl acrylate, ethyl acrylate, 2-ethylhexyl acrylate, ureido methacrylate, styrene, vinyl acetate, and vinyl versatate;
wherein the weight percent of structural units of the phosphorus acid monomer or a salt thereof is from 0.2 to 4 weight percent, based on the weight of the phosphorus acid monomer functionalized polymer particles;
wherein the weight percent of the sulfonic acid functionalized polymer is from 0.4 to 4 weight percent, based on the weight of the sulfonic acid functionalized polymer and the itaconic acid functionalized polymer particles.

4. The process of claim 3 wherein the sulfonic acid functionalized polymer further comprises structural units of another monomer selected from the group consisting of acrylates, methacrylates, dialkylaminoalkyl acrylates, and dialkylaminoalkyl methacrylates.

5. The process of claim 4 wherein sulfonic acid functionalized polymer is a homopolymer of 2-acrylamido-2-methylpropane sulfonic acid or a salt thereof; or a copolymer comprising from 50 to 95 weight percent structural units of 2-acrylamido-2-methylpropane sulfonic acid or a salt thereof and from 5 to 50 weight percent structural units of 2-hydroxylpropyl acrylate, based on the weight of the 2-acrylamido-2-methylpropane sulfonic acid and the 2-hydroxylpropyl acrylate; wherein the weight percent of structural units of the phosphorus acid monomer or a salt thereof is from 0.2 to 1.5 weight percent, based on the weight of the phosphorus acid monomer functionalized polymer particles.

6. The process of claim 1 which further includes the step of mixing with the coatings composition one or more materials selected from the groups consisting of rheology modifiers; opaque polymers; fillers; colorants, other pigments including encapsulated or partially encapsulated pigments and opaque pigments; dispersants; wetting aids; dispersing aids; dispersant adjuvants; surfactants; co-solvents; coalescing agents and plasticizers; defoamers; preservatives; anti-mar additives; flow agents; leveling agents; slip additives; and neutralizing agents.

7. A composition comprising a) a stable aqueous dispersion of polymer particles functionalized with structural units of a phosphorus acid monomer or a salt thereof and; b) a water-soluble polymer functionalized with structural units of a sulfonic acid monomer or a salt thereof; wherein the weight percent of the sulfonic acid functionalized polymer is from 0.1 to 10 percent, based on the weights of the phosphorus acid functionalized polymer particles and sulfonic acid functionalized polymer; and the weight percent of the phosphorus acid functionalized polymer particles is from 90 to 99.9 weight percent; wherein the weight percent of structural units of phosphorus acid monomer or a salt thereof is from 0.1 to 5 weight percent, based on the weight of the phosphorus acid functionalized polymer particles.

8. The composition of claim 7 which further comprises from 20 to 80 weight percent TiO 2 based on the weight of the phosphorus acid functionalized polymer particles and the water-soluble polymer; wherein the weight percent of structural units of phosphorus acid monomer or a salt thereof is from 0.2 to 1.5 weight percent, based on the weight of the phosphorus acid functionalized polymer particles.

9. The composition of claim 8 which further comprises one or more materials selected from the groups consisting of rheology modifiers; opaque polymers; fillers; colorants, other pigments including encapsulated or partially encapsulated pigments and opaque pigments; dispersants; wetting aids; dispersing aids; dispersant adjuvants; surfactants; co-solvents; coalescing agents and plasticizers; defoamers; preservatives; anti-mar additives; flow agents; leveling agents; slip additives; and neutralizing agents.

Assignees

• Rohm & Haas

Inventors

• Bohling James C
• Derocher Jonathan
• Henderson Kevin J
• Van Dyk Antony K

Classifications

• C09D5/027

  Dispersing agents (anti-settling agents C09D7/45) · CPC title

• C08J3/203

  Solid polymers with solid and/or liquid additives · CPC title

• C09D5/02

  Emulsion paints {including aerosols} · CPC title

• C09D133/08 Primary

  Homopolymers or copolymers of acrylic acid esters · CPC title

• C09D7/00

  Features of coating compositions, not provided for in group C09D5/00 (driers C09F9/00); Processes for incorporating ingredients in coating compositions · CPC title