Method for producing chromium-containing molten steel

Patent metadata

Field	Value
Publication number	US-2023304110-A1
Application number	US-202118022791-A
Country	US
Kind code	A1
Filing date	Aug 23, 2021
Priority date	Sep 10, 2020
Publication date	Sep 28, 2023
Grant date	—

Abstract

A method for producing chromium-containing molten steel from a raw material including a chromium-containing raw material includes a first step in which a slag basicity before rough decarburization by oxygen blowing is adjusted to be not less than 1.5 and not more than 3.0, a slag basicity after rough decarburization by oxygen blowing is adjusted to be not less than 2.0 and not more than 3.5, and then tapping is performed while slag containing a chromium oxide generated by the oxygen blowing is made to remain in the furnace, and a second step in which the slag containing a chromium oxide made to remain is reduced by using a carbon source or a metal source newly added into the same furnace so that chromium is recovered into molten steel. The slag basicity is determined by dividing a CaO concentration by an SiO 2 concentration on a mass basis in the slag.

First claim

1 . A method for producing chromium-containing molten steel comprising, using a steelmaking refining furnace, melting and heating a raw material containing a chromium-containing raw material and performing rough decarburization by oxygen blowing,
wherein the method has: a first step of adjusting slag basicity before the rough decarburization by oxygen blowing in a range of not less than 1.5 and not more than 3.0 and the slag basicity after the rough decarburization by oxygen blowing in a range of not less than 2.0 and not more than 3.5 and then performing tapping while keeping the slag containing chromium oxide generated by the oxygen blowing remaining in the furnace; and a second step of reducing the remaining slag containing chromium oxide by a carbon source or a metal source newly added into the same furnace to recover chromium into molten steel, wherein the slag basicity is determined by dividing a CaO concentration by an SiO 2 concentration on a mass basis in the slag.

2 . The method for producing chromium-containing molten steel according to claim 1 , wherein
a CaO-containing raw material is added and melted during the oxygen blowing in the first step.

3 . The method for producing chromium-containing molten steel according to claim 1 , wherein
a slag basicity (C/S)pre before the rough decarburization by the oxygen blowing and a slag basicity (C/S)post after the rough decarburization by the oxygen blowing in the first step satisfy a formula (1) below.
( C/S )post−( C/S )pre≥−0.2  (1)

4 . The method for producing chromium-containing molten steel according to claim 1 , wherein
in the first step, after the oxygen blowing, a concentration of the oxide of chromium in the slag is set to be in a range of not less than 5 mass % and not more than 50 mass % by using one or two types selected from an Si-containing raw material and an Al-containing raw material.

5 . The method for producing chromium-containing molten steel according to claim 2 , wherein
a slag basicity (C/S)pre before the rough decarburization by the oxygen blowing and a slag basicity (C/S)post after the rough decarburization by the oxygen blowing in the first step satisfy a formula (1) below.
( C/S )post−( C/S )pre≥−0.2  (1)

6 . The method for producing chromium-containing molten steel according to claim 2 , wherein
in the first step, after the oxygen blowing, a concentration of the oxide of chromium in the slag is set to be in a range of not less than 5 mass % and not more than 50 mass % by using one or two types selected from an Si-containing raw material and an Al-containing raw material.

7 . The method for producing chromium-containing molten steel according to claim 3 , wherein
in the first step, after the oxygen blowing, a concentration of the oxide of chromium in the slag is set to be in a range of not less than 5 mass % and not more than 50 mass % by using one or two types selected from an Si-containing raw material and an Al-containing raw material.

8 . The method for producing chromium-containing molten steel according to claim 5 , wherein
in the first step, after the oxygen blowing, a concentration of the oxide of chromium in the slag is set to be in a range of not less than 5 mass % and not more than 50 mass % by using one or two types selected from an Si-containing raw material and an Al-containing raw material.

Assignees

• Jfe Steel Corp

Inventors

• Oda Nobuhiko
• Ogasawara Futoshi
• KAKIGI Kentaro
• Fukuyama Takayoshi

Classifications

• C21C7/0025 Primary

  Adding carbon material · CPC title

• C21C5/28

  Manufacture of steel in the converter {(C21C5/005 takes precedence)} · CPC title

• C21C7/068

  Decarburising · CPC title

• C21C5/005 Primary

  Manufacture of stainless steel · CPC title

• C21C5/30 Primary

  Regulating or controlling the blowing · CPC title