Negative electrode current collector for solid-state battery and negative electrode for solid-state battery including the same

Patent metadata

Field	Value
Publication number	US-2023268517-A1
Application number	US-202118024264-A
Country	US
Kind code	A1
Filing date	Sep 14, 2021
Priority date	Sep 14, 2020
Publication date	Aug 24, 2023
Grant date	—

Abstract

A negative electrode current collector and a negative electrode for a solid-state battery including the same are provided. The negative electrode current collector comprises a metal foil which is electroconductive, and a coating layer formed on a surface of the metal foil and comprising metal-carbon composite particles. The metal-carbon composite particles comprise metal particles and carbon particles and apply the metal particles evenly on the surface of the metal foil, and are capable of inducing even lithium electrodeposition between the coating layer and the metal foil, thereby forming a uniform lithium metal plating film on the negative electrode current collector.

First claim

What is claimed is:

1 . A negative electrode current collector for a solid-state battery, the negative electrode current collector comprising:
a metal foil which is electroconductive-; and a coating layer formed on a surface of the metal foil and comprising metal-carbon composite particles, wherein the metal-carbon composite particles comprise metal particles and carbon particles and one or more of the metal particles and one or more of the carbon particles are attached to each other, the composite particles have a particle diameter of 20 μm or less, and a content of metal in the composite particles is 50 parts by weight or less based on 100 parts by weight of carbon.

2 . The negative electrode current collector according to claim 1 , wherein the metal particle comprises one or more selected from the group consisting of Ni, Cu, Ag, Au, Pt, Al, Zn and Bi.

3 . The negative electrode current collector according to claim 1 , wherein the carbon particle comprises one or more selected from the group consisting of natural graphite, artificial graphite, hard carbon, soft carbon, carbon black, acetylene black, ketjen black, channel black, furnace black, lamp black, thermal black, carbon nanotubes, fullerene, carbon fibers and fluorocarbon.

4 . A negative electrode for a solid-state battery which comprises the negative electrode current collector as defined in claim 1 ,
wherein the negative electrode does not comprise negative electrode active material, and wherein lithium is electrodeposited to and detached from the surface of the metal foil during operation of a battery.

5 . The negative electrode according to claim 4 , wherein the lithium is electrodeposited between the metal foil and the coating layer.

6 . The negative electrode current collector according to claim 1 , wherein the metal particle and the carbon particle are attached to each other chemically, physically or both.

7 . A solid-state battery comprising the negative electrode as defined in claim 5 .

8 . A method for preparing composite particles, the method comprising:
preparing a reaction solution containing a metal salt and a carbonaceous material, and carrying out a reaction to grow metal particles a surface of the carbonaceous material in the reaction solution.

9 . The method according to claim 8 , wherein a solid content including the metal salt and the carbonaceous material in the reaction solution is 30 wt % or less.

10 . The method according to claim 8 , wherein the metal salt is one or more selected from the group consisting of metal chloride, metal iodide, metal cyanide, metal bromide, metal sulfide, metal hydroxide, metal phosphite and metal chloride hydrate.

11 . The method according to claim 8 , wherein the metal salt is chloride of one or more selected from the group consisting of Ni, Cu, Ag, Au, Pt, Al, Zn and Bi.

12 . The negative electrode current collector according to claim 1 , wherein the metal-carbon composite particles have a particle diameter of 20 μm or less.

13 . The negative electrode current collector according to claim 1 , wherein the coating layer has a porous structure having pores derived from the interstitial volumes among the composite particles.

14 . The solid-state battery according to claim 7 , wherein a solid electrolyte membrane is interposed between a positive electrode and a negative electrode.

15 . The solid-state battery according to claim 14 , wherein the solid electrolyte membrane comprises at least one selected from a sulfide-based solid electrolyte material, an oxide-based solid electrolyte material and a polymeric solid electrolyte material.

Assignees

• Lg Energy Solution Ltd

Inventors

• Cho Sung-Ju
• Lee Jung-Pil

Classifications

• Y02E60/10

  Energy storage using batteries · CPC title

• H01M2004/021

  Physical characteristics, e.g. porosity, surface area · CPC title

• H01M10/0562

  Solid materials · CPC title

• H01M4/134

  Electrodes based on metals, Si or alloys · CPC title

• C23C28/00

  Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D · CPC title