Method for preparing metal oxide or metal hydroxide nano thin-film material by molten salt method

Patent metadata

Field	Value
Publication number	US-2023121139-A1
Application number	US-201917618879-A
Country	US
Kind code	A1
Filing date	Sep 30, 2019
Priority date	Apr 11, 2019
Publication date	Apr 20, 2023
Grant date	—

Abstract

Provided is a method for preparing a metal oxide or a metal hydroxide nano thin-film material by a molten salt method, which mainly comprises the following steps: heating a low-melting-point salt to a molten state, adding a substrate into the molten salt before or after melting for reaction; adding a metal source and continuing the reaction for a period of time; removing the substrate, cooling the substrate to a room temperature, cleaning and drying the substrate to obtain the metal oxide or metal hydroxide nano thin-film material; wherein, the mass ratio of the low-melting-point salt to the metal source is 100-1.5:1. The metal oxide and metal hydroxide nano-film materials with various nano-morphologies prepared by the method of the present application have morphologies that can be regulated and controlled by the types and proportions of the low-melting-point salts and metal sources.

First claim

1 . A method for preparing a metal oxide or a metal hydroxide nano thin-film material by a molten salt method, comprising the following steps: heating a low-melting-point salt to a molten state, adding a substrate into the molten salt before or after melting and reaction will occur for 5 s to 1 h; then adding a metal source, continuing to raise a temperature or keeping the temperature unchanged, and reaction will occur for a predetermined period of time; removing the substrate, cooling the substrate to a room temperature, cleaning and drying the substrate to obtain metal oxide or metal hydroxide nano thin-film material; wherein, a mass ratio of the low-melting-point salt to the metal source is 100-1.5:1;
the substrate is FTO conductive glass, metal titanium foil, 304 stainless steel metal, metal copper foil, nickel foam, carbon felt cloth, carbon paper or carbon fiber cloth; the low-melting-point salt refers to a salt with a melting point lower than 400° C., comprising nitrate, chloride, sulfate, phosphate, acetate or carbonate; the metal source comprises nitrate, sulfate, chloride, phosphate, titanate, tungstate, acetate, molybdate or carbonate of any one of metal elements of copper, manganese, nickel, cobalt, zinc, iron, titanium, aluminum, vanadium, chromium, molybdenum, ruthenium, tungsten, zirconium, lanthanum and cerium; a range of raising the temperature is between a melting point and a decomposition temperature or a boiling point of the low-melting-point salt, and the predetermined period of time is 5 s to 5 h.

2 . (canceled)

3 . (canceled)

4 . (canceled)

5 . (canceled)

6 . (canceled)

7 . (canceled)

8 . (canceled)

Assignees

• Univ Zhejiang

Inventors

• Gu Yijie
• Wu Jinming

Classifications

• C23C8/80

  After-treatment · CPC title

• C23C8/42

  only one element being applied · CPC title

• C01B13/18 Primary

  by thermal decomposition of compounds, e.g. of salts or hydroxides · CPC title

• Y02E60/13

  Energy storage using capacitors · CPC title

• C01G3/02

  Oxides; Hydroxides · CPC title