Gas diffusion electrode base material and production method therefor, and solid polymer fuel cell

Patent metadata

Field	Value
Publication number	US-2022029170-A1
Application number	US-201917276273-A
Country	US
Kind code	A1
Filing date	Sep 26, 2019
Priority date	Sep 28, 2018
Publication date	Jan 27, 2022
Grant date	—

Abstract

A fuel cell with high productivity, high power generation performance and high durability is described, along with a gas diffusion electrode base material having a microporous layer on one side of an electrically conductive porous base material, where the electrically conductive porous base material contains carbon fiber and resin carbide and has a density of 0.25 to 0.39 g/cm3 and a pore mode diameter in a range of 30 to 50 μm. The microporous layer contains a carbonaceous powder and a fluororesin and has a surface roughness of 2.0 to 6.0 μm, a porosity of 50 to 95%, and a pore mode diameter of 0.050 to 0.100 μm.

First claim

1 . A gas diffusion electrode base material having a microporous layer on one side of an electrically conductive porous base material,
the electrically conductive porous base material containing carbon fiber and resin carbide and having a density of 0.25 to 0.39 g/cm 3 and a pore mode diameter in a range of 30 to 50 μm, and the microporous layer containing a carbonaceous powder and a fluororesin and having a surface roughness of 2.0 to 6.0 μm, a porosity of 50 to 95%, and a pore mode diameter of 0.050 to 0.100 μm.

2 . The gas diffusion electrode base material according to claim 1 , wherein a silicon/carbon element ratio on a surface of the electrically conductive porous base material opposite to a surface of the electrically conductive porous base material having the microporous layer is 0.020 or more.

3 . The gas diffusion electrode base material according to claim 1 , wherein an oxygen/carbon element ratio on the surface of the electrically conductive porous base material opposite to the surface of the electrically conductive porous base material having the microporous layer is 0.005 or more.

4 . The gas diffusion electrode base material according to claim 1 , wherein a cumulative pore volume per 1 cm 2 in the pore mode diameter of 30 to 50 μm in the electrically conductive porous base material is 1.5 to 4.0 μL/cm 2 .

5 . The gas diffusion electrode base material according to claim 1 , wherein the number of holes having a diameter of 150 μm or more on a surface of the microporous layer is 0.001 to 0.050 holes/cm 2 .

6 . The gas diffusion electrode base material according to claim 1 , wherein a coverage (strike-through rate) of a carbonaceous powder on an electrically conductive porous base material surface opposite to a surface of the gas diffusion electrode base material having the microporous layer is less than 10%.

7 . The gas diffusion electrode base material according to claim 1 , which has an in-plane gas diffusibility of 40 to 80 cc/min.

8 . The gas diffusion electrode base material according to claim 1 , wherein a DBP absorption value of the carbonaceous powder contained in the microporous layer is 156 to 220 mL/100 g.

9 . The gas diffusion electrode base material according to claim 1 , wherein a primary particle size of the carbonaceous powder contained in the microporous layer is 20 to 39 nm.

10 . The gas diffusion electrode base material according to claim 1 , wherein the microporous layer further contains a fibrous carbide having a fiber diameter of 5 nm or more and 10 μm or less and an aspect ratio of 10 or more.

11 . The gas diffusion electrode base material according to claim 10 , wherein an oxygen/carbon element ratio of the fibrous carbide is 0.020 or more.

12 . A production method for the gas diffusion electrode base material according to claim 1 , comprising simultaneously adding a fluororesin and a water repellent processing additive different from the fluororesin to an electrically conductive porous base material and then applying an MPL ink in which a carbonaceous powder, fluororesin particles, and a surfactant are dispersed in water.

13 . The production method for a gas diffusion electrode base material according to claim 12 , wherein a water repellent processing additive having a mass retention rate of 50% or less when heat-treated at a temperature of 300° C. or higher is used.

14 . The production method for a gas diffusion electrode base material according to claim 12 , wherein a silicone-based water repellent processing additive, a paraffin-based water repellent processing additive, or a polymer compound (hydrocarbon-based water repellent processing additive) having a side chain consisting of a perfluoroalkyl group or a hydrocarbon group in a main chain of an acrylate polymer is used as a water repellent processing additive.

15 . A solid polymer fuel cell comprising:
a polymer electrolyte membrane; a catalyst layer formed on each side of the polymer electrolyte membrane; the gas diffusion electrode base material according to claims 1 to 11 formed outside the catalyst layer; and two separators sandwiching the polymer electrolyte membrane, the catalyst layer, and the gas diffusion electrode base material.

Assignees

• Toray Industries

Inventors

• Utsunomiya Masamichi
• Watanabe Fumitaka

Classifications

• Y02P70/50

  Manufacturing or production processes characterised by the final manufactured product · CPC title

• H01M4/861 Primary

  with a gradient in the porosity · CPC title

• H01M8/1018

  Polymeric electrolyte materials · CPC title

• H01M2008/1095

  Fuel cells with polymeric electrolytes · CPC title

• H01M4/8817

  Treatment of supports before application of the catalytic active composition (coated porous composites H01M8/0245) · CPC title