Abstract

A coating method for a clad steel in which stainless sheets are combined on adjacent surfaces of an aluminum sheet may include preparing the clad steel, preparing a coating solution in which an epoxy resin and titanium dioxide (TiO 2 ) powder are combined in an acrylic resin, etching the clad steel to improve adhesion property between the coating solution and the clad steel, heating the clad steel, and performing electrodeposition by immersing the clad steel in the coating solution.

First claim

What is claimed is:

1 . A coating method for a clad steel in which stainless sheets are combined on adjacent surfaces of an aluminum sheet, the method comprising:
preparing the clad steel; preparing a coating solution in which an epoxy resin and titanium dioxide (TiO 2 ) powder are combined in an acrylic resin; etching the clad steel to improve adhesion property between the coating solution and the clad steel; heating the clad steel; and performing electrodeposition by immersing the clad steel in the coating solution.

2 . The coating method of claim 1 , wherein in the preparing of the coating solution, the coating solution is prepared including in percent by weight (wt %), acrylic resin of 40 to 50%, TiO 2 of 10 to 15%, epoxy resin of 10 to 15%, melamine curing agent of 10 to 20%, aromatic solvent of 5 to 10%, and cyclohexanone of 10 to 15%.

3 . The coating method of claim 2 , further comprising degreasing the clad steel between the preparing of the clad steel and the etching of the clad steel.

4 . The coating method of claim 3 , wherein in the degreasing of the clad steel, the clad steel is cathodically degreased in 25 to 35 g/l of trisodium phosphate (Na 3 PO 4 ) aqueous solution for a time period of 30 seconds to 3 minutes under conditions in which a current density is 1 to 4 A/dm and a voltage is 4 to 6V.

5 . The coating method of claim 2 , wherein in the etching of the clad steel, the clad steel is immersed in an aqueous solution including 100 to 200 g/l of ammonium hydroxide (NH 4 OH) and 50 to 200 g/l of potassium hydrogen phthalate (KHP) for 3 to 5 minutes to be etched, and a temperature at a time of the etching is 20 to 30° C.

6 . The coating method of claim 2 , wherein in the heating of the clad steel, the clad steel is heated at 100 to 200° C. for a time period of 2 to 3 minutes.

7 . The coating method of claim 2 , wherein in the performing of the electrodeposition, the clad steel is immersed in the coating solution, and then, a voltage of 10 to 20V is applied at 40 to 50° C. for a time period of 1 to 5 minutes to electrodeposit the coating solution on the clad steel.

8 . The coating method of claim 2 , further comprising drying at 80 to 100° C. for 10 to 20 minutes after the performing of the electrodeposition.

9 . A coating solution for coating a clad steel comprising in percent by weight (wt %), acrylic resin of 40 to 50%, TiO 2 of 10 to 15%, epoxy resin of 10 to 15%, melamine curing agent of 10 to 20%, aromatic solvent of 5 to 10%, and cyclohexanone of 10 to 15%.

Assignees

• Hyundai Motor Co Ltd
• Kia Motors Corp

Inventors

• Yoo Chang Yeol

Classifications

• C09D5/084 Primary

  Inorganic compounds · CPC title

• C09D133/00

  Coating compositions based on homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by only one carboxyl radical, or of salts, anhydrides, esters, amides, imides, or nitriles thereof; Coating compositions based on derivatives of such polymers · CPC title

• C23F1/28

  for etching iron group metals · CPC title

• C08K2003/2241

  Titanium dioxide · CPC title

• C23F1/40

  for etching other metallic material · CPC title