Non-phosphorus chemical conversion treatment agent and treatment liquid for plastic working, chemical conversion film, and metal material with chemical conversion film

Patent metadata

Field	Value
Publication number	US-2016237285-A1
Application number	US-201615135025-A
Country	US
Kind code	A1
Filing date	Apr 21, 2016
Priority date	Oct 22, 2013
Publication date	Aug 18, 2016
Grant date	—

Abstract

A non-phosphorus chemical conversion treatment agent and treatment liquid for plastic working are provided, with reduced environmental impact, which are able to form films that are excellent in lubricity and corrosion resistance after plastic working by achieving large film thicknesses even in a system containing a salt of molybdic acid as its main constituent. An exemplary non-phosphorus chemical conversion treatment agent for plastic working is an agent containing a molybdic acid component (A), an acid component (B), and an aqueous medium (C), which is characterized in that the (B) comprises at least an organic acid component (B1) having at least one group selected from a carboxyl group and a phenolic hydroxyl group.

First claim

What is claimed is:

1 . A non-phosphorus chemical conversion treatment agent or treatment liquid for plastic working, comprising:
(A) a molybdic acid component; (B) an acid component different from (A); and (C) an aqueous medium;
wherein (B) comprises at least one organic acid component (B1) having at least one group selected from a carboxyl group and a phenolic hydroxyl group.

2 . The non-phosphorus chemical conversion treatment agent or treatment liquid for plastic working according to claim 1 , wherein (B1) has a pKa value of 5 or less.

3 . The non-phosphorus chemical conversion treatment agent or treatment liquid for plastic working according to claim 1 , wherein (B1) comprises one or more selected from the group consisting of a carboxylic acid, an aminocarboxylic acid, a hydroxy acid, catechols, and ascorbic acid.

4 . The non-phosphorus chemical conversion treatment agent or treatment liquid for plastic working according to claim 1 , wherein (B1) comprises one or more selected from the group consisting of EDTA, NTA, HEDTA, DTPA, EDDA, GEDTA, CyDTA, HIDA, TTHA, malic acid, tartaric acid, citric acid, oxalic acid, azelaic acid, aspartic acid, maleic acid, malonic acid, lactic acid, ascorbic acid, catechol, tiron, and salts thereof.

5 . The non-phosphorus chemical conversion treatment agent or treatment liquid for plastic working according to claim 1 , wherein (A) and (B1) are present in amounts such that a molar ratio of the molybdic acid amount to a total amount of the carboxyl group and the phenolic hydroxyl group of (B1), calculated as:
(molybdic acid)/(total of carboxyl group and phenolic hydroxyl group) is in a range of from 0.01 to 800.

6 . The non-phosphorus chemical conversion treatment agent or treatment liquid for plastic working according to claim 5 , further containing a metal component (D) comprising at least one element selected from aluminum, zinc, calcium, iron, manganese, magnesium and cobalt.

7 . The non-phosphorus chemical conversion treatment agent or treatment liquid for plastic working according to claim 6 , wherein a molar ratio of (A) to (D) is in a range of from 0.3 to 200.

8 . A chemical conversion film obtained by treating a metal material with the non-phosphorus chemical conversion treatment liquid for plastic working according to claim 1 .

9 . A metal material comprising the chemical conversion film according to claim 8 .

10 . The metal material according to claim 9 , further comprising a lubricant layer on the chemical conversion film.

11 . A method for producing a metal material having a chemical conversion film, the method comprising a chemical conversion treatment step of treating a metal material with the non-phosphorus chemical conversion treatment liquid for plastic working according to claim 1 , thereby forming a chemical conversion film on the metal material.

12 . The method for producing a metal material with a chemical conversion film according to claim 11 , the method comprising a step of applying a lubricant onto the chemical conversion film after the chemical conversion treatment step.

Assignees

• Henkel Ag & Co Kgaa

Inventors

• Doda Tatsunori
• Matsuo Hiroyuki

Classifications

• C23C22/40 Primary

  containing molybdates, tungstates or vanadates · CPC title

• C09D5/086 Primary

  Organic or non-macromolecular compounds · CPC title