Fluorine-containing self-lubricating fabric coating material and method for preparing the same

Patent metadata

Field	Value
Publication number	US-2016208431-A1
Application number	US-201414910938-A
Country	US
Kind code	A1
Filing date	Aug 13, 2014
Priority date	Aug 13, 2013
Publication date	Jul 21, 2016
Grant date	—

Abstract

The present invention provides a fluorine-containing self-lubricating fabric coating material and method for preparing the same. The coating material consists of 30 to 70 pbw of fluorine resin, 10 to 40 pbw of a curing agent, 5 to 25 pbw of a reactive diluents, 0.5 to 5 pbw of a silane coupling agent and 0.5 to 3 pbw of a silicon surfactant. It is of high fluorine content and high stability. Besides, the coating material system with characteristics of self-lubricating and weather resistance is solvent-free, environmentally friendly, and has wide applications.

First claim

1 . A fluorine-containing self-lubricating fabric coating material consists of:
(a) 30 to 70 pbw of fluorine resin, (b) 10 to 40 pbw of a curing agent, (c) 5 to 25 pbw of a reactive diluents, (d) 0.5 to 5 pbw of a silane coupling agent and (e) 0.5 to 3 pbw of a silicon surfactant; wherein the structure formula of the fluorine resin is

with both R 1 and R 2 refer to —(CF 2 ) n — and n ranging from 1 to 18, or refer to the following aromatic groups with both R 3 and R 4 referring to —CF 3 or —CF 2 CF 3 .

2 . The fluorine-containing self-lubricating fabric coating material according to claim 1 , comprises the following preparation steps:
adding 30 to 40 pbw of fluorine monomer and 20 to 30 pbw of epoxy chloropropane into a reaction flask, stirring and heating up to 60˜70 □; mixing 5 to 10 pbw of NaOH and 15 to 20 pbw of water to prepare lye solution and dropping the lye solution into the reaction flask within 1 to 1.5 hours at the temperature of 60 to 70 □; refluxing the reactant at 70 □ to 1.5 hours until the system presents a whitish yellow color; adding deionized water together with toluene, stirring until homogenous, standing and layering the system repeatedly to remove water, distilling separated organic layer under reduced pressure to remove toluene and unreacted epoxy chloropropane so that a light yellow viscous resin is obtained.

3 . The fluorine-containing self-lubricating fabric coating material according to claim 1 , has the curing agent which is acid anhydrides used in conjunction with fluorine epoxy resin including acid anhydrides, o-phthalic anhydride, pyromellitic dianhydride, methylcyclohexene tetracarboxylic dianhydride, and cis-butenedioic anhydride.

4 . The fluorine-containing self-lubricating fabric coating material according to claim 3 , has the reactive diluents which is at least one component selected from the group consisting of 1,6-hexanediol diacrylate, 2-hydroxyethyl methacrylate, cresyl glycidyl ether, castor oil glycidyl ether, and ethylene glycol diglycidyl ether.

5 . The fluorine-containing self-lubricating fabric coating material according to claim 4 , includes the silane coupling agent with the general formula being Y(CH 2 ) n SiX 3 , wherein n=0˜3, and X refers to at least one group selected from the group consisting of chlorine, methoxyl, oxethyl, methoxyethoxy and acetoxyl, and Y refers to amine or/and epoxy group.

6 . The fluorine-containing self-lubricating fabric coating material according to claim 5 , includes the silicon surfactant which is at least one kind of silicon surfactant selected from the group consisting of silane-based, oxosilane-based, anionic, cationic and nonionic.

7 . A method for preparing the fluorine-containing self-lubricating fabric coating material according to claim 1 comprises the steps of:
dissolving a silane coupling agent and a curing agent into a reactive diluents successively according to proportioning of the coating, stirring for 0.5 to 1 hour to obtain homogenous solution;
adding fluorine epoxy resin into the solution under stirring and stirring the mixture for 1 to 2 hours to get the coating material; painting the coating material on clean fabric, drying at 40 to 60° C. by air-circulating oven for 1 to 2 hours and curing at 150 to 170° C. under 0.2 to 0.3 Mpa for 2 to 3 hours when used.

8 . The fluorine-containing self-lubricating fabric coating material according to claim 2 , has the curing agent which is acid anhydrides used in conjunction with fluorine epoxy resin including acid anhydrides, o-phthalic anhydride, pyromellitic dianhydride, methylcyclohexene tetracarboxylic dianhydride, and cis-butenedioic anhydride.

9 . The fluorine-containing self-lubricating fabric coating material according to claim 8 , has the reactive diluents which is at least one component selected from the group consisting of 1,6-hexanediol diacrylate, 2-hydroxyethyl methacrylate, cresyl glycidyl ether, castor oil glycidyl ether, and ethylene glycol diglycidyl ether.

10 . The fluorine-containing self-lubricating fabric coating material according to claim 9 , includes the silane coupling agent with the general formula being Y(CH 2 ) n SiX 3 , wherein n=0˜3, and X refers to at least one group selected from the group consisting of chlorine, methoxyl, oxethyl, methoxyethoxy and acetoxyl, and Y refers to amine or/and epoxy group.

11 . The fluorine-containing self-lubricating fabric coating material according to claim 10 , includes the silicon surfactant which is at least one kind of silicon surfactant selected from the group consisting of silane-based, oxosilane-based, anionic, cationic and nonionic.

12 . A method for preparing the fluorine-containing self-lubricating fabric coating material according to claim 2 comprises the steps of:
dissolving a silane coupling agent and a curing agent into a reactive diluents successively according to proportioning of the coating, stirring for 0.5 to 1 hour to obtain homogenous solution;
adding fluorine epoxy resin into the solution under stirring and stirring the mixture for 1 to 2 hours to get the coating material; painting the coating material on clean fabric, drying at 40 to 60° C. by air-circulating oven for 1 to 2 hours and curing at 150 to 170° C. under 0.2 to 0.3 Mpa for 2 to 3 hours when used.

13 . A method for preparing the fluorine-containing self-lubricating fabric coating material according to claim 3 comprises the steps of:
dissolving a silane coupling agent and a curing agent into a reactive diluents successively according to proportioning of the coating, stirring for 0.5 to 1 hour to obtain homogenous solution;
adding fluorine epoxy resin into the solution under stirring and stirring the mixture for 1 to 2 hours to get the coating material; painting the coating material on clean fabric, drying at 40 to 60° C. by air-circulating oven for 1 to 2 hours and curing at 150 to 170° C. under 0.2 to 0.3 Mpa for 2 to 3 hours when used.

14 . A method for preparing the fluorine-containing self-lubricating fabric coating material according to claim 8 comprises the steps of:
dissolving a silane coupling agent and a curing agent into a reactive diluents successively according to proportioning of the coating, stirring for 0.5 to 1 hour to obtain homogenous solution;
adding fluorine epoxy resin into the solution under stirring and stirring the mixture for 1 to 2 hours to get the coating material; painting the coating material on clean fabric, drying at 40 to 60° C. by air-circulating oven for 1 to 2 hours and curing at 150 to 170° C. under 0.2 to 0.3 Mpa for 2 to 3 hours when used.

15 . A method for preparing the fluorine-containing self-lubricating fabric coating material according to claim 4 comprises the steps of:
dissolving a silane coupling agent and a curing agent into a reactive diluents successively according to proportioning of the coating, stirring for 0.5 to 1 hour to obtain homogenous solution;
adding fluorine epoxy resin into the solution under stirring and stirring the mixture for 1 to 2 hours to get the coating material; painting the coating material on clean fabric, drying at 40 to 60° C. by air-circulating oven for 1 to 2 hours and curing at 150 to 170° C. under 0.2 to 0.3 Mpa for 2 to 3 hours when used.

16 . A method for preparing the fluorine-containing self-lubricating fabric coating material according to claim 9 comprises the steps of:
dissolving a sila

Assignees

• Univ Xiamen

Inventors

• Dai Lizong
• Mao Jie
• Chen Lingnan
• Xu Yiting
• Zeng Birong
• Qiu Wuhui
• Song Cunfeng
• Luo wei ang
• Kang Qilong

Classifications

• C09D163/00

  Coating compositions based on epoxy resins; Coating compositions based on derivatives of epoxy resins · CPC title

• D06M15/55 Primary

  Epoxy resins · CPC title

• C23C14/58

  After-treatment · CPC title

• D06M2200/40

  Reduced friction resistance, lubricant properties; Sizing compositions · CPC title

• D06M13/192

  Polycarboxylic acids; Anhydrides, halides or salts thereof {(D06M13/1845 takes precedence)} · CPC title