Metal composite hydroxide and method for producing same, positive electrode active material for non-aqueous electrolyte secondary battery and method for producing same, and non-aqueous electrolyte secondary battery

Patent metadata

Field	Value
Publication number	US-12451483-B2
Application number	US-201916975353-A
Country	US
Kind code	B2
Filing date	Feb 20, 2019
Priority date	Feb 22, 2018
Publication date	Oct 21, 2025
Grant date	Oct 21, 2025

Abstract

A metal composite hydroxide represented by a general formula (1): Ni1−x−yCoxMnyMz(OH)2+α (where 0.02≤x≤0.3, 0.02≤y≤0.3, 0≤z≤0.05, and −0.5≤α≤0.5 are satisfied and M is at least one element selected from the group consisting of Mg, Ca, Al, Si, Fe, Cr, V, Mo, W, Nb, Ti, and Zr), in which the metal composite hydroxide contains a first particle having a core portion inside the particle and a shell portion formed around the core portion and [(D90−D10)/MV] is less than 0.80.

First claim

The invention claimed is:

1. A metal composite hydroxide represented by a general formula (1): Ni 1−x−y Co x Mn y M z (OH) 2+α (where 0.02≤x≤0.3, 0.02≤y≤0.3, 0≤z≤0.05, and −0.5≤α≤0.5 are satisfied and M is at least one element selected from the group consisting of Mg, Ca, Al, Si, Fe, Cr, V, Mo, W, Nb, Ti, and Zr), wherein
[(D90−D10)/MV] that indicates a dispersion of a particle size in particle size distribution calculated by D90, D10 and a volume average particle diameter (MV) by a laser diffraction scattering method is less than 0.80,
the metal composite hydroxide comprises a first particle having a core portion inside the particle and a shell portion formed around the core portion,
a composition of the core portion is represented by a general formula (2): Ni 1-x1-y1 Co x1 Mn y1 M z1 (OH) 2+α1 (where 0.4<(1−x 1 −y 1 )≤0.96, 0≤z 1 ≤0.05, and −0.5≤α 1 ≤0.5 are satisfied),
a composition of the shell portion is represented by a general formula (3): Ni 1-x2-y2 Co x2 Mn y2 M z2 (OH) 2+α2 (where (1−x 1 −y 1 )/(1−x 2 −y 2 )>1.0, 0<(1−x 2 −y 2 )<0.6, 0≤z 2 ≤0.05, and −0.5≤α 2 ≤0.5 are satisfied),
the shell portion has a thickness to be 10% or more and 40% or less of a radius of the first particle in a direction from a surface to a center of the particle in the first particle having a particle size in a range to be ±10% of the volume average particle diameter (MV) of the metal composite hydroxide,
the core portion has a radius to be 60% or more and 90% or less of the radius of the first particle in a direction from the center thereof in the first particle having the particle size in the range to be ±10% of the volume average particle diameter (MV) of the metal composite hydroxide, and
the nickel is distributed uniformly in the entire core portion such that the nickel is detected uniformly therein by energy dispersive X-ray analysis (EDX) on a cross-section of the metal composite hydroxide under a scanning transmission electron microscope (STEM).

2. The metal composite hydroxide according to claim 1 , which has a volume average particle diameter (MV) of 5 μm or more and 20 μm or less.

3. The metal composite hydroxide according to claim 1 , wherein the element M is uniformly present inside the first particle and/or on a surface of the first particle.

4. The metal composite hydroxide according to claim 1 , wherein the shell portion has a composition that is uniform throughout the shell portion.

5. The metal composite hydroxide according to claim 1 , wherein
the thickness of the shell portion is 10% or more and 20% or less of the radius of the first particle, and
the radius of the core portion is 80% or more and 90% or less of the radius of the first particle.

6. A method for producing a metal composite hydroxide that contains a first particle having a core portion inside the particle and a shell portion formed around the core portion and is represented by a general formula (1): Ni 1−x−y Co x Mn y M z (OH) 2+α (where 0.02≤x≤0.3, 0.02≤y≤0.3, 0≤z≤0.05, and −0.5≤α≤0.5 are satisfied and M is at least one element selected from the group consisting of Mg, Ca, Al, Si, Fe, Cr, V, Mo, W, Nb, Ti, and Zr), the method comprising:
a first crystallization process of supplying a first raw material aqueous solution containing nickel and at least one of cobalt, manganese, or the element M, adjusting a pH value of a reaction aqueous solution to 11.5 or more and 13.5 or less at a liquid temperature of 25° C., while a fluctuation range of a pH value during a crystallization reaction is controlled to be within ±0.2, and performing crystallization to form the core portion represented by a general formula (2): Ni 1-x1-y1 Co x1 Mn y1 M z1 (OH) 2+α1 (where 0.4<(1−x 1 −y 1 )≤0.96, 0≤z 1 ≤0.05, and −0.5≤α 1 ≤0.5 are satisfied); and
a second crystallization process of supplying a second raw material aqueous solution having a lower nickel content than the first raw material aqueous solution to a reaction aqueous solution that contains the core portion and has a pH value adjusted to be 10.5 or more and 12.0 or less at a liquid temperature of 25° C. and lower than the pH value in the first crystallization process and forming the shell portion represented by a general formula (3): Ni 1-x2-y2 Co x2 Mn y2 M z2 (OH) 2+α2 (where (1−x 1 −y 1 )/(1−x 2 −y 2 )>1.0, 0<(1−x 2 −y 2 )<0.6, 0≤z 2 ≤0.05, and −0.5≤α 2 ≤0.5 are satisfied) around the core portion, wherein
the first crystallization process and the second crystallization process are performed by a batch crystallization method, and
the first crystallization process and the second crystallization process are performed by adjusting amounts of the first raw material aqueous solution and second raw material aqueous solution supplied so that the shell portion has a thickness to be 10% or more and 40% or less of a radius of the first particle in a direction from a surface to a center of the first particle in the first particle having a particle size in a range to be ±10% of the volume average particle diameter (MV) and so that the core portion has a radius to be 60% or more and 90% or less of the radius of the first particle in a direction from the center thereof in the first particle having the particle size in the range to be ±10% of the volume average particle diameter (MV) of the metal composite hydroxide.

7. The method according to claim 6 , wherein the shell portion has a composition that is uniform throughout the shell portion.

8. The method according to claim 6 , wherein
the pH value of the reaction aqueous solution prepared and utilized in the first crystallization process is adjusted to 12.0 or more and 13.0 or less at the liquid temperature of 25° C., and
the pH value of the reaction aqueous solution prepared and utilized in the second crystallization process is adjusted to 11.5 or more and 12.0 or less at the liquid temperature of 25° C.

9. The method according to claim 6 , wherein
the thickness of the shell portion is 10% or more and 20% or less of the radius of the first particle, and
the radius of the core portion is 80% or more and 90% or less of the radius of the first particle.

10. A positive electrode active material for non-aqueous electrolyte secondary battery comprising a lithium-metal composite oxide represented by a general formula (4): Li 1+a Ni 1−x−y Co x Mn y M z O 2+β (where −0.05≤a≤0.50, 0.02≤x≤0.3, 0.02≤y≤0.3, 0≤z≤0.05, −0.5≤β≤0.5, and M is at least one element selected from the group consisting of Mg, Ca, Al, Si, Fe, Cr, V, Mo, W, Nb, Ti, and Zr), wherein
[(D90−D10)/MV] that indicates a dispersion of a particle size in particle size distribution calculated by D90, D10 and the volume average particle diameter (MV) by a laser diffraction scattering method is less than 0.80,
the lithium-metal composite oxide contains a second particle having a core portion inside the particle and a shell portion formed around the core portion,
a composition of the core portion in the second particle is represented by a general formula (5): Li 1+a Ni 1-x1-y1 Co x1 Mn y1 M z1 O 2+β1 (where −0.05≤α≤0.50, 0.4<(1−x 1 −y 1 )≤0.96, 0≤z 1 ≤0.05, and −0.5≤β 1 ≤0.5 are satisfied),
a composition of the shell portion in the second particle is represented by a general formula (6): Li 1+a Ni 1-x2-y2 Co x2 Mn y2 M z2 O 2+β2 (where −0.05≤α≤0.50, (1−x 1 −y 1 )/(1−x 2 −y 2 )>1.0, 0<(1-x 2-y2 )<0.5, 0≤z 2 <0.05, −0.5≤β 2 ≤0.5 are satisfied),
the shell portion has a thickness to be 10% or more and 40% or less of a radius of the second particle in a direction from a surface to a center of the second particle in the second particle having a particle size in a range to be ±10% of the volume average particle diameter (MV),
the core portion has a radius to be 60% or more and 90% or less of the radius of the s

Assignees

• Sumitomo Metal Mining Co

Inventors

• Toma Takahiro
• KANEDA Haruki
• Koshika Yuki

Classifications

• H01M2004/028

  Positive electrodes · CPC title

• H01M2004/027

  Negative electrodes · CPC title

• H01M10/0525

  Rocking-chair batteries, i.e. batteries with lithium insertion or intercalation in both electrodes; Lithium-ion batteries · CPC title

• H01M4/505

  of mixed oxides or hydroxides containing manganese for inserting or intercalating light metals, e.g. LiMn2O4 or LiMn2OxFy · CPC title

• H01M4/364

  as mixtures · CPC title