Electrode catalyst, composition for forming gas diffusion electrode, gas diffusion electrode, membrane electrode assembly, and fuel cell stack

Patent metadata

Field	Value
Publication number	US-12374700-B2
Application number	US-202117910153-A
Country	US
Kind code	B2
Filing date	Mar 16, 2021
Priority date	Mar 23, 2020
Publication date	Jul 29, 2025
Grant date	Jul 29, 2025

Abstract

The present invention provides an electrode catalyst which has excellent catalytic activity, and which can contribute to reducing the cost of a polymer electrolyte fuel cell (PEFC). According to the present invention, an electrode catalyst includes a hollow carrier including nanopores having a pore size of 1 to 20 nm, and a plurality of catalyst particles. The catalyst particles are supported both inside and outside the nanopores of the carrier, and comprise (zero-valent) Pt, and when a particle size distribution analysis of the catalyst particles is carried out using a three-dimensional reconstructed image obtained by electron beam tomography measurement employing STEM, the conditions of formula (S1): 100×(N10/N20)≤8.0 are satisfied (in the formula, N10 is the number of noble metal particles not in contact with a pore having a pore size of 1 nm or more, and N20 is the number of catalyst particles supported inside the nanopores of the carrier).

First claim

The invention claimed is:

1. An electrode catalyst which includes a conductive hollow carbon carrier having a Nanopore of a pore size of 1 to 20 nm, and a plurality of catalyst particles supported on the carrier, wherein
the catalyst particle is composed of Pt (0 valent),
the catalyst particle is supported on both of inside of the Nanopore and outside the Nanopore of the carrier, and
when an analysis of a particle size distribution of the catalyst particles is performed by using a three-dimensional reconstructed image obtained by an electron beam tomography measurement using an STEM (scanning transmission electron microscopy), the condition of the following equation (S1) is satisfied:
100×( N 10/ N 20)≤8.0  (S1)

in the above equation (S1),
N10 is the number of non-contact particles (n101+n102), which is the sum of the number of particles (n101) of noble metal particles that are not in contact with pores having a pore diameter of 1 nm or more that can be confirmed by the electron tomography measurement and the number of noble metal particles (n102) that are not in contact with the hollow carbon carrier itself and exist outside the hollow carbon carrier,
N20 is the number of particles of the catalyst particles supported inside the Nanopores of the carrier.

2. The electrode catalyst according to claim 1 , wherein,
when an analysis of a particle size distribution of the catalyst particles is performed by using a three-dimensional reconstructed image obtained by an electron beam tomography measurement using an STEM (scanning transmission electron microscopy), the condition of the following equation (S2) is satisfied:
100×{ N 10/( N 20+ N 30)}≤6.0  (S2)

in the formula (S2),
N10 is synonymous with N10 in the formula (S1),
N20 is synonymous with N20 in the formula (S1),
N30 is the number of particles of the catalyst particles supported on the outside of the Nanopores of the carrier.

3. The electrode catalyst according to claim 1 , wherein,
when an analysis of a particle size distribution of the catalyst particles is performed by using a three-dimensional reconstructed image obtained by an electron beam tomography measurement using an STEM (scanning transmission electron microscopy),
with respect to the catalyst particles supported inside the Nanopore of the carrier,
an average distance from the inlet of the Nanopores to the supported position of the catalyst particles is of 6.0 nm or more.

4. The electrode catalyst according to claim 1 , wherein,
when an analysis of a particle size distribution of the catalyst particles is performed by using a three-dimensional reconstructed image obtained by an electron beam tomography measurement using an STEM (scanning transmission electron microscopy),
the catalyst particles supported inside the Nanopore of the carrier exist within a range that a distance from the inlet of the Nanopore to the supported position of the catalyst particles of 0 to 24 nm.

5. The electrode catalyst according to claim 1 , wherein,
when an analysis of a particle size distribution of the catalyst particles is performed by using a three-dimensional reconstructed image obtained by an electron beam tomography measurement using an STEM (scanning transmission electron microscopy),
a particle size of the catalyst particles supported inside the Nanopore of the carrier is more than 0 nm and 4 nm or less.

6. The electrode catalyst according to claim 1 , wherein,
when an analysis of a particle size distribution of the catalyst particles is performed by using a three-dimensional reconstructed image obtained by an electron beam tomography measurement using an STEM (scanning transmission electron microscopy),
a ratio of the catalyst particles supported inside the Nanopore is 50% or more.

7. The electrode catalyst according to claim 6 , wherein,
when an analysis of a particle size distribution of the catalyst particles is performed by using a three-dimensional reconstructed image obtained by an electron beam tomography measurement using an STEM (scanning transmission electron microscopy),
a ratio of the catalyst particles supported inside the Nanopore is 70% or more.

8. The electrode catalyst according to claim 1 , wherein at least a part of the surface of the catalyst particles is covered with a Pt oxide film.

9. The electrode catalyst according to claim 1 . wherein the hollow carbon carrier has a BET specific surface area (nitrogen adsorption specific surface area) of 200 to 1500 m 2 /g.

10. The electrode catalyst according to claim 9 , wherein the hollow carbon carrier is Ketjen EC300J.

11. A powder of a electrode catalyst, which contains 10 wt % or more of the electrode catalyst according to claim 1 .

12. A composition for forming a gas diffusion electrode, which contains the electrode catalyst according to claim 1 or a powder of the electrode catalyst.

13. A gas diffusion electrode, which contains electrode catalyst according to claim 1 or a powder of the electrode catalyst.

14. A membrane-electrode assembly (MEA), which comprises the gas diffusion electrode according to claim 13 .

15. A fuel cell stack, which comprises the membrane-electrode assembly (MEA) of claim 14 .

Assignees

• N E Chemcat Corp

Inventors

• Wada Yoshiyuki
• Mizusaki Tomoteru
• Nagamori Kiyotaka
• Aoki Satoshi
• Shiina Hiroki
• Seki Yasuhiro

Classifications

• H01M8/1004

  characterised by membrane-electrode assemblies [MEA] (H01M8/12 takes precedence) · CPC title

• H01M4/923

  Compounds thereof with non-metallic elements · CPC title

• H01M4/8657

  layered · CPC title

• B01J23/42

  Platinum · CPC title

• H01M8/10

  Fuel cells with solid electrolytes · CPC title