Method for coating a substrate with a Co-PI modified BiVO4/WO3 heterostructure film

Patent metadata

Field	Value
Publication number	US-12247281-B2
Application number	US-202217971683-A
Country	US
Kind code	B2
Filing date	Oct 24, 2022
Priority date	Oct 24, 2022
Publication date	Mar 11, 2025
Grant date	Mar 11, 2025

Abstract

A method for coating a substrate with a Co-Pi modified BiVO 4 /WO 3 heterostructure film includes direct current reactive sputtering tungsten (W) onto a substrate in a gaseous mixture containing oxygen to form a tungsten trioxide (WO 3 ) film, direct current reactive sputtering bismuth (Bi) onto the tungsten trioxide (WO 3 ) film in a gaseous mixture containing oxygen to form a dibismuth trioxide (Bi 2 O 3 ) film, drop-casting a vanadyl acetylacetonate solution onto the Bi 2 O 3 film and heating at a temperature of at least 450° C. in ambient air to convert the Bi 2 O 3 film to a BiVO 4 film, and photoelectrochemically coating the BiVO 4 film with a cobalt-phosphate (Co-Pi) to form a modified film on the surface of the substrate. A photoanode containing the Co-Pi modified BiVO 4 /WO 3 heterostructure film prepared by the method, and its application in water splitting.

First claim

The invention claimed is:

1. A method for coating a substrate with a Co-Pi modified BiVO 4 /WO 3 heterostructure film, comprising:
direct current reactive sputtering tungsten (W) onto a substrate in a gaseous mixture comprising oxygen to form a tungsten trioxide (WO 3 ) film on the substrate;
direct current reactive sputtering bismuth (Bi) onto the tungsten trioxide (WO 3 ) film in a gaseous mixture comprising oxygen to form a dibismuth trioxide (Bi 2 O 3 ) film on the WO 3 film;
drop-casting a vanadyl acetylacetonate solution onto the Bi 2 O 3 film and heating at a temperature of at least 450° C. in ambient air to convert the Bi 2 O 3 film to a BiVO 4 film;
wherein the BiVO 4 film is a porous film comprising crystalline BiVO 4 ;
immersing the BiVO 4 film on the substrate in an aqueous mixture containing a cobalt salt and a phosphate salt;
photoelectrochemically coating the BiVO 4 film with a cobalt-phosphate (Co-Pi) to form a modified film on the surface of the substrate.

2. The method of claim 1 , wherein direct current reactive sputtering tungsten onto the substrate is carried out at a power of 50 to 200 watts (W) for 1 to 30 minutes and the gaseous mixture is introduced at a flow rate of 50 to 100 standard cubic centimeters per minute (sccm).

3. The method of claim 1 , wherein a distance of tungsten source to the substrate is in a range of 5 to 20 centimeters (cm).

4. The method of claim 1 , wherein direct current reactive sputtering bismuth onto the WO 3 film is carried out at a power of 5 to 50 W for 1 to 30 minutes and the gaseous mixture is introduced at a flow rate of 10 to 70 sccm.

5. The method of claim 1 , wherein a base pressure of the sputtering is maintained at 1×10 −6 to 20×10 −6 torr, and a working pressure of the sputtering is maintained at 1×10 −3 to 10×10 −3 torr.

6. The method of claim 1 , further comprising heating the WO 3 film in ambient air at a temperature of at least 500° C. for 1 to 3 hours with a heating ramp rate of 10 to 30° C./min.

7. The method of claim 1 , wherein the heating of the Bi 2 O 3 film after drop casting is carried out for 1 to 3 hours with a heating ramp rate of 0.5 to 5° C./min.

8. The method of claim 1 , wherein the gaseous mixture comprises oxygen gas and argon gas, wherein a volume ratio of oxygen gas to argon gas is in a range of 1:10 to 10:1.

9. The method of claim 1 , wherein the WO 3 film has:
a uniform sheet-like morphology;
an average thickness of 50 to 250 nanometers (nm); and
a photocurrent density of 0.5 to 1 milliamperes per square centimeter (mA cm −2 ) at 1.23 V RHE .

10. The method of claim 1 , wherein the Bi 2 O 3 film has an interparticle porosity structure, and is uniformly deposited on the surface of the WO 3 film.

11. The method of claim 1 , wherein the BiVO 4 film has:
an average pore size of 0.01 to 1 micrometer (μm);
an average thickness of 100 to 600 nm; and
a photocurrent density of 0.8 to 1.5 mA cm −2 at 1.23 V RHE .

12. The method of claim 1 , wherein the Co-Pi modified BiVO 4 /WO 3 heterostructure film is uniform and pinhole-free, and comprises a plurality of Co-Pi particles uniformly distributed on the modified film.

13. The method of claim 12 , wherein the Co-Pi particles have an average particle size of 20 to 200 nm.

14. The method of claim 1 , wherein the Co-Pi modified BiVO 4 /WO 3 heterostructure film has a thickness in a range of 150 to 850 nm.

15. The method of claim 1 , further comprising:
mixing at least one cobalt (Co) salt and at least one phosphate (Pi) salt in a liquid to form the aqueous mixture having a pH value ranging from 5.5 to 7.5;
wherein a molar ratio of Co to Pi is in a range of 1:50 to 1:400;
adding the aqueous mixture to a photoelectrochemical cell connected to a power supply;
at least partially immersing the substate coated with the BiVO 4 film in the aqueous mixture;
wherein the substate is a fluorinated tin oxide (FTO) glass;
applying a potential to the aqueous mixture via the substrate to form a plurality of cobalt-phosphate (Co-Pi) particles on the surface of the BiVO 4 film;
removing the substrate from the aqueous mixture and drying to form the modified film on the surface of the substrate.

16. The method of claim 15 , wherein the cobalt salt is at least one selected from the group consisting of cobalt sulfide, cobalt fluoride, cobalt naphthenate, cobalt acetate, cobalt monoantimonide, cobalt oxide, cobalt triantimonide, cobalt hydroxide, cobalt chloride, cobalt thiocyanate, cobalt acetylacetonate, cobalt sulfate, cobalt carbonyl, cobalt nitrate, cobalt bromide, and/or a hydrate thereof.

17. The method of claim 15 , wherein the phosphate salt is at least one selected from the group consisting of sodium phosphate, sodium phosphate dibasic, sodium phosphate monobasic, potassium phosphate, potassium phosphate dibasic, potassium phosphate monobasic, and/or a hydrate thereof.

Assignees

• Univ King Fahd Pet & Minerals

Inventors

• Salih Amar Kamal Mohmeadkhair
• Drmosh Qasem Ahmed Qasem
• Kandiel Tarek
• Yamani Zain Hassan

Classifications

• Y02E60/36

  Hydrogen production from non-carbon containing sources, e.g. by water electrolysis · CPC title

• C23C18/1295

  with after-treatment of the deposited inorganic material · CPC title

• C23C18/1208

  Oxides, e.g. ceramics · CPC title

• C23C28/345

  with at least one oxide layer · CPC title

• C25D5/011

  Electroplating using electromagnetic wave irradiation (using locally applied electromagnetic radiation C25D5/024) · CPC title