Polychloroprene-based contact adhesives containing ethylene-vinyl acetate copolymer

Patent metadata

Field	Value
Publication number	US-12139645-B2
Application number	US-201816961461-A
Country	US
Kind code	B2
Filing date	Jan 11, 2018
Priority date	Jan 11, 2018
Publication date	Nov 12, 2024
Grant date	Nov 12, 2024

Abstract

Contact adhesive compositions comprising polychloroprene and, based on the polychloroprene content, 10 to 99 wt % of ethylene-vinyl acetate copolymer exhibit outstanding adhesion to substrates such as ethylene-vinyl acetate copolymers, thermoplastic elastomers or flexible PVC. The contact adhesive compositions of the invention are especially suitable for use in the bonding of articles, preferably articles in which at least part of the articles to be bonded consists of polyurethane, flexible PVC, ethylene-vinyl acetate copolymers and/or thermoplastic elastomers. This allows the adhesive composition to be employed widely in the footwear industry, for the bonding of roofing membranes containing flexible PVC, ethylene-propylene-diene rubber (EPDM) and/or ethylene-vinyl acetate copolymers, or for the bonding of synthetic leather based on flexible PVC.

First claim

The invention claimed is:

1. Contact adhesive composition comprising:
polychloroprene,
15 to 90 wt %, based on polychloroprene content, of an ethylene-vinyl acetate copolymer having a vinyl acetate content of 27 to 80 wt %, and
60-95 wt % of solvent, based on a total weight of the contact adhesive composition,

wherein the solvent is one or more members selected from the group consisting of organic solvents.

2. Contact adhesive composition according to claim 1 , comprising 60-95 wt % of solvent, and also a total of 5-40 wt % of polychloroprene and ethylene-vinyl acetate copolymer, based in each case on the total weight of the contact adhesive composition.

3. Contact adhesive composition according to claim 1 , comprising 0.1-35 wt % of further components selected from resins, magnesium oxide, zinc oxide, isocyanate-based crosslinkers, and ageing inhibitors, based on the total weight of the contact adhesive composition.

4. Contact adhesive composition according to claim 1 , which is free from methyl methacrylate.

5. Contact adhesive composition according to claim 1 , further comprising at least one of terpene phenolic resin, alkyl-phenolic resin, coumarone-indene resin, α-methylstyrene resin, chlorinated rubber, silica, and resin acid esters.

6. Contact adhesive composition according to claim 1 , wherein the polychloroprene has a weight-average molecular weight Mw of more than 200,000 daltons.

7. Contact adhesive composition according to claim 1 , comprising one or more isocyanate-based crosslinkers selected from di- and polyisocyanates.

8. A method of bonding an article in which at least part of the article to be bonded consists of at least one of polyurethane rubber, flexible PVC, ethylene-vinyl acetate copolymers, and thermoplastic elastomers, said method comprising bonding the articles with a contact adhesive composition according to claim 1 .

9. Method according to claim 8 , wherein the article is a footwear item.

10. Method according to claim 8 , wherein the article is a roofing membrane comprising at least one of flexible PVC, ethylene-propylene-diene rubber, and ethylene-vinyl acetate copolymers, or the article is synthetic leather based on flexible PVC.

11. Method according to claim 8 , wherein the contact adhesive composition, in solution in the solvent, is applied to a surface of the article to be bonded to another surface, the solvent is evaporated at least partially by flashing off or under reduced pressure, and then the surface of the article, now covered with the adhesive, is pressed against said another surface.

12. Method according to claim 11 , wherein the solvent is evaporated at a temperature of between 0° C. and 80° C.

13. Method according to claim 11 , wherein, after the evaporation of the solvent, the adhesive is heat-activated at a temperature of between 40° C. and 100° C.

Assignees

• Arlanxeo Deutschland Gmbh

Inventors

• Hoch Martin
• Lente Christian
• Friese Regina
• Schneider Martin

Classifications

• C09J2423/04

  Presence of homo or copolymers of ethene · CPC title

• C09J2431/00

  Presence of polyvinyl acetate · CPC title

• C09J2427/008

  in the pretreated surface to be joined · CPC title

• C09J2411/00

  Presence of chloroprene · CPC title

• C09J5/00

  Adhesive processes in general; Adhesive processes not provided for elsewhere, e.g. relating to primers · CPC title