Preparation method for metal foam

Patent metadata

Field	Value
Publication number	US-12097562-B2
Application number	US-201816610556-A
Country	US
Kind code	B2
Filing date	May 15, 2018
Priority date	May 16, 2017
Publication date	Sep 24, 2024
Grant date	Sep 24, 2024

Abstract

Methods for preparing a metal foam are provided. The methods may include forming a metal foam precursor using a slurry that includes metal powder, a dispersant, and a binder and sintering the metal foam precursor.

First claim

What is claimed is:

1. A method for preparing a metal foam, the method comprising:
forming a metal foam precursor on a metal base material by coating the metal base material with a slurry and drying; and
sintering the metal foam precursor to form the metal foam, thereby adhering the metal foam to the metal base material,
wherein the drying is performed at a temperature in a range of 50° C. to 250° C.,
wherein the slurry consists of metal powder, a dispersant and a binder,
wherein the slurry does not comprise water,
wherein the slurry consists of 1 to 500 parts by weight of the binder relative to 100 parts by weight of the metal powder and 10 to 1,600 parts by weight of the dispersant relative to 100 parts by weight of the binder,
wherein the dispersant is at least one selected from the group consisting of pentanol, octanol, 2-methoxyethanol, 2-ethoxyethanol, 2-butoxyethanol, texanol, terpineol, dihydric alcohol and polyhydric alcohol, and
wherein the prepared metal foam has a porosity of 60% or more.

2. The method for preparing the metal foam according to claim 1 , wherein the slurry consists of 7 to 500 parts by weight of the binder relative to 100 parts by weight of the metal powder and 10 to 1,400 parts by weight of the dispersant relative to 100 parts by weight of the binder.

3. The method for preparing the metal foam according to claim 1 , wherein the metal powder comprises copper powder.

4. The method for preparing the metal foam according to claim 1 , wherein the metal powder has an average particle diameter in a range of 0.1 μm to 30 μm.

5. The method for preparing the metal foam according to claim 1 , wherein the binder is alkyl cellulose, polyalkylene carbonate or a polyvinyl alcohol-based binder.

6. The method for preparing the metal foam according to claim 1 , wherein the dispersant is at least one selected from the group consisting of texanol, terpineol, dihydric alcohol and polyhydric alcohol.

7. The method for preparing the metal foam according to claim 1 , wherein the metal base material is a base material of any one metal selected from the group consisting of copper, molybdenum, silver, platinum, gold, aluminum, chromium, indium, tin, magnesium, zinc, nickel, iron, cobalt and manganese, or a base material of a mixture or alloy of two or more selected from the group of metals.

8. The method for preparing the metal foam according to claim 7 , wherein the metal powder comprises copper powder, and the metal base material comprises copper.

9. The method for preparing the metal foam according to claim 8 , wherein the sintering is performed at 1000° C. for 2 hours.

10. The method for preparing the metal foam according to claim 1 , wherein the sintering is performed at a temperature in a range of 500° C. to 2000° C.

11. The method for preparing the metal foam according to claim 1 , wherein the sintering is performed by induction heating.

12. The method for preparing the metal foam according to claim 1 , wherein the metal foam precursor is sintered in an atmosphere including hydrogen and argon.

Assignees

• Lg Chemical Ltd

Inventors

• Kim So Jin
• Shin Jong Min
• Lee Jin Kyù

Classifications

• B22F2007/047

  non-pressurised baking of the paste or slurry containing metal powder · CPC title

• B22F2301/10

  Copper · CPC title

• B22F7/008

  characterised by the composition · CPC title

• B22F7/004

  comprising at least one non-porous part · CPC title

• B22F2202/06

  Use of electric fields · CPC title