Method of producing negative electrode plate for non-aqueous electrolyte secondary battery

Patent metadata

Field	Value
Publication number	US-12034142-B2
Application number	US-202117501092-A
Country	US
Kind code	B2
Filing date	Oct 14, 2021
Priority date	Nov 5, 2020
Publication date	Jul 9, 2024
Grant date	Jul 9, 2024

Abstract

(A) A first layer is formed by applying a first negative electrode slurry to the surface of a negative electrode substrate. (B) A second layer is formed by applying a second negative electrode slurry to the surface of the first layer. The first negative electrode slurry includes a first negative electrode composite material. The second negative electrode slurry includes a second negative electrode composite material. Each of the first negative electrode composite material and the second negative electrode composite material includes a negative electrode active material and a cellulose-based binder. The negative electrode active material includes a first graphite powder and a second graphite powder. The first negative electrode composite material includes the cellulose-based binder at a first mass fraction. The second negative electrode composite material includes the cellulose-based binder at a second mass fraction.

First claim

What is claimed is:

1. A method of producing a negative electrode plate for a non-aqueous electrolyte secondary battery, the method comprising:
(A) applying a first negative electrode slurry to a surface of a negative electrode substrate to form a first layer;
(B) applying a second negative electrode slurry to a surface of the first layer to form a second layer; and
(C) compressing the first layer and the second layer to produce the negative electrode plate,
the first negative electrode slurry including a first negative electrode composite material,
the second negative electrode slurry including a second negative electrode composite material,
each of the first negative electrode composite material and the second negative electrode composite material including a negative electrode active material and a cellulose-based binder,
the negative electrode active material consisting essentially of a first graphite powder and a second graphite powder,
the first graphite powder having a circularity of 0.94 or more, and
a fraction of a D50 of the second graphite powder to a D50 of the first graphite powder being 29% to 54%,

in each of the first negative electrode composite material and the second negative electrode composite material,
the first graphite powder having a mass fraction of 88.1% to 93.6%, and
the second graphite powder having a mass fraction of 5% to 10%,

the first negative electrode composite material including the cellulose-based binder at a first mass fraction,
the second negative electrode composite material including the cellulose-based binder at a second mass fraction, and
a ratio of the first mass fraction to the second mass fraction being 0.40 to 0.56.

2. The method of producing a negative electrode plate for a non-aqueous electrolyte secondary battery according to claim 1 , wherein
the first graphite powder has a D50 of 13 μm to 19 μm.

3. The method of producing a negative electrode plate for a non-aqueous electrolyte secondary battery according to claim 1 , wherein
the negative electrode active material has a span value of 1.08 to 1.18,
the span value is calculated by the following expression (1):
(span value)=( D 90 −D 10)/ D 50  (1)

in the expression (1),
D90 represents D90 of the negative electrode active material,
D10 represents D10 of the negative electrode active material, and
D50 represents D50 of the negative electrode active material.

4. The method of producing a negative electrode plate for a non-aqueous electrolyte secondary battery according to claim 1 , wherein
the negative electrode active material has a tap density of 0.9 g/cm 3 to 1.2 g/cm 3 .

Assignees

• Prime Planet Energy & Solutions Inc

Inventors

• Sotome Kazuhiro
• Ishikawa Kaori
• Matsuo Yuta
• Takahashi Kentaro
• Ikeda Daisuke
• Hayashi Kunihiko
• Uchida Naoki

Classifications

• H01M2004/027

  Negative electrodes · CPC title

• H01M2004/021

  Physical characteristics, e.g. porosity, surface area · CPC title

• H01M4/622

  being polymers · CPC title

• H01M4/583

  Carbonaceous material, e.g. graphite-intercalation compounds or CFx · CPC title

• H01M4/366

  as layered products · CPC title