Ultra-high performance concrete with waste brick powder and preparation method and application thereof

Patent metadata

Field	Value
Publication number	US-11905213-B2
Application number	US-202318340924-A
Country	US
Kind code	B2
Filing date	Jun 26, 2023
Priority date	Jun 27, 2022
Publication date	Feb 20, 2024
Grant date	Feb 20, 2024

Abstract

An ultra-high performance concrete (UHPC) with waste brick powder and preparation method and application thereof are provided, which relates to the technical field of concrete. The preparation method includes the following steps: stimulating activity of a brick powder by a method of mechanically stimulating activity to obtain waste brick powder; and preparing UHPC according to a mass ratio of cement to waste brick powder of 5:5-7:3 to obtain the UHPC with waste brick powder. The UHPC is prepared by treating waste bricks from construction waste (mechanically stimulating activity) to make waste brick powder with activity, therefore partially replacing cement. The UHPC is applied in a construction field.

First claim

What is claimed is:

1. A preparation method of an ultra-high performance concrete with waste brick powder, wherein raw materials of the ultra-high performance concrete with waste brick powder comprise, in parts by mass, 35-42 parts of cement, 28-35 parts of brick powder, 10 parts of fly ash, 20 parts of silica fume, 100 parts of grit, 15.6 parts of steel fiber, 30 parts of water reducing agent and 17 parts of water;
the brick powder and the cement are in a total amount of 70 parts;
the preparation method of the ultra-high performance concrete with waste brick powder comprises following steps:
stimulating activity of the brick powder by using a method of mechanically stimulating activity to obtain the waste brick powder; and
preparing ultra-high performance concrete by weighing the raw materials in parts by mass to obtain the ultra-high performance concrete with the waste brick powder; and
the method of mechanically stimulating activity specifically comprises stimulating the activity of the brick powder by using a ball mill to ball mill a brick powder with a particle size of 8-75 micrometers for 45 minutes at a rate greater than 45 revolutions per minute.

2. The preparation method of the ultra-high performance concrete with waste brick powder according to claim 1 , wherein the cement is P·O52.5 ordinary portland cement.

3. The preparation method of the ultra-high performance concrete with waste brick powder according to claim 1 , wherein the fly ash is first-grade fly ash.

4. The preparation method of the ultra-high performance concrete with waste brick powder according to claim 1 , wherein the steel fiber is copper plated steel fiber.

5. The preparation method of the ultra-high performance concrete with waste brick powder according to claim 1 , wherein the water reducing agent is polycarboxylate superplasticizer, and a water reducing rate of the water reducing agent is greater than 30%.

6. An ultra-high performance concrete with waste brick powder prepared by using the preparation method according to claim 1 .

Assignees

• Univ Zhengzhou

Inventors

• Yuan Chengfang
• Feng Hu
• Raza Ali
• Shen Lei
• Sun Yanan
• Zhang Changjiu
• Wang Baoliang
• Wu Xiaohan
• Chen Na
• Sun Gangzhu

Classifications

• C04B18/16 Primary

  from building or ceramic industry · CPC title

• C04B7/19

  Portland cements · CPC title

• C04B14/48

  Metal · CPC title

• C04B18/08

  Flue dust {, i.e. fly ash} · CPC title

• C04B18/146

  Silica fume · CPC title