Electrolyte compositions for redox flow batteries

Patent metadata

Field	Value
Publication number	US-11837767-B2
Application number	US-202117388962-A
Country	US
Kind code	B2
Filing date	Jul 29, 2021
Priority date	Dec 23, 2020
Publication date	Dec 5, 2023
Grant date	Dec 5, 2023

Abstract

Stable and high performance positive and negative electrolytes compositions to be used in redox flow battery systems are described. The redox flow battery system, comprises: at least one rechargeable cell comprising a positive electrolyte, a negative electrolyte, and an ionically conductive membrane positioned between the positive electrolyte and the negative electrolyte, the positive electrolyte in contact with a positive electrode, and the negative electrolyte in contact with a negative electrode. The positive electrolyte consists essentially of water, a first amino acid, an inorganic acid, an iron precursor, a supporting electrolyte, and optionally a boric acid. The negative electrolyte consists essentially of water, the iron precursor, the supporting electrolyte, and a negative electrolyte additive. The iron precursor is FeCl 2 , FeCl 3 , FeSO 4 , Fe 2 (SO 4 ) 3 , FeO, Fe, Fe 2 O 3 , or combinations thereof. The supporting electrolyte is LiCl, NaCl, Na 2 SO 4 , KCl, NH 4 Cl, or combinations thereof. The negative electrolyte additive is boric acid or a combination of the boric acid and a second amino acid.

First claim

What is claimed is:

1. A redox flow battery system, comprising:
at least one rechargeable cell comprising a positive electrolyte, a negative electrolyte, and an ionically conductive membrane positioned between the positive electrolyte and the negative electrolyte, the positive electrolyte in contact with a positive electrode, and the negative electrolyte in contact with a negative electrode;
the positive electrolyte consisting essentially of water, a first amino acid, an inorganic acid, an iron precursor, a supporting electrolyte, and optionally a boric acid; and
the negative electrolyte consisting essentially of water, the iron precursor, the supporting electrolyte, and a negative electrolyte additive;
wherein the iron precursor is FeCl 2 , FeCl 3 , FeSO 4 , Fe 2 (SO 4 ) 3 , FeO, Fe, Fe 2 O 3 , or combinations thereof;
wherein the supporting electrolyte is LiCl, NaCl, Na 2 SO 4 , KCl, NH 4 Cl, or combinations thereof; and
wherein the negative electrolyte additive is boric acid and optionally a second amino acid;
wherein the ionically conductive membrane comprises an ionically conductive thin film composite membrane comprising a microporous support membrane and a hydrophilic ionomeric polymer coating layer on a surface of the microporous support membrane, wherein the hydrophilic ionomeric polymer coating layer is ionically conductive; and
wherein the hydrophilic ionomeric polymer comprises a polyphosphoric acid-complexed polysaccharide polymer, a polyphosphoric acid and metal ion-complexed polysaccharide polymer, a metal ion-complexed polysaccharide polymer, a boric acid-complexed polysaccharide polymer, an alginate polymer, an alginic acid polymer, a hyaluronic acid polymer, a boric acid-complexed polyvinyl alcohol polymer, polyphosphoric acid-complexed polyvinyl alcohol polymer, a polyphosphoric acid and metal ion-complexed polyvinyl alcohol polymer, a metal ion-complexed polyvinyl alcohol polymer, a metal ion-complexed poly(acrylic acid) polymer, a boric acid-complexed poly(acrylic acid) polymer, a metal ion-complexed poly(methacrylic acid), a boric acid-complexed poly(methacrylic acid), or combinations thereof; and wherein metal ion is ferric ion or ferrous ion.

2. The battery system of claim 1 wherein the ionically conductive membrane is made from a perfluorinated ionomer, a partially fluorinated polymer, a non-fluorinated hydrocarbon polymer, a non-fluorinated polymer with an aromatic backbone, or an acid-base blend.

3. The battery system of claim 1 wherein the boric acid is present in the positive and negative electrolytes.

4. The battery system of claim 1 wherein the first amino acid in the positive electrolyte is glycine.

5. The battery system of claim 1 wherein the first amino acid in the positive electrolyte is glycine and the negative electrolyte additive is a combination of boric acid and a second amino acid, and wherein the second amino acid is glycine.

6. The battery system of claim 1 wherein the inorganic acid in the positive electrolyte is HCl, H 2 SO 4 , or combinations thereof.

7. The battery system of claim 1 wherein the positive electrolyte consisting essentially of FeCl 2 at a concentration of 1.0-4.5 M, KCl at a concentration of 1.0-3.5 M or NH 4 Cl at a concentration of 1.0-4.0 M, HCl at a concentration of 0.05-2.5M, and glycine at a concentration of 0.01-3.0 M, optionally boric acid at a concentration of 0.01-1.0 M, and optionally the FeCl 3 at a concentration of 0.1-1.0 M.

8. The battery system of claim 1 wherein the negative electrolyte consisting essentially of FeCl 2 at a concentration of 1.0-4.5 M, KCl at a concentration of 1.0-3.5 M or NH 4 Cl at a concentration of 1.0-4.0 M, and the boric acid at a concentration of 0.01-1.0 M, optionally glycine at a concentration of 0.01-3.0 M, and optionally the FeCl 3 at a concentration of 0.1-1.0 M.

9. The battery system of claim 1 wherein a pH of the positive electrolyte is in a range of −1 to 3 and a pH of the negative electrolyte is in a range of 0 to 5.

10. The battery system of claim 1 wherein a pH of the positive electrolyte is in a range of 0 to 2 and a pH of the negative electrolyte is in a range of 1 to 4.5.

11. The battery system of claim 1 wherein the polysaccharide polymer comprises chitosan, sodium alginate, potassium alginate, calcium alginate, ammonium alginate, alginic acid, sodium hyaluronate, potassium hyaluronate, calcium hyaluronate, ammonium hyaluronate, hyaluronic acid, dextran, pullulan, carboxymethyl curdlan, sodium carboxymethyl curdlan, potassium carboxymethyl curdlan, calcium carboxymethyl curdlan, ammonium carboxymethyl curdlan, κ-carrageenan, λ-carrageenan, τ-carrageenan, carboxymethyl cellulose, sodium carboxymethyl cellulose, potassium carboxymethyl cellulose, calcium carboxymethyl cellulose, ammonium carboxymethyl cellulose, pectic acid, chitin, chondroitin, xanthan gum, or combinations thereof.

12. The battery system of claim 1 wherein the hydrophilic ionomeric polymer is a polyphosphoric acid-complexed chitosan polymer, a polyphosphoric acid and metal ion-complexed chitosan polymer, a metal ion-complexed alginic acid polymer, a sodium alginate polymer, an alginic acid polymer, a hyaluronic acid polymer, or combinations thereof, where in the metal ion is ferric ion or ferrous ion.

13. The battery system of claim 1 wherein the hydrophilic ionomeric polymer is a boric acid-complexed polyvinyl alcohol polymer, a boric acid-complexed alginic acid, or a blend of boric acid-complexed polyvinyl alcohol and alginic acid polymer.

14. The battery system of claim 1 wherein the support membrane comprises polyethylene, polypropylene, polyamide, polyacrylonitrile, polyethersulfone, sulfonated polyethersulfone, polysulfone, sulfonated polysulfone, poly(ether ether ketone), sulfonated poly(ether ether ketone), polyester, polyvinylidene fluoride, carbon, polycarbonate, cellulose, acrylic, phenolic, cellulose acetate, cellulose triacetate, polybenzimidazole, or combinations thereof.

15. The battery system of claim 1 wherein the hydrophilic ionomeric polymer is present in the micropores of the support membrane.

16. A redox flow battery system comprising:
at least one rechargeable cell comprising a positive electrolyte, a negative electrolyte, and an ionically conductive thin film composite (TFC) membrane positioned between the positive electrolyte and the negative electrolyte, the positive electrolyte in contact with a positive electrode, and the negative electrolyte in contact with a negative electrode;
the TFC membrane comprising a microporous support membrane and a hydrophilic ionomeric polymer coating layer on a surface of the microporous support membrane, wherein the hydrophilic ionomeric polymer coating layer is ionically conductive;
the positive electrolyte consisting essentially of FeCl 2 at a concentration of 1.0-4.5 M, KCl at a concentration of 1.0-3.5 M, HCl at a concentration of 0.05-2.5 M, and glycine at a concentration of 0.01-3.0 M, optionally boric acid at a concentration of 0.01-1.0 M, and optionally FeCl 3 at a concentration of 0.1-1.0 M; and
the negative electrolyte consisting essentially of FeCl 2 at a concentration of 1.0-4.5 M, KCl at a concentration of 1.0-3.5 M, and boric acid at a concentration of 0.01-1.0 M, optionally glycine at a concentration of 0.01-3.0 M, and optionally FeCl 3 at a concentration of 0.1-1.0 M;
wherein the hydrophilic ionomeric polymer comprises a polyphosphoric acid-complexed polysaccharide polymer, a polyphosphoric acid and metal ion-complexed polysaccharide polymer, a metal ion-complexed polysaccharide polymer, a boric acid-complexed polysaccharide

Assignees

• Uop Llc

Inventors

• Liu Chunqing
• Dong Xueliang
• Ba Chaoyi
• Miller Stuart R
• Yang James H K

Classifications

• H01M8/188 Primary

  by recharging of redox couples containing fluids; Redox flow type batteries · CPC title

• H01M8/08

  Fuel cells with aqueous electrolytes · CPC title

• H01M2300/0005

  Acid electrolytes · CPC title

• H01M8/0245

  in the form of layered or coated products · CPC title

• H01M8/0239

  Organic resins; Organic polymers · CPC title