Compositionally modulated zinc-manganese multilayered coatings

Patent metadata

Field	Value
Publication number	US-11633940-B2
Application number	US-202117364954-A
Country	US
Kind code	B2
Filing date	Jul 1, 2021
Priority date	Feb 28, 2018
Publication date	Apr 25, 2023
Grant date	Apr 25, 2023

Abstract

The present disclosure provides electrolyte solutions for electrodeposition of zinc-manganese alloys, methods of forming electrolyte solutions, methods of electrodepositing zinc-manganese alloys, and multilayered zinc-manganese alloys. An electrolyte solution for electroplating can include a metal salt, boric acid, an alkali metal chloride, polyethylene glycol, and a hydroxy benzaldehyde. An electrolyte solution can be formed by dissolving a metal salt, boric acid, an alkali metal chloride, polyethylene glycol, and a hydroxy benzaldehyde in water or an aqueous solution. Electrodepositing zinc-manganese alloys on a substrate can include introducing a cathode and an anode into an electrolyte solution comprising a metal salt, boric acid, an alkali metal chloride, polyethylene glycol, and a hydroxy benzaldehyde. Electrodepositing can further include passing a current between the cathode and the anode through the electrolyte solution to deposit zinc and manganese onto the cathode.

First claim

What is claimed is:

1. A substrate comprising:
a zinc-manganese coating having a thickness of about 1 micron to about 100 microns and comprising a plurality of alternating layers, the layers having a zinc content and a manganese content, the substrate comprising one or more of steel, copper, brass, or nickel,
wherein:
a first one or more layers of the plurality of layers has a manganese content of about 1 wt % to about 25 wt %,
a second one or more layers of the plurality of layers has a manganese content of about 0.1 wt % to about 5 wt %, the second one or more layers of the plurality of layers being different from the first one or more layers of the plurality of layers.

2. The substrate of claim 1 , wherein a third one or more layers of the plurality of layers has a manganese content of about 0.5 wt % to about 1 wt %.

3. The substrate of claim 2 , wherein a fourth one or more layers of the plurality of layers has a manganese content of about 2 wt % to about 3 wt %.

4. The substrate of claim 1 , wherein a third one or more layers of the plurality of layers has a manganese content of about 10 wt % to about 15 wt %.

5. The substrate of claim 4 , wherein a fourth one or more layers of the plurality of layers has a manganese content of about 0.1 wt % to about 3.5 wt %.

6. A method for electrodepositing a zinc-manganese alloy on a substrate, the method comprising:
introducing a cathode and an anode with a solution comprising:
a zinc salt, a manganese salt, an alkali metal citrate, an alkali metal acetate, a citric acid, glycine, and a thiamine; and

passing a first current between the cathode and the anode through the electrolyte solution to deposit a first layer containing zinc and manganese onto the cathode.

7. The method of claim 6 , wherein the anode is a zinc material or a carbonaceous electrode material.

8. The method of claim 6 , wherein passing a current comprises passing a current between the cathode and the anode at a current density of about 1 mA/cm 2 to about 200 mA/cm 2 .

9. The method of claim 8 , wherein the current is a series of pulses and each pulse has a duration of about 20 milliseconds to about 800 milliseconds.

10. The method of claim 9 , wherein the temperature of the solution is maintained at a temperature of about 20° C. to about 35° C. while passing the current.

11. The method of claim 6 , further comprising depositing a second layer comprising zinc and manganese onto the first layer by passing a second current between the cathode and the anode, the second current having a current density different than a current density of the first current.

12. The method of claim 6 , further comprising depositing a second layer comprising zinc and manganese onto the first layer by passing a second current between the cathode and the anode, the second current having substantially the same current density as a current density of the first current.

13. The method of claim 11 , further comprising repeating passing currents between the cathode and the anode to form a coating having a plurality of alternating layers having a manganese content, wherein the currents have substantially the same duration and the layers have substantially the same thickness and substantially the same manganese content.

14. The method of claim 11 , further comprising repeating passing currents between the cathode and the anode to form a coating having a plurality of alternating layers, wherein the layers have substantially the same thickness and two or more of the layers have a different manganese content.

15. A substrate comprising:
a zinc-manganese coating having a thickness of about 1 micron to about 100 microns and comprising a plurality of alternating layers, the layers having a zinc content and a manganese content, the substrate comprising one or more of steel, copper, brass, or nickel, wherein:
a first one or more layers of the plurality of layers has a manganese content of about 1 wt % to about 25 wt %, and
a second one or more layers of the plurality of layers has a manganese content of about 20 wt % to about 25 wt %, the second one or more layers of the plurality of layers being different from the first one or more layers of the plurality of layers.

16. The substrate of claim 15 , wherein a third one or more layers of the plurality of layers has a manganese content of about 0.5 wt % to about 5 wt %.

17. The substrate of claim 1 , wherein the second one or more layers is disposed on the first one or more layers.

18. The substrate of claim 15 , wherein the second one or more layers is disposed on the first one or more layers.

19. The substrate of claim 16 , wherein a third one or more layers of the plurality of layers has a manganese content of about 0.5 wt % to about 1 wt %.

20. The substrate of claim 19 , wherein the manganese content of the first one or more layers of the plurality of layers is different than the manganese content of the second one or more layers.

Assignees

• Boeing Co

Inventors

• Gaydos Stephen P
• Ijeri Vijaykumar S
• Prakash Om
• Tiwari Shashi Kant
• Singh Raghuvir
• Paswan Sharma
• Pathak Lokesh C

Classifications

• C25D5/10

  Electroplating with more than one layer of the same or of different metals (for bearings C25D7/10) · CPC title

• C25D5/623

  Porosity of the layers · CPC title

• C25D5/48

  After-treatment of electroplated surfaces · CPC title

• B32B2311/20

  Zinc · CPC title

• C25D5/18

  Electroplating using modulated, pulsed or reversing current · CPC title