Oxide ore smelting method

Patent metadata

Field	Value
Publication number	US-11608543-B2
Application number	US-201716094493-A
Country	US
Kind code	B2
Filing date	Apr 26, 2017
Priority date	Apr 27, 2016
Publication date	Mar 21, 2023
Grant date	Mar 21, 2023

Abstract

The present invention addresses the problem, in methods for producing a metal or alloy by reducing a mixture that contains an oxide ore, of providing an oxide ore smelting method with good productivity and efficiency. The present invention is an oxide ore smelting method for producing a metal or alloy by reducing a mixture that contains an oxide ore, the method comprising at least: a mixing step S 1 for mixing an oxide ore with a carbonaceous reducing agent; a mixture-molding step S 2 for molding the mixture obtained to obtain a mixture-molded body; and a reducing step S 3 for heating the mixture-molded body obtained at a specified reducing temperature in a reducing furnace.

First claim

The invention claimed is:

1. A nickel oxide ore smelting method for producing ferronickel by reducing a mixture containing a nickel oxide ore, the method comprising;
a mixing treatment step for mixing at least the nickel oxide ore and a carbonaceous reducing agent;
a mixture-molding step for molding the mixture obtained to obtain a mixture-molded body; and
a reducing step for heating the mixture-molded body obtained at a predetermined reducing temperature in a reducing furnace,
wherein in the mixture-molding step, the nickel oxide ore and the carbonaceous reducing agent are mixed, so that a proportion of the carbonaceous reducing agent is 5.0% or more and 40.0% or less, when a total value of chemical equivalents of the carbonaceous reducing agent required for reducing nickel oxide and iron oxide constituting the nickel oxide ore without excess or deficiency is taken as 100%, and
wherein the mixture is molded into a rod shape or a cylindrical shape, and the mixture-molded body obtained is cut into a flat plate-shaped or disk-shaped pellet in the mixture-molding step.

2. The nickel oxide ore smelting method according to claim 1 , wherein a movable hearth furnace is used as the reducing furnace and the flat plate-shaped or disk-shaped pellet is charged into the movable hearth furnace and reduced and heated in the reducing step.

3. The nickel oxide ore smelting method according to claim 1 , wherein the reducing temperature in the reducing step is 1250° C. or more and 1450° C. or less.

4. The nickel oxide ore smelting method according to claim 1 , further comprising a separating step for separating slag and obtaining the ferronickel after the reducing step is performed.

5. The nickel oxide ore smelting method according to claim 1 , wherein the mixture-molding step comprises a drying treatment step of drying the mixture-molded body, so that a content of Fe 2 O 3 contained in 100 parts by weight of a solid content of the mixture-molded body after the drying treatment step is in a range of 50 parts by weight or more and 60 parts by weight or less.

6. A nickel oxide ore smelting method for producing ferronickel by reducing a mixture containing a nickel oxide ore, the method comprising:
a mixing treatment step for mixing at least the nickel oxide ore and a carbonaceous reducing agent;
a mixture-molding step for molding the mixture obtained to obtain a mixture-molded body; and
a reducing step for heating the mixture-molded body obtained at a predetermined reducing temperature in a reducing furnace,
wherein in the mixture-molding step, the nickel oxide ore and the carbonaceous reducing agent are mixed, so that a proportion of the carbonaceous reducing agent is 5.0% or more and 40.0% or less, when a total value of chemical equivalents of the carbonaceous reducing agent required for reducing nickel oxide and iron oxide constituting the nickel oxide ore without excess or deficiency is taken as 100%, and
wherein a pellet is formed as the mixture-molded body in the mixture-molding step, and
the pellet is laminated to form a pellet laminate and the pellet laminate is charged into the reducing furnace and subjected to the heating in the reducing step.

7. The nickel oxide ore smelting method according to claim 6 ,
wherein the mixture is molded into the pellet having a cubic shape, a rectangular parallelepiped shape or a cylindrical shape in the mixture-molding step.

8. The nickel oxide ore smelting method according to claim 6 , wherein the mixture is molded into a volume of 8000 mm 3 or more in the mixture-molding step.

9. The nickel oxide ore smelting method according to any one of claims 6 to 8 , wherein a movable hearth furnace is used as the reducing furnace and the pellet laminate is charged into a hearth of the movable hearth furnace and subjected to the heating in the reducing step.

10. A nickel oxide ore smelting method for producing a metal or an alloy by reducing a mixture containing a nickel oxide ore, the method comprising:
a mixing treatment step for mixing at least the nickel oxide ore and a carbonaceous reducing agent;
a mixture-molding step for molding the mixture obtained to obtain a mixture-molded body;
a reducing step for heating the mixture-molded body obtained at a predetermined reducing temperature in a reducing furnace,
wherein in the mixture-molding step, the nickel oxide ore and the carbonaceous reducing agent are mixed, so that a proportion of the carbonaceous reducing agent is 5.0% or more and 40.0% or less, when a total value of chemical equivalents of the carbonaceous reducing agent required for reducing nickel oxide and iron oxide constituting the nickel oxide ore without excess or deficiency is taken as 100%, and
wherein the mixture is molded by being filled into a predetermined container, followed by compacting the resultant mixture which is filled in the container, and a mixture-filled container is obtained as the mixture-molded body, in the mixture-molding step.

11. The nickel oxide ore smelting method according to claim 10 , wherein the mixture-filled container is heated in a state of having a lid on the mixture-filled container in the reducing step.

12. The nickel oxide ore smelting method according to claim 10 , wherein the container has a rectangular parallelepiped shape or a cubic shape.

13. The nickel oxide ore smelting method according to claim 10 , wherein a movable hearth furnace is used as the reducing furnace and the mixture-filled container is charged into the movable hearth furnace and reduced and heated in the reducing step.

14. The nickel oxide ore smelting method according to claim 10 , wherein ferronickel is obtained as the alloy.

Assignees

• Sumitomo Metal Mining Co

Inventors

• Iseki Takashi
• Goda Yukihiro
• Kobayashi Jun-Ichi
• Okada Shuji

Classifications

• C22C38/08

  containing nickel {(C22C38/105 takes precedence)} · CPC title

• C22B23/021

  by reduction in solid state, e.g. by segregation processes · CPC title

• Y02P10/20

  Recycling · CPC title

• C21B13/08

  in rotary furnaces · CPC title

• C21B13/105

  Rotary hearth-type furnaces · CPC title