Coating agent, process of forming coating films, primer treatment process, process of repairing concretes, and process of constructing roads

Patent metadata

Field	Value
Publication number	US-11549033-B2
Application number	US-201816624655-A
Country	US
Kind code	B2
Filing date	Aug 21, 2018
Priority date	Aug 22, 2017
Publication date	Jan 10, 2023
Grant date	Jan 10, 2023

Abstract

A coating agent is capable of forming a coating film that has enhanced adhesion and adherence to a substrate, and enhanced water resistance as well and composed mainly of an aqueous material. A process of forming a coating agent uses the coating agent, a primer treatment process uses the coating agent, a process of doing repairs to concretes uses the coating agent, and a process of laying down roads uses the coating agent. The coating agent is composed mainly of a polyphenol derivative and containing a polymerizing agent, and has a pH of 9 or less. The polymerizing agent contains a compound having two or more functional groups selected from the group of an amino group and a mercapto group per molecule. In the process of forming a coating film, the coating agent is applied onto a substrate in an alkaline environment having a pH of greater than 9.

First claim

What is claimed is:

1. A process of laying down a road by successively carrying out the steps, comprising:
a step of preparing a coating agent comprising a main component containing a polyphenol derivative and a polymerizing agent,
a step of applying the coating agent onto a substrate in an alkaline environment to form a coating film thereon,
a step of forming a water-repellent layer on the coating film, and
a step of forming an asphalt on the water-repellent layer, wherein the water-repellent layer in the step of forming the water-repellent layer contains at least one of a polyurethane resin, an acrylic resin, an epoxy resin, a synthetic rubber, and a polyester-based unwoven fabric,
wherein the coating agent has a pH of no greater than 9, and
the polymerizing agent contains a compound having two or more functional groups selected from the group consisting of an amino group and a mercapto group per molecule.

2. The process of laying down a road according to claim 1 , wherein after the step of applying the coating agent onto the substrate and before the step of forming a water-repellent layer, a step of applying a solution containing at least one of an alkylamine, thiol fluoride or fluorine carbide is provided.

3. A process of forming a coating film, comprising:
a step of preparing a coating agent comprising a main component containing a polyphenol derivative and a polymerizing agent,
(i) a step of applying the coating agent onto a substrate in an alkaline environment having a pH of greater than 9 to form a coating film thereon, or
(ii) a step of contacting the coating agent with an alkaline substrate having a pH of greater than 9 to form a coating film on at least a portion of a surface layer of the substrate, and
a step of, after formation of the coating film in (i) or (ii), bringing a solution containing at least one of an alkylamine, thiol fluoride or fluorine carbide into contact with the coating film,
wherein the coating agent has a pH of no greater than 9, and
the polymerizing agent contains a compound having two or more functional groups selected from the group consisting of an amino group and a mercapto group per molecule.

4. A process of forming a coating film, comprising:
a step of preparing a coating agent comprising a main component containing a polyphenol derivative, a polymerizing agent and a buffer solution, and
(i) a step of applying the coating agent onto a substrate in an alkaline environment having a pH of greater than 9 to form a coating film thereon, or
(ii) a step of contacting the coating agent with an alkaline substrate having a pH of greater than 9 to form a coating film on at least a portion of a surface layer of a substrate,
wherein the coating agent has a pH of no greater than 9, and
the polymerizing agent contains a compound having two or more functional groups selected from the group consisting of an amino group and a mercapto group per molecule.

Assignees

• Nat Inst Materials Science

Inventors

• Naito Masanobu

Classifications

• C09D7/63

  organic · CPC title

• C09D171/12 Primary

  Polyphenylene oxides · CPC title

• C08K5/0025

  Crosslinking or vulcanising agents; including accelerators · CPC title

• C08K5/138

  Phenolates · CPC title

• C09D5/002

  Priming paints (C09D5/08 takes precedence) · CPC title