Abstract

Polypropylene composition comprising a polypropylene base material, a carbon fibre and an adhesion promoter with an excellent impact/stiffness balance, its preparation, articles comprising the composition and the use of the composition.

First claim

The invention claimed is:

1. A polypropylene composition comprising:
a. 37.0 to 95.0 wt %, based on a total weight of the polypropylene composition, of a polypropylene base material (PBM), wherein the polypropylene base material (PBM) comprises a propylene homopolymer (hPP) and a heterophasic propylene copolymer (HECO) in a weight ratio of propylene homopolymer (hPP) to heterophasic propylene copolymer (HECO) in a range of 1:5 to 1:25; and
b. 4.5 to 50.0 wt %, based on the total weight of the polypropylene composition, of a carbon fiber (CF); and
c. 0.5 to 13.0 wt %, based on the total weight of the polypropylene composition, of an adhesion promoter (AP),
wherein the carbon fiber (CF) comprised in the polypropylene composition is a roving and has an average fiber length in a range of 4.0 to 17.0 mm, the polypropylene composition is present as particles with the components a) and c) forming a polymer matrix (PM) having a melt flow rate MFR 2 (230° C., 2.16 kg) measured according to ISO 1133 in a range of 2.0 to 250 g/10 min and wherein an average particle length of the polypropylene composition corresponds to an average fiber length of the carbon fiber (CF), and wherein
the propylene homopolymer (hPP) has
a1. a melting temperature measured according to ISO 11357-3 of at least 150° C. and/or
b1. a xylene cold soluble (XCS) content of 4.0 wt %, based on a total weight of the propylene homopolymer (hPP),
the heterophasic propylene copolymer (HECO) has
a2. a xylene cold soluble (XCS) content of >5.0 wt %, based on a total weight of the heterophasic propylene copolymer (HECO), and/or
b2. a comonomer content of ≤30.0 mol %, based on a total weight of the heterophasic propylene copolymer (HECO), and
wherein the polypropylene base material (PBM) and the adhesion promoter (AP) are the only polymeric compounds in the polypropylene composition.

2. The polypropylene composition according to claim 1 , wherein the average fiber length of the carbon fiber (CF) is in a range of 7.0 to 16.0 mm.

3. The polypropylene composition according to claim 1 , wherein a fiber average diameter of the carbon fiber (CF) is in a range of 5 to 30 μm.

4. The polypropylene composition according to claim 1 , wherein the polypropylene composition comprises 1.0 to 8.0 wt %, based on the total weight of the polypropylene composition, of an adhesion promoter (AP).

5. The polypropylene composition according to claim 1 , wherein the adhesion promoter (AP) is a polypropylene containing a group derived from a polar compound selected from the group consisting of acid anhydride, carboxylic acid, carboxylic acid derivative, primary and secondary amine, hydroxyl, oxazoline and epoxide.

6. The polypropylene composition according to claim 1 , wherein the adhesion promoter (AP) is a maleic anhydride functionalized polypropylene.

7. An article comprising the polypropylene composition according to claim 1 .

8. The article according to claim 7 , wherein the article is an injection molded article.

9. The article according to claim 7 , wherein the average fiber length of the carbon fiber (CF) comprised in the article is smaller or equal to the average fiber length of the carbon fiber (CF) comprised in the polypropylene composition.

10. A process for the preparation of a polypropylene composition according to claim 1 , comprising the steps of:
a. providing a polypropylene base material (PBM),
b. providing an adhesion promoter (AP),
c. melting the polypropylene base material (PBM) of step a) and melting the adhesion promoter (AP) of step b),
d. providing a carbon fiber (CF) as a continuous roving,
e. combining the polypropylene base material (PBM) and the adhesion promoter (AP) of step c) with the carbon fiber (CF) of step d) to obtain a carbon fiber (CF) reinforced polypropylene material, and
f. solidifying and cutting the carbon fiber (CF) reinforced polypropylene material into particles with an average particle length in a range of 4.0 to 17.0 mm to obtain the polypropylene composition.

11. The process according to claim 10 , wherein comprising melt compounding at least a part of the polypropylene base material (PBM) of step a) and at least a part or a whole amount of the adhesion promoter (AP) of step b) in step c) to form a pre-compound, and combining the pre-compound with the carbon fiber (CF) in step e).

12. The process according to claim 10 , comprising carrying out step e) by first impregnating the carbon fiber (CF) of step d) with a first part of the polypropylene base material (PBM1) and with a part or a whole of the adhesion promoter (AP) of step c) and subsequently coating a thus impregnated carbon fiber (CF) with a remaining second part of the polypropylene base material (PBM2) and any remaining adhesion promoter (AP) of step c) to obtain a carbon fiber (CF) reinforced polypropylene material.

13. A process for the preparation of a polypropylene composition comprising:
a. 37.0 to 95.0 wt %, based on a total weight of the polypropylene composition, of a polypropylene base material (PBM) wherein the polypropylene base material (PBM) is:
i. a propylene homopolymer (hPP) and/or
ii. a propylene copolymer (cPP); and

b. 4.5 to 50.0 wt %, based on the total weight of the polypropylene composition, of a carbon fiber (CF); and
c. 0.5 to 13.0 wt %, based on the total weight of the polypropylene composition, of an adhesion promoter (AP),
wherein the carbon fiber (CF) comprised in the polypropylene composition is a roving and has an average fiber length in a range of 4.0 to 17.0 mm, the polypropylene composition is present as particles with the components a) and c) forming a polymer matrix (PM) having a melt flow rate MFR 2 (230° C., 2.16 kg) measured according to ISO 1133 in a range of 2.0 to 250 g/10 min and wherein an average particle length of the polypropylene composition corresponds to an average fiber length of the carbon fiber (CF), and wherein
the propylene homopolymer (hPP) has
a1. a melting temperature measured according to ISO 11357-3 of at least 150° C. and/or
b1. a xylene cold soluble (XCS) content of ≤4.0 wt %, based on a total weight of the propylene homopolymer (hPP),
the propylene copolymer (cPP) is a heterophasic propylene copolymer (HECO) having
a2. a xylene cold soluble (XCS) content of >5.0 wt %, based on a total weight of the heterophasic propylene copolymer (HECO), and/or
b2. a comonomer content of ≤30.0 mol %, based on a total weight of the heterophasic propylene copolymer (HECO), and
wherein the polypropylene base material (PBM) and the adhesion promoter (AP) are the only polymeric compounds in the polypropylene composition,
the process comprising steps of:
a′. providing a polypropylene base material (PBM),
b′. providing an adhesion promoter (AP),
c′. melting the polypropylene base material (PBM) of step a) and melting the adhesion promoter (AP) of step b),
d′. providing a carbon fiber (CF) as a continuous roving,
e′. impregnating the carbon fiber (CF) of step d′) with a first part of the polypropylene base material (PBM1) and with a whole of the adhesion promoter (AP) of step c′) and subsequently coating a thus impregnated carbon fiber (CF) with a remaining second part of the polypropylene base material (PBM2) to obtain a carbon fiber (CF) reinforced polypropylene material, and
f′. solidifying and cutting the carbon fiber (CF) reinforced polypropylene material into particles with an average particle length in a range of 4.0 to 17.0 mm to obtain the polypropylene composition.

Assignees

• Borealis Ag

Inventors

• Lummerstorfer Thomas
• Stockreiter Wolfgang
• Jerabek Michael
• Hochradl Stefan
• Tranninger Michael

Classifications

• B29C45/0001

  characterised by the choice of material · CPC title

• C08L23/14

  Copolymers of propene (C08L23/16 takes precedence) · CPC title

• C08J5/042

  with carbon fibres · CPC title

• C08L2207/02

  Heterophasic composition · CPC title

• C08L2205/16

  Fibres; Fibrils · CPC title